Co-Ni ferrite is one of the crucial materials for the electronic industry. A partial substitution with a rare-earth metal brings about modification in crystal lattice and broadens knowledge in the discovery of new magnetic material. Current work reports a Ga3+ substitution in the Co-Ni ferrite with composition Co0.5Ni0.5Fe2-xGaxO4 (where x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0), herein referred to as spinel ferrite microspheres (CoNiGa-SFMCs). The samples were crystallized hydrothermally showing a hollow sphere morphology. The crystal phase, magnetic, morphology, and optical behaviour were examined using various microscopy and spectroscopic tools. While the XRD confirmed the phase of SFMCs, the crystallite size varied between 9 and 12 nm. The Tauc plot obtained from DRS (diffuse reflectance spectroscopy) shows the direct optical energy bandgap (Eg) of the products, with the pristine reading having the value of 1.41 eV Eg; the band gap increased almost linearly up to 1.62 eV along with rising the Ga3+ amount. The magnetic features, on the other hand, indicated the decrease in coercivity (Hc) as more Ga3+ is introduced. Moreover, there was a gradual increase in both saturation magnetization (Ms) and magnetic moment (nB) with increasing amount of Ga3+ till x = 0.6 and then a progressive decline with increases in the x content; this was ascribed to the spin-glass-like behavior at low temperatures. It was detected that magnetic properties correlate well with crystallite/particle size, cation distribution, and anisotropy.
RESUMO
Tm-Tb co-substituted Co-Ni nanospinel ferrites (NSFs) as (Co0.5Ni0.5) [TmxTbxFe2-2x]O4 (x = 0.00-0.05) NSFs were attained via the ultrasound irradiation technique. The phase identification and morphologies of the NSFs were explored using X-rays diffraction (XRD), selected area electron diffraction (SAED), and transmission and scanning electronic microscopes (TEM and SEM). The magnetization measurements against the applied magnetic field (M-H) were made at 300 and 10 K with a vibrating sample magnetometer (VSM). The various prepared nanoparticles revealed a ferrimagnetic character at both 300 and 10 K. The saturation magnetization (Ms), the remanence (Mr), and magneton number (nB) were found to decrease upon the Tb-Tm substitution effect. On the other hand, the coercivity (Hc) was found to diminish with increasing x up to 0.03 and then begins to increase with further rising Tb-Tm content. The Hc values are in the range of 346.7-441.7 Oe at 300 K to 4044.4-5378.7 Oe at 10 K. The variations in magnetic parameters were described based on redistribution of cations, crystallites and/or grains size, canting effects, surface spins effects, super-exchange interaction strength, etc. The observed magnetic results indicated that the synthesized (Co0.5Ni0.5)[TmxTbxFe2-x]O4 NSFs could be considered as promising candidates to be used for room temperature magnetic applications and magnetic recording media.