Flexibility and torsional behaviour of rotary nickel-titanium PathFile, RaCe ISO 10, Scout RaCe and stainless steel K-File hand instruments.
Nakagawa, R K L; Alves, J L; Buono, V T L; Bahia, M G A.
Afiliação
  • Nakagawa RK; Department of Restoration Dentistry, Faculty of Dentistry, Universidade Federal de Minas Gerais, Belo Horizonte, Brazil.
Int Endod J ; 47(3): 290-7, 2014 Mar.
Article em En | MEDLINE | ID: mdl-23815415
AIM: To assess and compare the flexibility and torsional resistance of PathFile, RaCe ISO 10 and Scout RaCe instruments in relation to stainless steel K-File hand instruments. METHODOLOGY: Rotary PathFile (sizes 13, 16 and 19; .02 taper), Race ISO 10 (size 10; 0.02, 0.04 and 0.06 tapers), Scout RaCe (sizes 10, 15 and 20; 0.02 taper) and hand K-File (sizes 10, 15 and 20; 0.02 taper) instruments were evaluated. Alloy chemical composition, phases present and transformation temperatures were determined for the NiTi instruments. For all instruments, diameters at each millimetre from the tip as well as cross-sectional areas at 3 mm from the tip were measured based on ANSI/ADA Specification No. 101 using image analysis software. Resistance to bending and torsional resistance were determined according to specification ISO 3630-1. Vickers microhardness measurements were also taken in all instruments to assess their strength. Data were analysed using analysis of variance (α = 0.05). RESULTS: The alloys used in the manufacture of the three types of NiTi instruments had approximately the same chemical composition, but the PathFile instruments had a higher Af transformation temperature and contained a small amount of B19' martensite. All instruments had diameter values within the standard tolerance. The bending and torsional resistance values were significantly increased relative to the instrument diameter and cross-sectional area. CONCLUSIONS: PathFile instruments were the most flexible and the least torque resistant, whilst the stainless steel instruments were the least flexible although they were more torque resistant than the NiTi instruments.
Assuntos
Palavras-chave

Texto completo: 1 Bases de dados: MEDLINE Assunto principal: Titânio / Preparo de Canal Radicular / Análise de Falha de Equipamento / Instrumentos Odontológicos / Níquel Idioma: En Revista: Int Endod J Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil

Texto completo: 1 Bases de dados: MEDLINE Assunto principal: Titânio / Preparo de Canal Radicular / Análise de Falha de Equipamento / Instrumentos Odontológicos / Níquel Idioma: En Revista: Int Endod J Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil