Current changes toward a more biobased economy have recently created tremendous renewed interest in using lignin as a valuable source for chemicals and materials. Here, we present a facile cationization approach aiming to impart kraft lignin water-solubility, with similar good features as lignosulfonates. Eucalyptus globulus kraft lignin obtained from a paper mill black liquor by applying the LignoBoost process was used as the substrate. Its reaction with 3-chloro-2-hydroxypropyl-trimethylammonium chloride (CHPTAC) in an aqueous alkaline medium was studied to assess the impact of different reaction conditions (temperature, time, educt concentration, molar CHPTAC-to-lignin ratio) on the degree of cationization. It has been shown that at pH 13, 10 wt % lignin content, 70 °C, and 3 h reaction time, a CHPTAC-to-lignin minimum molar ratio of 1.3 is required to obtain fully water-soluble products. Elemental analysis (4.2% N), size-exclusion chromatography (M w 2180 Da), and quantitative 13C NMR spectroscopy of the product obtained at this limit reactant concentration suggest introduction of 1.2 quaternary ammonium groups per C9 unit and substitution of 75% of the initially available phenolic OH groups. The possible contribution of benzylic hydroxyls to the introduction of quaternary ammonium moieties through a quinone methide mechanism has been proposed. Since both molecular characteristics and degree of substitution, and hence solubility or count of surface charge, of colloidal particles can be adjusted within a wide range, cationic kraft lignins are promising materials for a wide range of applications, as exemplarily demonstrated for flocculation of anionic dyes.
RESUMO
All-lignin coating formulations were prepared while combining water-soluble cationic kraft lignin (quaternized LignoBoost®, CL) and anionic lignosulphonate (LS). The electrostatic attraction between positively charged CL and negatively charged LS led to the formation of insoluble self-organized macromolecule aggregates that align to films. The structures of the formed layers were evaluated by atomic force microscopy (AFM), firstly on glass lamina using dip-coating deposition and then on handsheets and industrial uncoated paper using roll-to-roll coating in a layer-by-layer mode. Coated samples were also characterized by optical microscopy, scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (SEM/EDS), and contact angle measurements. It was suggested that the structure of all-lignin aggregates is the result of the interaction of amphiphilic water-soluble lignin molecules leading to their specifically ordered mutual arrangement depending on the order and the mode of their application on the surface. The all-lignin coating of cellulosic fiber imparts lower air permeability and lower free surface energy to paper, mainly due to a decrease in surface polarity, thus promoting the paper's hydrophobic properties. Moderate loading of lignin coating formulations (5-6 g m-2) did not affect the mechanical strength of the paper.