Fully automated measurement system for temperature-dependent X-ray total scattering at beamline BL04B2 at SPring-8.

Data-driven approaches in materials science demand the collection of large amounts of data on the target materials at synchrotron beamlines. To accurately gather suitable experimental data, it is essential to establish fully automated measurement systems to reduce the workload of the beamline staff. Moreover, the recent COVID-19 pandemic has further emphasized the necessity of automated and/or remote measurements at synchrotron beamlines. Here, the installation of a new sample changer combined with a high-temperature furnace and a fully automated alignment system on beamline BL04B2 at SPring-8 is reported. The system allows X-ray total scattering measurements of up to 21 samples at different temperatures (from room temperature to 1200°C) to be conducted without any human assistance.

Time-resolved pair distribution function analysis of disordered materials on beamlines BL04B2 and BL08W at SPring-8.

A dedicated apparatus has been developed for studying structural changes in amorphous and disordered crystalline materials substantially in real time. The apparatus, which can be set up on beamlines BL04B2 and BL08W at SPring-8, mainly consists of a large two-dimensional flat-panel detector and high-energy X-rays, enabling total scattering measurements to be carried out for time-resolved pair distribution function (PDF) analysis in the temperature range from room temperature to 873 K at pressures of up to 20 bar. For successful time-resolved analysis, a newly developed program was used that can monitor and process two-dimensional image data simultaneously with the data collection. The use of time-resolved hardware and software is of great importance for obtaining a detailed understanding of the structural changes in disordered materials, as exemplified by the results of commissioned measurements carried out on both beamlines. Benchmark results obtained using amorphous silica and demonstration results for the observation of sulfide glass crystallization upon annealing are introduced.

Efficient Decarbonylation of Furfural to Furan Catalyzed by Zirconia-Supported Palladium Clusters with Low Atomicity.

Decarbonylation of furfural to furan was efficiently catalyzed by ZrO2 -supported Pd clusters in the liquid phase under a N2 atmosphere without additives. Although Pd/C and Pd/Al2 O3 have frequently been used for decarbonylation, Pd/ZrO2 exhibited superior catalytic performance compared with these conventional catalysts. Transmission electron microscopy and X-ray absorption fine structure measurements revealed that the size of the Pd particles decreased with an increase in the specific surface area of ZrO2 . ZrO2 with a high surface area immobilized Pd as clusters consisting of several (three to five) Pd atoms, whereas Pd aggregated to form nanoparticles on other supports such as carbon and Al2 O3 despite their high surface areas. The catalytic activity of Pd/ZrO2 was enhanced with a decrease in particle size, and the smallest Pd/ZrO2 was the most active catalyst for decarbonylation. When CeO2 was used as the support, a decrease in Pd particle size with an increase in surface area was also observed. Single Pd atoms were deposited on CeO2 with a high surface area, with a strong interaction through the formation of a Pd-O-Ce bond, which led to a lower catalytic activity than that of Pd/ZrO2 . This result suggests that zero-valent small Pd clusters consisting of more than one Pd atom are the active species for the decarbonylation reaction. Recycling tests proved that Pd/ZrO2 maintained its catalytic activity until its sixth use.