The Highly Durable Antibacterial Gel-like Coatings for Textiles.

Hospital-acquired infections are considered a priority for public health systems, which poses a significant burden for society. High-touch surfaces of healthcare centers, including textiles, provide a suitable environment for pathogenic bacteria to grow, necessitating incorporating effective antibacterial agents into textiles. This paper introduces a highly durable antibacterial gel-like solution, Silver Shell finish, which contains chitosan-bound silver chloride microparticles. The study investigates the coating's environmental impact, health risks, and durability during repeated washing. The structure of the Silver Shell finish was studied using Transmission Electron Microscopy (TEM) and Energy-Dispersive X-ray Spectroscopy (EDX). TEM images showed a core-shell structure, with chitosan forming a protective shell around groupings of silver micro-particles. Field Emission Scanning Electron Microscopy (FESEM) demonstrated the uniform deposition of Silver Shell on the surface of fabrics. AATCC Test Method 100 was employed to quantitatively analyze the antibacterial properties of fabrics coated with silver microparticles. Two types of bacteria, Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) were used in this study. The antibacterial results showed that after 75 wash cycles, a 100% reduction for both S. aureus and E. coli in the coated samples using crosslinking agents was observed. The coated samples without a crosslinking agent exhibited a 99.88% and 99.81% reduction for S. aureus and E. coli after 50 washing cycles. AATCC-147 was performed to investigate the coated samples' leaching properties and the crosslinking agent's effect against S. aureus and E. coli. All coated samples demonstrated remarkable antibacterial efficacy even after 75 wash cycles.

The Highly Durable Antibacterial Gel-like Coatings for Textiles.

Hospital-acquired infections are considered a priority for public health systems since they pose a significant burden for society. High-touch surfaces of healthcare centers, including textiles, provide a suitable environment for pathogenic bacteria to grow, necessitating incorporating effective antibacterial agents into textiles. This paper introduces a highly durable antibacterial gel-like solution, Silver Shell™ finish, which contains chitosan-bound silver chloride microparticles. The study investigates the coating's environmental impact, health risks, and durability during repeated washing. The structure of the Silver Shell™ finish was studied using transmission electron microscopy (TEM) and energy-dispersive X-ray spectroscopy (EDX). The TEM images showed a core-shell structure, with chitosan forming a protective shell around groupings of silver microparticles. The field-emission scanning electron microscopy (FESEM) demonstrated the uniform deposition of Silver Shell™ on the surfaces of the fabrics. AATCC Test Method 100 was employed to quantitatively analyze the antibacterial properties of the fabrics coated with silver microparticles. Two types of bacteria, Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli), were used in this study. The antibacterial results showed that after 75 wash cycles, a 100% reduction for both S. aureus and E. coli in the coated samples using crosslinking agents was observed. The coated samples without a crosslinking agent exhibited 99.88% and 99.81% reductions for S. aureus and E. coli after 50 washing cycles. To compare the antibacterial properties toward non-pathogenic and pathogenic strains of the same species, MG1655 model E. coli strain (ATCC 29213) and a multidrug-resistant clinical isolate were used. The results showed the antibacterial efficiency of the Silver ShellTM solution (up to 99.99% reduction) coated on cotton fabric. AATCC-147 was performed to investigate the coated samples' leaching properties and the crosslinking agent's effects against S. aureus and E. coli. All coated samples demonstrated remarkable antibacterial efficacy, even after 75 wash cycles. The crosslinking agent facilitated durable attachment between the silver microparticles and cotton substrate, minimizing the release of particles from the fabrics. Color measurements were conducted to assess the color differences resulting from the coating process. The results indicated fixation values of 44%, 32%, and 28% following 25, 50, and 75 washing cycles, respectively.

Electrospun Nanomaterials Based on Cellulose and Its Derivatives for Cell Cultures: Recent Developments and Challenges.

The development of electrospun nanofibers based on cellulose and its derivatives is an inalienable task of modern materials science branches related to biomedical engineering. The considerable compatibility with multiple cell lines and capability to form unaligned nanofibrous frameworks help reproduce the properties of natural extracellular matrix and ensure scaffold applications as cell carriers promoting substantial cell adhesion, growth, and proliferation. In this paper, we are focusing on the structural features of cellulose itself and electrospun cellulosic fibers, including fiber diameter, spacing, and alignment responsible for facilitated cell capture. The study emphasizes the role of the most frequently discussed cellulose derivatives (cellulose acetate, carboxymethylcellulose, hydroxypropyl cellulose, etc.) and composites in scaffolding and cell culturing. The key issues of the electrospinning technique in scaffold design and insufficient micromechanics assessment are discussed. Based on recent studies aiming at the fabrication of artificial 2D and 3D nanofiber matrices, the current research provides the applicability assessment of the scaffolds toward osteoblasts (hFOB line), fibroblastic (NIH/3T3, HDF, HFF-1, L929 lines), endothelial (HUVEC line), and several other cell types. Furthermore, a critical aspect of cell adhesion through the adsorption of proteins on the surfaces is touched upon.

Fibrous Polymer-Based Composites Obtained by Electrospinning for Bone Tissue Engineering.

Currently, the significantly developing fields of tissue engineering related to the fabrication of polymer-based materials that possess microenvironments suitable to provide cell attachment and promote cell differentiation and proliferation involve various materials and approaches. Biomimicking approach in tissue engineering is aimed at the development of a highly biocompatible and bioactive material that would most accurately imitate the structural features of the native extracellular matrix consisting of specially arranged fibrous constructions. For this reason, the present research is devoted to the discussion of promising fibrous materials for bone tissue regeneration obtained by electrospinning techniques. In this brief review, we focus on the recently presented natural and synthetic polymers, as well as their combinations with each other and with bioactive inorganic incorporations in order to form composite electrospun scaffolds. The application of several electrospinning techniques in relation to a number of polymers is touched upon. Additionally, the efficiency of nanofibrous composite materials intended for use in bone tissue engineering is discussed based on biological activity and physiochemical characteristics.