Low Temperature Thermal Atomic Layer Deposition of Aluminum Nitride Using Hydrazine as the Nitrogen Source.

Aluminum nitride (AlN) thin films were grown using thermal atomic layer deposition in the temperature range of 175-350 °C. The thin films were deposited using trimethyl aluminum (TMA) and hydrazine (N2H4) as a metal precursor and nitrogen source, respectively. Highly reactive N2H4, compared to its conventionally used counterpart, ammonia (NH3), provides a higher growth per cycle (GPC), which is approximately 2.3 times higher at a deposition temperature of 300 °C and, also exhibits a low impurity concentration in as-deposited films. Low temperature AlN films deposited at 225 °C with a capping layer had an Al to N composition ratio of 1:1.1, a close to ideal composition ratio, with a low oxygen content (7.5%) while exhibiting a GPC of 0.16 nm/cycle. We suggest that N2H4 as a replacement for NH3 is a good alternative due to its stringent thermal budget.

A Comprehensive Study on the Effect of TiN Top and Bottom Electrodes on Atomic Layer Deposited Ferroelectric Hf0.5Zr0.5O2 Thin Films.

The discovery of ferroelectricity in HfO2-based materials in 2011 provided new research directions and opportunities. In particular, for atomic layer deposited Hf0.5Zr0.5O2 (HZO) films, it is possible to obtain homogenous thin films with satisfactory ferroelectric properties at a low thermal budget process. Based on experiment demonstrations over the past 10 years, it is well known that HZO films show excellent ferroelectricity when sandwiched between TiN top and bottom electrodes. This work reports a comprehensive study on the effect of TiN top and bottom electrodes on the ferroelectric properties of HZO thin films (10 nm). Investigations showed that during HZO crystallization, the TiN bottom electrode promoted ferroelectric phase formation (by oxygen scavenging) and the TiN top electrode inhibited non-ferroelectric phase formation (by stress-induced crystallization). In addition, it was confirmed that the TiN top and bottom electrodes acted as a barrier layer to hydrogen diffusion into the HZO thin film during annealing in a hydrogen-containing atmosphere. These features make the TiN electrodes a useful strategy for improving and preserving the ferroelectric properties of HZO thin films for next-generation memory applications.

Hollow Cathode Plasma-Enhanced Atomic Layer Deposition of Silicon Nitride Using Pentachlorodisilane.

In this work, a novel chlorodisilane precursor, pentachlorodisilane (PCDS, HSi2Cl5), was investigated for the growth of silicon nitride (SiN x) via hollow cathode plasma-enhanced atomic layer deposition (PEALD). A well-defined self-limiting growth behavior was successfully demonstrated over the growth temperature range of 270-360 °C. At identical process conditions, PCDS not only demonstrated approximately >20% higher growth per cycle than that of a commercially available chlorodisilane precursor, hexachlorodisilane (Si2Cl6), but also delivered a better or at least comparable film quality determined by characterizing the refractive index, wet etch rate, and density of the films. The composition of the SiN x films grown at 360 °C using PCDS, as determined by X-ray photoelectron spectroscopy, showed low O content (∼2 at. %) and Cl content (<1 at. %; below the detection limit). Fourier transform infrared spectroscopy spectra suggested that N-H bonds were the dominant hydrogen-containing bonds in the SiN x films without a significant amount of Si-H bonds originating from the precursor molecules. The possible surface reaction pathways of the PEALD SiN x using PCDS on the surface terminated with amine groups (-NH2 and -NH-) are proposed. The PEALD SiN x films grown using PCDS also exhibited a leakage current density as low as 1-2 nA/cm2 at 2 MV/cm and a breakdown electric field as high as ∼12 MV/cm.

Investigation of the Physical Properties of Plasma Enhanced Atomic Layer Deposited Silicon Nitride as Etch Stopper.

Correlations between physical properties linking film quality with wet etch rate (WER), one of the leading figures of merit, in plasma-enhanced atomic layer deposition (PEALD) grown silicon nitride (SiN x) films remain largely unresearched. Achieving a low WER of a SiN x film is especially significant in its use as an etch stopper for technology beyond 7 nm node semiconductor processing. Herein, we explore the correlation between the hydrogen concentration, hydrogen bonding states, bulk film density, residual impurity concentration, and the WERs of PEALD SiN x using Fourier transform infrared spectrometry, X-ray reflectivity, and spectroscopic ellipsometry, etc. PEALD SiN x films for this study were deposited using hexachlorodisilane and hollow cathode plasma source under a range of process temperatures (270-360 °C) and plasma gas compositions (N2/NH3 or Ar/NH3) to understand the influence of hydrogen concentration, hydrogen bonding states, bulk film density, and residual impurity concentration on the WER. Varying hydrogen concentration and differences in the hydrogen bonding states resulted in different bulk film densities and, accordingly, a variation in WER. We observe a linear relationship between hydrogen bonding concentration and WER as well as a reciprocal relationship between bulk film density and WER. Analogous to the PECVD SiN x processes, a reduction in hydrogen bonding concentration arises from either (1) thermal activation or (2) plasma excited species. However, unlike the case with silane (SiH4)-based PECVD SiN x, PEALD SiN x WERs are affected by residual impurities of Si precursors (i.e., chlorine impurity). Thus, possible wet etching mechanisms in HF in which the WER is affected by hydrogen bonding states or residual impurities are proposed. The shifts of amine basicity in SiN x due to different hydrogen bonding states and the changes in Si electrophilicity due to Cl impurity content are suggested as the main mechanisms that influence WER in the PEALD processes.