Effect of chlorhexidine application on the long-term shear bond strength to dentin of a resin-modified glass ionomer.

PURPOSE: The aim of this study was to investigate the effect of chlorhexidine digluconate (CHX) application on the shear bond strength (SBS) of a resin-modified glass ionomer cement (RMGIC) to polyalkenoic acid-preconditioned dentin after 24 hours, six months, and 12 months of water storage at 37°C. MATERIALS AND METHODS: Cylindrical molds, placed on flat, polyalkenoic acid (Cavity Conditioner® [GC]) preconditioned dentin surfaces of 90 human teeth embedded in resin, were filled with Fuji II LC® (GC), a RMGIC, with (n=45) or without (n=45) the prior application of a 0.05% CHX solution. Within each group, SBS was determined after 24 hours (n=15), six months (n=15), and 12 months (n=15) of storage in water at 37°C. The results were analyzed with two-way analysis of variance followed by Tukey multiple means comparisons (p<0.05). The type of bond failure (adhesive/cohesive/mixed) was noted and the results were analyzed with chi-square test (p<0.05). RESULTS: After 24 hours, the SBS of RMGIC was not significantly different with (9.0 ± 2.8 MPa) or without (8.3±0.6 MPa) the application of CHX. After six months, however, SBS increased significantly in the group without CHX (12.7±3.4 MPa) but remained unchanged in the CHX group (9.4±4.0 MPa). Similar results without CHX (12.6±3.8 MPa) and with CHX (9.5±3.2 MPa) were obtained after 12 months. No significant differences in the type of debonding were found between the various groups tested. CONCLUSION: The application of 0.05% CHX after dentin preconditioning did not seem to have affected the 24-hour SBS of RMGIC. However, the six- and 12-month SBS was significantly lower for CHX-treated samples, possibly as a result of CHX interference with both the bonding mechanism and the maturation reaction of RMGIC.