Chitosan-Coated Diatom Silica as Hemostatic Agent for Hemorrhage Control.
ACS Appl Mater Interfaces
; 8(50): 34234-34243, 2016 Dec 21.
Article
em En
| MEDLINE
| ID: mdl-27998147
ABSTRACT
Uncontrolled hemorrhage leads to high death risk both in military and civilian trauma. Current hemostatic agents still have various limitations and side effects. In this study, natural diatom silica obtained from diatomite and diatom culture was purified and developed for hemorrhage control. To improve the biocompatibility and hemostatic performance of diatom silica, a series of chitosan-coated diatom (CS-diatom) was developed. The composition of CS-diatom prepared was optimized by in vitro hemocompatibility and blood coagulation evaluation for that prepared with 0.5%, 1%, 3%, and 5% chitosan. The results demonstrated that the CS-diatom prepared with 1% chitosan exhibited favorable biocompatibility (hemolysis ratio < 5%, no cytotoxicity to MEFs), great fluid absorbility (24.39 ± 1.53 times the weight of liquid), and desirable hemostasis effect (351 ± 14.73 s at 5 mg/mL, 248 ± 32.42s at 10 mg/mL). Further blood coagulation mechanism study indicated that CS-diatom could provide an ideal interface to induce erythrocyte absorption and aggregation, along with activating the intrinsic coagulation pathway and thus accelerated blood coagulation. Benefitting from the multiple hemostatic performances, CS-diatom showed the shortest clotting time (98.34 ± 26.54 s) and lowest blood loss (0.31 ± 0.11 g) in rat-tail amputation model compare to diatomite and diatom as well as gauze and commercial QuikClot zeolite. The results evidenced that the CS-diatom was a safe and effective hemostatic agent and provided a new understanding of nonsynthetic mesoporous materials for hemorrhage control.
Palavras-chave
Buscar no Google
Bases de dados:
MEDLINE
Assunto principal:
Hemostáticos
/
Sistemas de Liberação de Medicamentos
/
Dióxido de Silício
/
Quitosana
/
Hemorragia
Limite:
Animals
Idioma:
En
Revista:
ACS Appl Mater Interfaces
Assunto da revista:
BIOTECNOLOGIA
/
ENGENHARIA BIOMEDICA
Ano de publicação:
2016
Tipo de documento:
Article
País de afiliação:
China