Giant magnetoresistance in non-magnetic phosphoric acid doped polyaniline silicon nanocomposites with higher magnetic field sensing sensitivity.

Phosphoric acid doped conductive polyaniline (PANI) polymer nanocomposites (PNCs) reinforced with silicon nanopowders have been successfully synthesized using a facile surface initiated polymerization (SIP) method. The chemical structures of the nanocomposites are characterized using Fourier transform infrared (FT-IR) spectroscopy. The enhanced thermal stability of the silicon-PANI PNCs compared with pure PANI is obtained using thermogravimetric analysis (TGA). The obtained optical band gap of the PNCs using Ultraviolet-visible diffuse reflectance spectroscopy (UV-vis DRS) decreases with increasing silicon loading. The dielectric properties of the PNCs are strongly related to the silicon loading level. Temperature dependent resistivity analysis reveals a quasi 3-D variable range hopping (VRH) electrical conduction mechanism for the synthesized PNCs. Room temperature giant magnetoresistance (GMR) is observed in the synthesized non-magnetic nanocomposites and analyzed using the wave-function shrinkage model.

Sulfur-infiltrated porous carbon microspheres with controllable multi-modal pore size distribution for high energy lithium-sulfur batteries.

Sulfur has received increasing attention as a cathode material for lithium-sulfur (Li-S) batteries due to its high theoretical specific capacity. However, the commercialization of Li-S batteries is limited by the challenges of poor electrical conductivity of sulfur, dissolution of the polysulfide intermediates into the electrolyte, and volume expansion of sulfur during cycling. Herein, we report the fabrication of novel-structured porous carbon microspheres with a controllable multi-modal pore size distribution, i.e., a combination of interconnected micropores, mesopores and macropores. Cathodes made of sulfur infiltrated in such a hierarchical carbon framework provide several advantages: (1) a continuous and high surface area carbon network for enhanced electrical conductivity and high sulfur loading; (2) macropores and large mesopores bridged by small mesopores to provide good electrolyte accessibility and fast Li ion transport and to accommodate volume expansion of sulfur; and (3) small mesopores and micropores to improve carbon/sulfur interaction and to help trap polysulfides. An initial discharge capacity at 1278 mA h g(-1) and capacity retention at 70.7% (904 mA h g(-1)) after 100 cycles at a high rate (1 C) were achieved. The material fabrication process is relatively simple and easily scalable.

Porous microspheres of MgO-patched TiO2 for CO2 photoreduction with H2O vapor: temperature-dependent activity and stability.

A novel MgO-patched TiO2 microsphere photocatalyst demonstrated 10 times higher activity toward CO production from CO2 photoreduction with H2O vapor, when the reaction temperature increased from 50 to 150 °C. The catalytic performance of hybrid MgO-TiO2 was much more stable than TiO2, particularly at a higher temperature, likely due to easier desorption of reaction intermediates and the enhanced CO2 adsorption by MgO.