The developing of pretreatment method to break the biomass barrier of lignocellulosic is a challenging task for achieve high value utilization. A fast microwave-assisted choline chloride/1,2-propanediol/methyl isobutyl ketone biphasic system was constructed for pretreating Eucalyptus to the production of furfural and cellulose-rich residues and the extraction of lignin. Results showed that the combination of AlCl3·6H2O and HCl had the best catalytic ability for furfural production among the examined catalysts. Under the optimal conditions (140 °C, 15 min, 0.075 M AlCl3·6H2O, 0.05 M HCl), the furfural yield of 55.4 %, the glucose yield of 90.3 % and the delignification rate of 92.4 % could be achieved. Moreover, the extracted lignin samples with a low polydispersity (1.55-1.73) and molecular weight (1380-2040 g/mol) are promising to act as precursor for the value-add products processing. These findings demonstrated an ultrafast pretreatment process with excellent results in biomass fractionation and comprehensive utilization of biomass components.
Assuntos
Eucalyptus , Lignina , Lignina/química , Propilenoglicol , Furaldeído , Biomassa , Colina/química , Micro-Ondas , Solventes/química , HidróliseRESUMO
Deep eutectic solvents (DESs) have emerged as promising and eco-friendly solvents for the efficient extraction of lignin from biomass due to their low cost and environmental benefits. Nevertheless, the prevalent use of acidic DESs in lignin extraction often results in excessive depolymerization and recondensation of lignin, thereby impeding its downstream applications. In this study, we developed a range of alkaline DESs (ADESs), both pure and peroxide-containing, for the extraction of high-quality lignin from bamboo. Moreover, carbon dioxide (CO2) was employed for the precipitation and regeneration of the extracted lignin. The obtained lignin fractions were comprehensively characterized in terms of yield, purity, morphology, solubility, structural features, and anti-UV/oxidant activity. The results showed that the monoethanolamine-based ADES demonstrated superior performance among the pure ADESs. Structural analysis confirmed the well-preserved substructures of lignin fractions obtained using ADESs, with ß-O-4 bond retention ranging from 49.8 % to 68.4 %. The incorporation of a suitable amount of peroxide improved lignin yield, morphology, solubility, and anti-UV/oxidant activity. Additionally, the anti-UV/oxidant activity of lignin exhibited a positive correlation with its phenolic hydroxyl content. This study provides a valuable reference for the green and sustainable production and valorization of lignin within the existing biorefinery framework.
Assuntos
Solventes Eutéticos Profundos , Lignina , Lignina/química , Solventes/química , Antioxidantes , Biomassa , Oxidantes , HidróliseRESUMO
In this study, light-colored lignin was extracted from bamboo shoot shells (BSS) using a hydrated deep eutectic solvent (DES) pretreatment. The hydrated DES used in pretreatment consist of formic acid, benzyl triethylammonium chloride (BTEAC) and water. The pretreatment using a hydrated DES containing 30% water (H30) demonstrate efficient delignification (82.9%). Additionally, the hydrated DES protected the ß-O-4 linkage from excessive cleavage and recondensation as well as keep the light-colored of lignin. Moreover, the hydrated DES extracted lignin exhibits superior antioxidant performance and tyrosinase inhibitory capacity compared to the control. Notably, incorporating 5% lignin of H30-extracted lignin into a commercial suncream led to a remarkable enhancement of the SPF value, elevating from 14.8 to 32.6. In summary, the proposed hydrated DES pretreatment method offers significant benefits for extracting light-colored lignin, thereby promoting the multifunctional application of lignin in cosmetics.
Assuntos
Solventes Eutéticos Profundos , Lignina , Solventes , Biomassa , Água , HidróliseRESUMO
Developing a biorefinery process for a highly integrated valorization and fractionation of lignocellulose is crucial for its utilization. Herein, a biphasic system comprising choline chloride/lactic acid and 2-methyltetrahydrofuran with Al2(SO4)3 and H2SO4 as catalysts was applied to pretreat Eucalyptus. Results showed that under the optimized conditions (150 °C, 30 min, 0.2 M Al2(SO4)3, 0.075 M H2SO4), the furfural yield and enzymatic hydrolysis efficiency could reach 54.7% and 97.0%, respectively. The efficient cellulose conversion was attributed to remarkable removal of lignin (91.0%) and hemicelluloses (100.0%), thereby causing the disruption of cell wall structure and enhancement of cellulose accessibility. Meanwhile, confocal Raman microscope and atomic force microscope displayed that the pretreatment resulted in the decreasing intensities of carbohydrates and lignin different regions of cell walls, and exposing of the embedded microfibers from noncellulosic polymers. Overall, the deep eutectic solvent-based biphasic system displayed high performance for effective utilization of carbohydrate components in lignocellulose.
Assuntos
Furaldeído , Lignina , Biomassa , Carboidratos , Celulose , Solventes Eutéticos Profundos , Hidrólise , Lignina/química , SolventesRESUMO
Bamboo processing residue, which is rich in parenchyma cells, was treated as huge waste in bamboo processing industry, such as reassemble bamboo and bamboo flooring. Herein, autohydrolysis and rapid different deep eutectic solvents (DES) delignification strategy were consecutively performed to remove hemicelluloses and lignin from bamboo processing residue. The xylooligosaccharides (XOS) with high yield (34.35%) was achieved in the autohydrolysis process. Results showed that alkaline DES pretreatment resulted in the highest glucose yield (88.22%) and relatively high delignification rate (83.75%) as well as well-preserved lignin structures. However, the lignin fractions obtained under acidic DES conditions were tending to assemble into lignin nanoparticles (LNPs) and having excellent antioxidant activity as compared to those obtained from alkaline DES system. In brief, the combination of autohydrolysis and rapid DES delignification can achieve orientated fractionation of the components from the industrialized bamboo.
Assuntos
Solventes Eutéticos Profundos , Lignina , Biomassa , Fracionamento Químico , Hidrólise , Lignina/química , Solventes/químicaRESUMO
BACKGROUND: Cocksfoot grass (Dactylis glomerata L.) with high biomass yield and rich cellulose can be used to produce bioethanol as fuel additive. In view of this, ultrasonic and hydrothermal pretreatments followed by successive alkali extractions were assembled into an integrated biorefinery process applied on cocksfoot grass to improve its enzymatic hydrolysis. In this work, the effects of ultrasonic and hydrothermal pretreatments followed by sequential alkali extractions on the enzymatic hydrolysis of cocksfoot grass were investigated. In addition, since large amount of hemicelluloses were released during the hydrothermal pretreatment and alkali extraction process, the yields, structural characteristics and differentials of water- and alkali-soluble hemicellulosic fractions isolated from different treatments were also comparatively explored. RESULTS: The integrated treatment significantly removed amorphous hemicelluloses and lignin, resulting in increased crystallinity of the treated residues. A maximum saccharification rate of 95.1% was obtained from the cellulose-rich substrate after the integrated treatment. In addition, the considerable hemicelluloses (31.4% water-soluble hemicelluloses and 53.4% alkali-soluble hemicelluloses) were isolated during the integrated treatment. The released water-soluble hemicellulosic fractions were found to be more branched as compared with the alkali-soluble hemicellulosic fractions and all hemicellulosic fractions were mixed polysaccharides mainly composed of branched xylans and ß-glucans. CONCLUSION: The combination of ultrasonic and hydrothermal pretreatments followed by successive alkali extractions can dramatically increase the enzymatic saccharification rate of the substrates and produce considerable amounts of hemicelluloses. Detailed information about the enzymatic hydrolysis rates of the treated substrates and the structural characteristics of the co-produced hemicelluloses will help the synergistic utilization of cellulose and hemicellulose in cocksfoot grass.
RESUMO
Herein, a two-step hydrothermal pretreatment combined with alkali extraction method was applied to deconstruct the poplar cell walls for enzymatic hydrolysis. Results revealed that 88.1 % of hemicelluloses and 77.6 % of lignin were removed during the integrated treatment performed at 180 °C and a maximum enzymatic hydrolysis efficiency of 96.1 % was achieved. Confocal Raman microscopy suggested that the removal of hemicelluloses from cell walls was inhomogeneous, and most hemicelluloses were released from the secondary wall. In addition, 35.2-56.8 % of hemicelluloses were isolated from the integrated treatment. Detailed structural analysis revealed that the water-soluble hemicelluloses possessed more branched structure than the alkali-soluble hemicelluloses and the hemicelluloses isolated from the poplar were mainly composed of a linear backbone of (1â4)-ß-d-Xylp with 4-O-Me-α-d-GlcpA attached as side chains. This work provides an efficient pathway to transform poplar into fermentable sugars and hemicelluloses with considerable yield.
RESUMO
Hereon, tobacco stalk was deconstructed by lyophilization, ball-milling, ultrasound-assisted alkali extraction, hydrothermal pretreatment (HTP), and alkali presoaking, respectively, followed by dilute alkali cooking to both improve its enzymatic digestibility and isolate the hemicellulosic streams. It was found that a maximum cellulose saccharification rate of 93.5% was achieved from the integrated substrate by ball-milling and dilute alkali cooking, which was 4.4-fold higher than that from the raw material. Interestingly, in this case, 76.9% of hemicelluloses were simultaneously recovered during the integrated treatment. Structural determination indicated that the hemicelluloses released from tobacco stalk by dilute alkali cooking were mixed polysaccharides, and the (1 â 4)-linked ß-D-Xylp backbone branched with L-Araf units at O-2/O-3 and 4-O-Me-α-D-GlcpA units at O-2 of the xylose residues was the main structure. In comparison, ultrasound-assisted alkali extraction, ball-milling, and HTP favored the extraction of hemicelluloses with less branched structure and lower molecular weights in the following alkali cooking.