Effect of multiple firings on optical and mechanical properties of Virgilite-containing lithium disilicate glass-ceramic of varying thickness.

ABSTRACT

OBJECTIVES: To investigate the effect of multiple firings on color, translucency, and biaxial flexure strength of Virgilite-containing (Li0.5Al0.5Si2.5O6) lithium disilicate glass ceramics of varying thickness. MATERIALS AND METHODS: Sixty discs were prepared from Virgilite-containing lithium disilicate blocks. Discs were divided according to thickness (n = 30) into T0.5 (0.5 mm) and T1.0 (1.0 mm). Each thickness was divided according to the number of firing cycles (n = 10); F1 (Control group) 1 firing cycle; F3 3 firing cycles, and F5 5 firing cycles. The discs were tested for color change (ΔE00) and translucency (TP00) using a spectrophotometer. Then, all samples were subjected to biaxial flexure strength testing using a universal testing machine. Data were collected and statistically analyzed (α = 0.5). For chemical analysis, six additional T0.5 discs (2 for each firing cycle) were prepared; for each firing cycle one disc was subjected to X-ray diffraction analysis (XRD) and another disc was subjected to Energy dispersive X-ray spectroscopy (EDX) and Scanning electron microscope (SEM). RESULTS: Repeated firing significantly reduced the translucency of F3 and F5 compared to F1 in T0.5 (p < 0.001), while for T1.0 only F5 showed a significant decrease in TP00 (p < 0.001). For ΔE00, a significant increase was recorded with repeated firings (p < 0.05) while a significant decrease resulted in the biaxial flexure strength regardless of thickness. CONCLUSIONS: Repeated firings had a negative effect on both the optical and mechanical properties of the Virgilite-containing lithium disilicate glass ceramics. CLINICAL RELEVANCE Repeated firings should be avoided with Virgilite-containing lithium disilicate ceramics to decrease fracture liability and preserve restoration esthetics.