Study of CuO Nanowire Growth on Different Copper Surfaces.

Cupric oxide (CuO) nanowires were produced by thermal oxidation of copper surfaces at temperatures up to 450 °C. Three different surfaces, namely a copper foil as well as evaporation deposited copper and an application relevant sputtered copper film on Si(100) substrates were characterized ex-situ before and after the experiment. The development of oxide layers and nanowires were monitored in-situ using grazing incidence small angle X-ray scattering. The number density of nanowires is highest for the sputtered surface and lowest for the surface prepared by evaporation deposition. This can be linked to different oxide grain sizes and copper grain boundary diffusions on the different surfaces. Small grains of the copper substrate and high surface roughness thereby lead to promoted growth of the nanowires.

A new device for high-temperature in situ GISAXS measurements.

A heating stage originally designed for diffraction experiments is implemented into a Bruker NANOSTAR instrument for in situ grazing incidence small-angle x-ray scattering experiments. A controlled atmosphere is provided by a dome separating the sample environment from the evacuated scattering instrument. This dome is double shelled in order to enable cooling water to flow through it. A mesoporous silica film templated by a self-assembled block copolymer system is investigated in situ during step-wise heating in air. The GISAXS pattern shows the structural development of the ordered lattice of parallel cylindrical pores. The deformation of the elliptical pore-cross section perpendicular to the film surface was studied with increasing temperature. Moreover, the performance of the setup was tested by controlled in situ heating of a copper surface under controlled oxygen containing atmosphere.

Synergy of multi-scale toughening and protective mechanisms at hierarchical branch-stem interfaces.

Biological materials possess a variety of artful interfaces whose size and properties are adapted to their hierarchical levels and functional requirements. Bone, nacre, and wood exhibit an impressive fracture resistance based mainly on small crystallite size, interface organic adhesives and hierarchical microstructure. Currently, little is known about mechanical concepts in macroscopic biological interfaces like the branch-stem junction with estimated 10(14) instances on earth and sizes up to few meters. Here we demonstrate that the crack growth in the upper region of the branch-stem interface of conifer trees proceeds along a narrow predefined region of transversally loaded tracheids, denoted as sacrificial tissue, which fail upon critical bending moments on the branch. The specific arrangement of the tracheids allows disconnecting the overloaded branch from the stem in a controlled way by maintaining the stem integrity. The interface microstructure based on the sharply adjusted cell orientation and cell helical angle secures a zig-zag crack propagation path, mechanical interlock closing after the bending moment is removed, crack gap bridging and self-repairing by resin deposition. The multi-scale synergetic concepts allows for a controllable crack growth between stiff stem and flexible branch, as well as mechanical tree integrity, intact physiological functions and recovery after the cracking.