Iron oxide (Fe2 O3 ) is an abundant and potentially low-cost material for fabricating lithium-ion battery anodes. Here, the growth of α-Fe2 O3 nano-flowers at an electrified liquid-liquid interface is demonstrated. Sonication is used to convert these flowers into quasi-2D platelets with lateral sizes in the range of hundreds of nanometers and thicknesses in the range of tens of nanometers. These nanoplatelets can be combined with carbon nanotubes to form porous, conductive composites which can be used as electrodes in lithium-ion batteries. Using a standard activation process, these anodes display good cycling stability, reasonable rate performance and low-rate capacities approaching 1500 mAh g-1 , consistent with the current state-of-the-art for Fe2 O3 . However, by using an extended activation process, it is found that the morphology of these composites can be significantly changed, rendering the iron oxide amorphous and significantly increasing the porosity and internal surface area. These morphological changes yield anodes with very good cycling stability and low-rate capacity exceeding 2000 mAh g-1 , which is competitive with the best anode materials in the literature. However, the data implies that, after activation, the iron oxide displays a reduced solid-state lithium-ion diffusion coefficient resulting in somewhat degraded rate performance.
RESUMO
There has been growing interest in the synthesis of efficient reversible oxygen electrodes for both the oxygen reduction reaction (ORR) and the oxygen evolution reactions (OER), for their potential use in a variety of renewable energy technologies, such as regenerative fuel cells and metal-air batteries. Here, a bi-functional electrocatalyst, derived from a novel dicyanamide based nitrogen rich MOF {[Co(bpe)2 (N(CN)2 )]â (N(CN)2 )â (5 H2 O)}n [Co-MOF-1, bpe=1,2-bis(4-pyridyl)ethane, N(CN)2- =dicyanamide] under different pyrolysis conditions is reported. Pyrolysis of the Co-MOF-1 under Ar atmosphere (at 800 °C) yielded a Co nanoparticle-embedded N-doped carbon nanotube matrix (Co/NCNT-Ar) while pyrolysis under a reductive H2 /Ar atmosphere (at 800 °C) and further mild calcination yielded Co3 O4 @Co core-shell nanoparticle-encapsulated N-doped carbon nanotubes (Co3 O4 @Co/NCNT). Both catalysts show bi-functional activity towards ORR and OER, however, the core-shell Co3 O4 @Co/NCNT nanostructure exhibited superior electrocatalytic activity for both the ORR with a potential of 0.88â V at a current density of -1â mA cm-2 and the OER with a potential of 1.61â V at 10â mA cm-2 , which is competitive with the most active bi-functional catalysts reported previously.
RESUMO
Highly active electrocatalysts for the oxygen evolution (OER) reaction are in most cases powder nanomaterials, which undergo substantial changes upon applying the high potentials required for high-current-density oxygen evolution. Owing to the vigorous gas evolution, the durability under OER conditions is disappointingly low for most powder electrocatalysts as there are no strategies to securely fix powder catalysts onto electrode surfaces. Thus reliable studies of catalysts during or after the OER are often impaired. Herein, we propose the use of composites made from precursors of polybenzoxazines and organophilically modified NiFe layered double hydroxides (LDHs) to form a stable and highly conducting catalyst layer, which allows the study of the catalyst before and after electrocatalysis. Characterization of the material by XRD, SEM, and TEM before and after 100â h electrolysis in 5 m KOH at 60 °C and a current density of 200â mA cm-2 revealed previously not observed structural changes.
RESUMO
Here, we demonstrate the production of 2D nanosheets of arsenic disulfide (As2S3) via liquid-phase exfoliation of the naturally occurring mineral, orpiment. The resultant nanosheets had mean lateral dimensions and thicknesses of 400 and 10 nm, and had structures indistinguishable from the bulk. The nanosheets were solution mixed with carbon nanotubes and cast into nanocomposite films for use as anodes in potassium-ion batteries. These anodes exhibited outstanding electrochemical performance, demonstrating an impressive discharge capacity of 619 mAh/g at a current density of 50 mA/g. Even after 1000 cycles at 500 mA/g, the anodes retained an impressive 94% of their capacity. Quantitative analysis of the rate performance yielded a capacity at a very low rate of 838 mAh/g, about two-thirds of the theoretical capacity of As2S3 (1305 mAh/g). However, this analysis also implied As2S3 to have a very small solid-state diffusion coefficient (â¼10-17 m2/s), somewhat limiting its potential for high-rate applications.
RESUMO
Resonance Raman spectroscopy is a powerful analytical tool for detecting and identifying analytes, but the associated strong fluorescence background severely limits the use of the technique. Here, we show that by attaching ß-cyclodextrin (ß-CD) cavities to reduced graphene-oxide (rGO) sheets we obtain a water dispersible material (ß-CD: rGO) that combines the hydrophobicity associated with rGO with that of the cyclodextrin cavities and provides a versatile platform for resonance Raman detection. Planar aromatic and dye molecules that adsorb on the rGO domains and nonplanar molecules included within the tethered ß-CD cavities have their fluorescence effectively quenched. We show that it is possible using the water dispersible ß-CD: rGO sheets to record the resonance Raman spectra of adsorbed and included organic chromophores directly in aqueous media without having to extract or deposit on a substrate. This is significant, as it allows us to identify and estimate organic analytes present in water by resonance Raman spectroscopy.
RESUMO
Cobalt oxide (Co3O4)-based nanostructures have the potential as low-cost materials for lithium-ion (Li-ion) and sodium-ion (Na-ion) battery anodes with a theoretical capacity of 890 mAh/g. Here, we demonstrate a novel method for the production of Co3O4 nanoplatelets. This involves the growth of flower-like cobalt oxyhydroxide (CoOOH) nanostructures at a polarized liquid|liquid interface, followed by conversion to flower-like Co3O4 via calcination. Finally, sonication is used to break up the flower-like Co3O4 nanostructures into two-dimensional (2D) nanoplatelets with lateral sizes of 20-100 nm. Nanoplatelets of Co3O4 can be easily mixed with carbon nanotubes to create nanocomposite anodes, which can be used for Li-ion and Na-ion battery anodes without any additional binder or conductive additive. The resultant electrodes display impressive low-rate capacities (at 125 mA/g) of 1108 and 1083 mAh/g, for Li-ion and Na-ion anodes, respectively, and stable cycling ability over >200 cycles. Detailed quantitative rate analysis clearly shows that Li-ion-storing anodes charge roughly five times faster than Na-ion-storing anodes.
RESUMO
Reduced-graphene oxide (rGO) sheets have been functionalized by covalently linking ß-cyclodextrin (ß-CD) cavities to the sheets via an amide linkage. The functionalized ß-CD:rGO sheets, in contrast to rGO, are dispersible over a wide range of pH values (2-13). Zeta potential measurements indicate that there is more than one factor responsible for the dispersibility. We show here that planar aromatic molecules adsorbed on the rGO sheet as well as nonplanar molecules included in the tethered ß-CD cavities have their fluorescence effectively quenched by the ß-CD:rGO sheets. The ß-CD:rGO sheets combine the hydrophobicity associated with rGO along with the hydrophobicity of the cyclodextrin cavities in a single water-dispersible material.
RESUMO
The need for sustainable catalysts for an efficient hydrogen evolution reaction is of significant interest for modern society. Inspired by comparable structural properties of [FeNi]-hydrogenase, here we present the natural ore pentlandite (Fe4.5Ni4.5S8) as a direct 'rock' electrode material for hydrogen evolution under acidic conditions with an overpotential of 280 mV at 10 mA cm(-2). Furthermore, it reaches a value as low as 190 mV after 96 h of electrolysis due to surface sulfur depletion, which may change the electronic structure of the catalytically active nickel-iron centres. The 'rock' material shows an unexpected catalytic activity with comparable overpotential and Tafel slope to some well-developed metallic or nanostructured catalysts. Notably, the 'rock' material offers high current densities (≤650 mA cm(-2)) without any loss in activity for approximately 170 h. The superior hydrogen evolution performance of pentlandites as 'rock' electrode labels this ore as a promising electrocatalyst for future hydrogen-based economy.
RESUMO
Aqueous dispersions of graphene oxide (GO) exhibit strong pH-dependent fluorescence in the visible that originates, in part, from the oxygenated functionalities present. Here we examine the spectral migration on nanosecond time-scales of the pH dependent features in the fluorescence spectra. We show, from time-resolved emission spectra (TRES) constructed from the wavelength dependent fluorescence decay curves, that the migration is associated with excited state proton transfer. Both 'intramolecular' and 'intermolecular' transfer involving the quasi-molecular oxygenated aromatic fragments are observed. As a prerequisite to the time-resolved measurements, we have correlated the changes in the steady state fluorescence spectra with the sequence of dissociation events that occur in GO dispersions at different values of pH.
RESUMO
The chemistry underlying the aqueous dispersibility of graphene oxide (GO) and reduced graphene oxide (r-GO) is a key consideration in the design of solution processing techniques for the preparation of processable graphene sheets. Here, we use zeta potential measurements, pH titrations, and infrared spectroscopy to establish the chemistry underlying the aqueous dispersibility of GO and r-GO sheets at different values of pH. We show that r-GO sheets have ionizable groups with a single pK value (8.0) while GO sheets have groups that are more acidic (pK = 4.3), in addition to groups with pK values of 6.6 and 9.0. Infrared spectroscopy has been used to follow the sequence of ionization events. In both GO and r-GO sheets, it is ionization of the carboxylic groups that is primarily responsible for the build up of charge, but on GO sheets, the presence of phenolic and hydroxyl groups in close proximity to the carboxylic groups lowers the pKa value by stabilizing the carboxylate anion, resulting in superior water dispersibility .