Multi-Functional Applications of H-Glass Embedded with Stable Plasmonic Gold Nanoislands.

Metal nanoparticles (MNPs) are synthesized using various techniques on diverse substrates that significantly impact their properties. However, among the substrate materials investigated, the major challenge is the stability of MNPs due to their poor adhesion to the substrate. Herein, it is demonstrated how a newly developed H-glass can concurrently stabilize plasmonic gold nanoislands (GNIs) and offer multifunctional applications. The GNIs on the H-glass are synthesized using a simple yet, robust thermal dewetting process. The H-glass embedded with GNIs demonstrates versatility in its applications, such as i) acting as a room temperature chemiresistive gas sensor (70% response for NO2 gas); ii) serving as substrates for surface-enhanced Raman spectroscopy for the identifications of Nile blue (dye) and picric acid (explosive) analytes down to nanomolar concentrations with enhancement factors of 4.8 × 106 and 6.1 × 105 , respectively; and iii) functioning as a nonlinear optical saturable absorber with a saturation intensity of 18.36 × 1015 W m-2 at 600 nm, and the performance characteristics are on par with those of materials reported in the existing literature. This work establishes a facile strategy to develop advanced materials by depositing metal nanoislands on glass for various functional applications.

H-Glass Supported Hybrid Gold Nano-Islands for Visible-Light-Driven Hydrogen Evolution.

Flat panel reactors, coated with photocatalytic materials, offer a sustainable approach for the commercial production of hydrogen (H2) with zero carbon footprint. Despite this, achieving high solar-to-hydrogen (STH) conversion efficiency with these reactors is still a significant challenge due to the low utilization efficiency of solar light and rapid charge recombination. Herein, hybrid gold nano-islands (HGNIs) are developed on transparent glass support to improve the STH efficiency. Plasmonic HGNIs are grown on an in-house developed active glass sheet composed of sodium aluminum phosphosilicate oxide glass (H-glass) using the thermal dewetting method at 550 °C under an ambient atmosphere. HGNIs with various oxidation states (Au0, Au+, and Au-) and multiple interfaces are obtained due to the diffusion of the elements from the glass structure, which also facilitates the lifetime of the hot electron to be ≈2.94 ps. H-glass-supported HGNIs demonstrate significant STH conversion efficiency of 0.6%, without any sacrificial agents, via water dissociation. This study unveils the specific role of H-glass-supported HGNIs in facilitating light-driven chemical conversions, offering new avenues for the development of high-performance photocatalysts in various chemical conversion reactions for large-scale commercial applications.

Nonlinear Optical Limiting and Radiation Shielding Characteristics of Sm2O3 Doped Cadmium Sodium Lithium Borate Glasses.

Strong nonlinear absorption (NLA), reduced optical limiting (OL) thresholds, and high radiation shielding parameters are required for the effective use of glasses in the laser radiation and nuclear radiation protecting materials. In view of this, the efficacy of Sm2O3 on the nonlinear optical (NLO) and OL properties were ascertained (at 532 nm) along with radiation shielding characteristics. The open and closed aperture Z-scan profiles revealed the presence of positive NLA and nonlinear refraction (NLR) phenomena respectively. OL measurements showed the existence of limiting behavior in the studied glasses. The NLA and NLR coefficients were improved while the OL thresholds were decreased as the doping of Sm2O3 elevated to a higher doping level. These improvements in NLA, NLR coefficients and OL efficiencies were attributed to the non-bridging oxygens and high polarizable Sm3+ ions. The NLA and OL results clearly suggest the high (5 mol %) Sm2O3 doped glass (Sm5CNLB) glass is beneficial to protect the delicate devices and human eye by suppressing the high energy laser light. The theoretical linear attenuation coefficients (LAC) values of the presented SmxCNLB glasses were obtained with the help of Phy-X software between 0.284 and 1.333 MeV. At 0.284 MeV, the maximum values occur and take values between 0.302 (for Sm0CNLB) and 0.409 cm-1 (for Sm5CNLB). We found that the LAC for the presented SmxCNLB glasses is a function of Sm2O3 content, where the LAC tends to increase, corresponding to the high probabilities of interaction, as the content of Sm2O3 changes from 0 to 5 mol %. The effective atomic number (Zeff) for the presented SmxCNLB glasses was examined between 0.284 and 1.333 MeV. As the amount of Sm2O3 is added, the Zeff increases, and this was observed at any energy.