In this study, nanocomposites based on polypropylene are synthesized by the in situ polymerization of propene in the presence of mesoporous SBA-15 silica, which acts as a carrier of the catalytic system (zirconocene as catalyst and methylaluminoxane as cocatalyst). The protocol for the immobilization and attainment of hybrid SBA-15 particles involves a pre-stage of contact between the catalyst with cocatalyst before their final functionalization. Two zirconocene catalysts are tested in order to attain materials with different microstructural characteristics, molar masses and regioregularities of chains. Some polypropylene chains are able to be accommodated within the silica mesostructure of these composites. Thus, an endothermic event of small intensity appears during heating calorimetric experiments at approximately 105 °C. The existence of these polypropylene crystals, confined within the nanometric channels of silica, is corroborated by SAXS measurements obtained via the change in the intensity and position of the first-order diffraction of SBA-15. The incorporation of silica also has a very significant effect on the rheological response of the resultant materials, leading to important variations in various magnitudes, such as the shear storage modulus, viscosity and δ angle, when a comparison is established with the corresponding neat iPP matrices. Rheological percolation is reached, thus demonstrating the role of SBA-15 particles as filler, in addition to the supporting role that they exert during the polymerizations.
Assuntos
Nanocompostos , Polipropilenos , Polimerização , Polipropilenos/química , Metalocenos , Peso Molecular , Espalhamento a Baixo Ângulo , Difração de Raios X , Nanocompostos/química , Dióxido de Silício/químicaRESUMO
Nanocomposites based on isotactic polypropylene (iPP) and mesoporous silica particles of either MCM-41 or SBA-15 were prepared by melt extrusion. The effect of the silica incorporated into an iPP matrix was firstly detected in the degradation behavior and in the rheological response of the resultant composites. Both were ascribed, in principle, to variations in the inclusion of iPP chains within these two mesostructures, with well different pore size. DSC experiments did not provide information on the existence of confinement in the iPP-MCM-41 materials, whereas a small endotherm, located at about 100 °C and attributed to the melting of confined crystallites, is clearly observed in the iPP-SBA-15 composites. Real-time variable-temperature Small Angle X-ray Scattering (SAXS) experiments with synchrotron radiation turned out to be crucial to finding the presence of iPP within MCM-41 pores. From these measurements, precise information was also deduced on the influence of the MCM-41 on iPP long spacing since overlapping does not occur between most probable iPP long spacing peak with the characteristic diffractions from the MCM-41 hexagonal nanostructure in comparison with existing superposition in SBA-15-based materials.