Dual Catalytic and Self-Assembled Growth of Two-Dimensional Transition Metal Dichalcogenides Through Simultaneous Predeposition Process.

The recent introduction of alkali metal halide catalysts for chemical vapor deposition (CVD) of transition metal dichalcogenides (TMDs) has enabled remarkable two-dimensional (2D) growth. However, the process development and growth mechanism require further exploration to enhance the effects of salts and understand the principles. Herein, simultaneous predeposition of a metal source (MoO3 ) and salt (NaCl) by thermal evaporation is adopted. As a result, remarkable growth behaviors such as promoted 2D growth, easy patterning, and potential diversity of target materials can be achieved. Step-by-step spectroscopy combined with morphological analyses reveals a reaction path for MoS2 growth in which NaCl reacts separately with S and MoO3 to form Na2 SO4 and Na2 Mo2 O7 intermediates, respectively. These intermediates provide a favorable environment for 2D growth, including an enhanced source supply and liquid medium. Consequently, large grains of monolayer MoS2 are formed by self-assembly, indicating the merging of small equilateral triangular grains on the liquid intermediates. This study is expected to serve as an ideal reference for understanding the principles of salt catalysis and evolution of CVD in the preparation of 2D TMDs.

Mesoporous Metal Fluoride Nanocomposite Films with Tunable Optical Properties Derived from Precursor Instability.

The precisely tailored refractive index of optical materials is the key to utilizing and manipulating light during its propagation through the matrix, thereby improving their application performances. In this paper, mesoporous metal fluoride films with engineered composition (MgF2 :LaF3 ) are demonstrated to achieve finely tunable refractive indices. These films are prepared using a precursor-derived one-step assembly approach via the simple mixing of precursor solutions (Mg(CF3 OO)2 and La(CF3 OO)3 ); then pores are formed simultaneously during solidification owing to the inherent instability of La(CF3 OO)3 . The mesoporous structures are realized through Mg(CF3 OO)2 and La(CF3 OO)3 ions, which interacted with each other based on their electrostatic forces, providing a wide range of refractive indices (from 1.37 to 1.16 at 633 nm). Furthermore, it is systematically several MgF2(1-x) -LaF3(x) layers with different compositions (x = 0.0, 0.3, and 0.5) to form the graded refractive index coating that is optically consecutive between the substrate and the air for broadband and omnidirectional antireflection. An average transmittance of ≈98.03% (400-1100 nm) is achieved with a peak transmittance of ≈99.04% (at 571 nm), and the average antireflectivity is maintained at ≈15.75% even at an incidence of light of 65° (400-850 nm).