Numerical Calculation of Apparent Contact Angles on the Hierarchical Surface with Array Microstructures by Wire Electrical Discharge Machining.

It is necessary to theoretically research wettability in superhydrophobic surface fabrication. Here, a numerical calculation approach is proposed for determining the contact angle of the water droplets on array micropillars by wire electrical discharge machining (WEDM). A hierarchical model is employed for these array microstructures, including mechanical analysis for a water droplet placed on a smooth array and wettability evaluation on the morphology of the WEDM surface. On pillars, equations are listed to solve the apparent contact angle according to force balance of gravity, tension, and pressure. As for the WEDM morphology, temperature simulation and measurement are carried out, and then the effect of roughness on surface wettability is studied. Constructed formulas predict the contact angle, and then the effect of geometric dimensions is obtained. In order to verify the assumption, array micropillars with different cross-profiles are prepared using high-speed WEDM on the Al alloy surface. Through the results of contact angle determination, the numerical calculation is carried out. This theoretical prediction is beneficial for improving the fabrication of the superhydrophobic surface by WEDM.

Experimental Study on the Comparison between Network Microstructure Titanium Matrix Composites and Ti6Al4V on EDM Milling.

Network microstructure titanium matrix composites (NMTMCs), featuring Ti6Al4V as the matrix and network-distributed TiB whiskers (TiBw) as reinforcement, exhibit remarkable potential for diverse applications due to their superior physical properties. Due to the difficulty in machining titanium matrix composites, electrical discharge machining (EDM) stands as one of the preferred machining techniques for NMTMCs. Nevertheless, the compromised surface quality and the recast layer significantly impact the performance of the workpiece machined by EDM. Therefore, for the purpose of enhancing the surface quality and restraining the defects of NMTMCs, this study conducted comparative EDM milling experiments between NMTMCs and Ti6Al4V to analyze the effects of discharge capacitance, charging current, and pulse interval on the surface roughness, recast layer thickness, recast layer uniformity, and surface microcrack density of both materials. The results indicated that machining energy significantly influences workpiece surface quality. Furthermore, comparative experiments exploring the influence of network reinforcement on EDM milling revealed that NMTMCs have a higher melting point, leading to an accumulation phenomenon in low-energy machining where the reinforcement could not be completely removed. The residual reinforcement in the recasting layer had an adsorption effect on molten metal affecting the thermal conductivity and uniformity within the recasting layer. Finally, specific guidelines are put forward for optimizing the material's surface roughness, recast layer thickness, and uniformity, along with minimizing microcrack density, which attain a processing effect that features a roughness of Ra 0.9 µm, an average recast layer thickness of 6 µm with a range of 8 µm, and a surface microcrack density of 0.08 µm-1.