Synthesis and magnetic properties of Fe3C-C core-shell nanoparticles.

Fe3C-C core-shell nanoparticles were fabricated on a large scale by metal-organic chemical vapor deposition at 700 °C with ferric acetylacetonate as the precursor. Analysis results of x-ray diffraction, transmission electron microscope and Raman spectroscope showed that the Fe3C cores with an average diameter of ∼35 nm were capsulated by the graphite-like C layers with the thickness of 2-5 nm. The comparative experiments revealed that considerable Fe3O4-Fe3C core-shell nanoparticles and C nanotubes were generated simultaneously at 600 and 800 °C, respectively. A formation mechanism was proposed for the as-synthesized core-shell nanostructures, based on the temperature-dependent catalytic activity of Fe3C nanoclusters and the coalescence process of Fe3C-C nanoclusters. The Fe3C-C core-shell nanoparticles exhibited a saturation magnetization of 23.6 emu g(-1) and a coercivity of 550 Oe at room temperature.

The Multifunctionality of Lanthanum-Strontium Cobaltite Nanopowder: High-Pressure Magnetic Studies and Excellent Electrocatalytic Properties for OER.

Simultaneous study of magnetic and electrocatalytic properties of cobaltites under extreme conditions expands the understanding of physical and chemical processes proceeding in them with the possibility of their further practical application. Therefore, La0.6Sr0.4CoO3 (LSCO) nanopowders were synthesized at different annealing temperatures tann = 850-900 °C, and their multifunctional properties were studied comprehensively. As tann increases, the rhombohedral perovskite structure of the LSCO becomes more single-phase, whereas the average particle size and dispersion grow. Co3+ and Co4+ are the major components. It has been found that LSCO-900 shows two main Curie temperatures, TC1 and TC2, associated with a particle size distribution. As pressure P increases, average ⟨TC1⟩ and ⟨TC2⟩ increase from 253 and 175 K under ambient pressure to 268 and 180 K under P = 0.8 GPa, respectively. The increment of ⟨dTC/dP⟩ for the smaller and bigger particles is sufficiently high and equals 10 and 13 K/GPa, respectively. The magnetocaloric effect in the LSCO-900 nanopowder demonstrates an extremely wide peak δTfwhm > 50 K that can be used as one of the composite components, expanding its working temperature window. Moreover, all LSCO samples showed excellent electrocatalytic performance for the oxygen evolution reaction (OER) process (overpotentials of only 265-285 mV at a current density of 10 mA cm-2) with minimal η10 for LSCO-900. Based on the experimental data, it was concluded that the formation of a dense amorphous layer on the surface of the particles ensures high stability as a catalyst (at least 24 h) during electrolysis in 1 M KOH electrolyte.