Chloride Insertion-Immobilization Enables Bright, Narrowband, and Stable Blue-Emitting Perovskite Diodes.

Metal halide perovskites show promise for light-emitting diodes (LEDs) owing to their facile manufacture and excellent optoelectronic performance, including high color purity and spectral stability, especially in the green region. However, for blue perovskite LEDs, the emission spectrum line width is broadened to over 25 nm by the coexistence of multiple reduced-dimensional perovskite domains, and the spectral stability is poor, with an undesirable shift (over 7 nm) toward longer wavelengths under operating conditions, degradation that occurs due to phase separation when mixed halides are employed. Here we demonstrate chloride insertion-immobilization, a strategy that enables blue perovskite LEDs, the first to exhibit narrowband (line width of 18 nm) and spectrally stable (no wavelength shift) performance. We prepare bromide-based perovskites and then employ organic chlorides for dynamic treatment, inserting and in situ immobilizing chlorides to blue-shift and stabilize the emission. We achieve sky-blue LEDs with a record luminance over 5100 cd/m2 at 489 nm, and an operating half-life of 51 min at 1500 cd/m2. By device structure optimization, we further realize an improved EQE of 5.2% at 479 nm and an operating half-life of 90 min at 100 cd/m2.

Electro-Optic Modulation Using Metal-Free Perovskites.

Electro-optic (EO) modulation is of interest to impart information onto an optical carrier. Inorganic crystals-most notably LiNbO3 and BaTiO3-exhibit EO modulation and good stability, but are difficult to integrate with silicon photonic technology. Solution-processed organic EO materials are readily integrated but suffer from thermal degradation at the temperatures required in operating conditions for accelerated reliability studies. Hybrid organic-inorganic metal halide perovskites have the potential to overcome these limitations; however, these have so far relied on heavy metals such as lead and cadmium. Here, we report linear EO modulation using metal-free perovskites, which maintain the crystalline features of the inorganic EO materials and incorporate the flexible functionality of organic EO chromophores. We find that, by introducing a deficiency of cations, we reduce the symmetry in the perovskite crystal and produce thereby an increased EO response. The best-engineered perovskites reported herein showcase an EO coefficient of 14 pm V-1 at a modulation frequency of 80 kHz, an order of magnitude higher than in the nondefective materials. We observe split peaks in the X-ray diffraction and neutron diffraction patterns of the defective sample, indicating that the crystalline structure has been distorted and the symmetry reduced. Density functional theory (DFT) studies link this decreased symmetry to NH4+ deficiencies. This demonstration of EO from metal-free perovskites highlights their potential in next-generation optical information transmission.