Selective synthesis of Zn(1 - x)Mn(x)Se nanobelts and nanotubes from [Zn(1 - x)Mn(x)Se](DETA)0.5 nanbelts in solution (x = 0-0.15) and their EPR and optical properties.

Zn(1 - x)Mn(x)Se (x = 0-0.15) nanobelts and nanotubes can be synthesized via the removal of diethylenetriamine (DETA) in 1-octadecene (ODE) and ethylene glycol (EG), respectively, using [Zn(1 - x)Mn(x)Se](DETA)(0.5) nanobelts as a template. The as-prepared ZnSe nanobelts are single-crystalline and grown along the [001] direction, and the ZnSe nanotubes consist of nanoparticles assembled along the [001] direction. In addition, Mn(2+)-doped Zn(1 - x)Mn(x)Se (x = 0.05, 0.10, 0.15) nanotubes are prepared for the first time if doped [Zn(1 - x)Mn(x)Se](DETA)(0.5) nanobelts are used as the template. The formation process of Zn(1 - x)Mn(x)Se nanobelts and nanotubes has been studied, and a plausible mechanism is proposed. Photoluminescence (PL) and electron paramagnetic resonance (EPR) spectra of Zn(1 - x)Mn(x)Se nanobelts and Zn(1 - x)Mn(x)Se nanotubes have been investigated.

High yield synthesis of matchstick-like PbS nanocrystals using mesoporous organosilica as template.

A simple hard template method has been developed to prepare uniform matchstick-like PbS nanocrystals. The approach combines functionalization of the mesoporous walls and channel surface with thioether groups, adsorption of Pb2+, and heating in an N2 atmosphere at high temperature. The structure, morphology and composition of the nanocrystals have been characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), energy dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The optical properties of the matchstick-like PbS nanocrystals have been systematically investigated by Raman spectroscopy, UV-visible absorption spectroscopy (UV-vis), and photoluminescence spectroscopy (PL). These results demonstrate that these matchstick-like PbS nanocrystals are single crystals and possess novel optical properties, suggesting that they may have many potential applications. A large blue shift is observed in the photoluminescence spectrum, and this clearly shows the quantum size effects of the matchstick-like PbS . Furthermore, a growth mechanism of the PbS heteronanostructure is proposed.