Complex Geometric Structure of a Simple Solid-Liquid Interface: GaN(0001)-Ga.

The equilibrium atomic interface structure between Ga and GaN(0001) is shown to contain substrate surface vacancies followed by substrate-induced layering and preferential lateral ordering in the liquid. The uncovered presence of point defects, in the form of vacancies at both sides of the solid-liquid interface, is an important structural feature which governs the local physical properties. Our x-ray diffraction study reveals that the layering is very stable and persists up to a temperature of 1123 K and a nitrogen pressure of 32 bar. The Ga layer spacing agrees remarkably well with the Friedel oscillation period for this system.

Hysteretic photochromic switching of Eu-Mg defects in GaN links the shallow transient and deep ground states of the Mg acceptor.

Although p-type activation of GaN by Mg underpins a mature commercial technology, the nature of the Mg acceptor in GaN is still controversial. Here, we use implanted Eu as a 'spectator ion' to probe the lattice location of Mg in doubly doped GaN(Mg):Eu. Photoluminescence spectroscopy of this material exemplifies hysteretic photochromic switching (HPS) between two configurations, Eu0 and Eu1(Mg), of the same Eu-Mg defect, with a hyperbolic time dependence on 'switchdown' from Eu0 to Eu1(Mg). The sample temperature and the incident light intensity at 355 nm tune the characteristic switching time over several orders of magnitude, from less than a second at 12.5 K, ~100 mW/cm2 to (an estimated) several hours at 50 K, 1 mW/cm2. Linking the distinct Eu-Mg defect configurations with the shallow transient and deep ground states of the Mg acceptor in the Lany-Zunger model, we determine the energy barrier between the states to be 27.7(4) meV, in good agreement with the predictions of theory. The experimental results further suggest that at low temperatures holes in deep ground states are localized on N atoms axially bonded to Mg acceptors.

Photoluminescence studies of a perceived white light emission from a monolithic InGaN/GaN quantum well structure.

In this work we demonstrate by photoluminescence studies white light emission from a monolithic InGaN/GaN single quantum well structure grown by metal organic chemical vapour deposition. As-grown and thermally annealed samples at high temperature (1000 °C, 1100 °C and 1200 °C) and high pressure (1.1 GPa) were analysed by spectroscopic techniques, and the annealing effect on the photoluminescence is deeply explored. Under laser excitation of 3.8 eV at room temperature, the as-grown structure exhibits two main emission bands: a yellow band peaked at 2.14 eV and a blue band peaked at 2.8 eV resulting in white light perception. Interestingly, the stability of the white light is preserved after annealing at the lowest temperature (1000 °C), but suppressed for higher temperatures due to a deterioration of the blue quantum well emission. Moreover, the control of the yellow/blue bands intensity ratio, responsible for the white colour coordinate temperatures, could be achieved after annealing at 1000 °C. The room temperature white emission is studied as a function of incident power density, and the correlated colour temperature values are found to be in the warm white range: 3260-4000 K.

Electronic structure of ytterbium-implanted GaN at ambient and high pressure: experimental and crystal field studies.

The results of high-pressure low-temperature optical measurements in a diamond-anvil cell of bulk gallium nitride crystals implanted with ytterbium are reported in combination with crystal field calculations of the Yb(3+) energy levels. Crystal field analysis of splitting of the (2)F(7/2) and (2)F(5/2) states has been performed, with the aim of assigning all features of the experimental luminescence spectra. A thorough analysis of the pressure behavior of the Yb(3+) luminescence lines in GaN allowed the determination of the ambient-pressure positions and pressure dependence of the Yb(3+) energy levels in the trigonal crystal field as well as the pressure-induced changes of the spin-orbit coupling coefficient.