RESUMO
OBJECTIVE: Due to increasing of aesthetic demand, ceramic crowns are widely used in different situations. However, to obtain long-term prognosis of restorations, a good conversion of resin cement is necessary. To evaluate the degree of conversion (DC) of one light-cure and two dual-cure resin cements under a simulated clinical cementation of ceramic crowns. MATERIAL AND METHODS: Prepared teeth were randomly split according to the ceramic's material, resin cement and curing protocol. The crowns were cemented as per manufacturer's directions and photoactivated either from occlusal suface only for 60 s; or from the buccal, occlusal and lingual surfaces, with an exposure time of 20 s on each aspect. After cementation, the specimens were stored in deionized water at 37°C for 7 days. Specimens were transversally sectioned from occlusal to cervical surfaces and the DC was determined along the cement line with three measurements taken and averaged from the buccal, lingual and approximal aspects using micro-Raman spectroscopy (Alpha 300R/WITec®). Data were analyzed by 3-way ANOVA and Tukey test at =5%. RESULTS: Statistical analysis showed significant differences among cements, curing protocols and ceramic type (p<0.001). The curing protocol 3x20 resulted in higher DC for all tested conditions; lower DC was observed for Zr ceramic crowns; Duolink resin cement culminated in higher DC regardless ceramic composition and curing protocol. CONCLUSION: The DC of resin cement layers was dependent on the curing protocol and type of ceramic.
Assuntos
Lâmpadas de Polimerização Dentária , Cimentos Dentários/química , Porcelana Dentária/química , Estética Dentária , Cimentos de Resina/química , Humanos , Teste de Materiais , Propriedades de SuperfícieRESUMO
UNLABELLED: Composite resin and metallic posts are the materials most employed for reconstruction of teeth presenting partial or total destruction of crowns. Resin-based cements have been widely used for cementation of ceramic crowns. The success of cementation depends on the achievement of adequate cement curing. OBJECTIVES: To evaluate the microhardness of Variolink® II (Ivoclar Vivadent, Schaan, Liechtenstein), used for cementing ceramic crowns onto three different coronal substrate preparations (dentin, metal, and composite resin), after 7 days and 3 months of water storage. The evaluation was performed along the cement line in the cervical, medium and occlusal thirds on the buccal and lingual aspects, and on the occlusal surface. MATERIAL AND METHODS: Thirty molars were distributed in three groups (N=10) according to the type of coronal substrate: Group D- the prepared surfaces were kept in dentin; Groups M (metal) and R (resin)- the crowns were sectioned at the level of the cementoenamel junction and restored with metallic cast posts or resin build-up cores, respectively. The crowns were fabricated in ceramic IPS e.max® Press (Ivoclar Vivadent, Schaan, Liechtenstein) and luted with Variolink II. After 7 days of water storage, 5 specimens of each group were sectioned in buccolingual direction for microhardness measurements. The other specimens (N=5) were kept stored in deionized water at 37ºC for three months, followed by sectioning and microhardness measurements. RESULTS: Data were first analyzed by three-way ANOVA that did not reveal significant differences between thirds and occlusal surface (p=0.231). Two-way ANOVA showed significant effect of substrates (p<0.001) and the Tukey test revealed that microhardness was significantly lower when crowns were cemented on resin cores and tested after 7 days of water storage (p=0.007). CONCLUSION: The type of material employed for coronal reconstruction of preparations for prosthetic purposes may influence the cement properties.
Assuntos
Cimentação/métodos , Cerâmica/química , Coroas , Cimentos de Resina/química , Água/química , Análise de Variância , Testes de Dureza , Humanos , Teste de Materiais , Ilustração Médica , Valores de Referência , Reprodutibilidade dos Testes , Propriedades de Superfície , Fatores de TempoRESUMO
Abstract Due to increasing of aesthetic demand, ceramic crowns are widely used in different situations. However, to obtain long-term prognosis of restorations, a good conversion of resin cement is necessary. Objective: To evaluate the degree of conversion (DC) of one light-cure and two dual-cure resin cements under a simulated clinical cementation of ceramic crowns. Material and Methods: Prepared teeth were randomly split according to the ceramic's material, resin cement and curing protocol. The crowns were cemented as per manufacturer's directions and photoactivated either from occlusal suface only for 60 s; or from the buccal, occlusal and lingual surfaces, with an exposure time of 20 s on each aspect. After cementation, the specimens were stored in deionized water at 37°C for 7 days. Specimens were transversally sectioned from occlusal to cervical surfaces and the DC was determined along the cement line with three measurements taken and averaged from the buccal, lingual and approximal aspects using micro-Raman spectroscopy (Alpha 300R/WITec®). Data were analyzed by 3-way ANOVA and Tukey test at =5%. Results: Statistical analysis showed significant differences among cements, curing protocols and ceramic type (p<0.001). The curing protocol 3x20 resulted in higher DC for all tested conditions; lower DC was observed for Zr ceramic crowns; Duolink resin cement culminated in higher DC regardless ceramic composition and curing protocol. Conclusion: The DC of resin cement layers was dependent on the curing protocol and type of ceramic.
Assuntos
Humanos , Cimentos de Resina/química , Cimentos Dentários/química , Porcelana Dentária/química , Estética Dentária , Lâmpadas de Polimerização Dentária , Propriedades de Superfície , Teste de MateriaisRESUMO
Composite resin and metallic posts are the materials most employed for reconstruction of teeth presenting partial or total destruction of crowns. Resin-based cements have been widely used for cementation of ceramic crowns. The success of cementation depends on the achievement of adequate cement curing. Objectives: To evaluate the microhardness of Variolink® II (Ivoclar Vivadent, Schaan, Liechtenstein), used for cementing ceramic crowns onto three different coronal substrate preparations (dentin, metal, and composite resin), after 7 days and 3 months of water storage. The evaluation was performed along the cement line in the cervical, medium and occlusal thirds on the buccal and lingual aspects, and on the occlusal surface. Material and Methods: Thirty molars were distributed in three groups (N=10) according to the type of coronal substrate: Group D- the prepared surfaces were kept in dentin; Groups M (metal) and R (resin)- the crowns were sectioned at the level of the cementoenamel junction and restored with metallic cast posts or resin build-up cores, respectively. The crowns were fabricated in ceramic IPS e.max® Press (Ivoclar Vivadent, Schaan, Liechtenstein) and luted with Variolink II. After 7 days of water storage, 5 specimens of each group were sectioned in buccolingual direction for microhardness measurements. The other specimens (N=5) were kept stored in deionized water at 37ºC for three months, followed by sectioning and microhardness measurements. Results: Data were first analyzed by three-way ANOVA that did not reveal significant differences between thirds and occlusal surface (p=0.231). Two-way ANOVA showed significant effect of substrates (p<0.001) and the Tukey test revealed that microhardness was significantly lower when crowns were cemented on resin cores and tested after 7 days of water storage (p=0.007). Conclusion: The type of material employed for coronal reconstruction of preparations ...
Assuntos
Humanos , Cimentação/métodos , Cerâmica/química , Coroas , Cimentos de Resina/química , Água/química , Análise de Variância , Testes de Dureza , Teste de Materiais , Ilustração Médica , Valores de Referência , Reprodutibilidade dos Testes , Propriedades de Superfície , Fatores de TempoRESUMO
OBJECTIVE: To test the hypothesis that the quality of the dentinal sealing provided by two-step etch-and-rinse adhesives cannot be altered by the addition of an extra layer of the respective adhesive or the application of a more hydrophobic, non-solvated resin. MATERIAL AND METHODS: full-crown preparations were acid-etched with phosphoric acid for 15 s and bonded with Adper Single Bond (3M ESPE), Excite DSC (Ivoclar/Vivadent) or Prime & Bond NT (Dentsply). The adhesives were used according to the manufacturers' instructions (control groups) or after application to dentin they were a) covered with an extra coat of each respective system or b) coated with a non-solvated bonding agent (Adper Scotchbond Multi-Purpose Adhesive, 3M ESPE). Fluid flow rate was measured before and after dentin surfaces were acid-etched and bonded with adhesives. RESULTS: None of the adhesives or experimental treatments was capable to block completely the fluid transudation across the treated dentin. Application of an extra coat of the adhesive did not reduce the fluid flow rate of adhesive-bonded dentin (p>0.05). Conversely, the application of a more hydrophobic non-solvated resin resulted in significant reductions in the fluid flow rate (p<0.05) for all tested adhesives. CONCLUSIONS: The quality of the dentinal sealing provided by etch-and-rinse adhesives can be significantly improved by the application of a more hydrophobic, non-solvated bonding agent.
Assuntos
Humanos , Condicionamento Ácido do Dente/métodos , Adesivos Dentinários , Colagem Dentária/métodos , Infiltração Dentária/prevenção & controle , Cimentos de Resina , Adesivos/química , Permeabilidade da Dentina , Adesivos Dentinários/química , Interações Hidrofóbicas e Hidrofílicas , Pressão Hidrostática , Dente Serotino , Cimentos de Resina/química , Coroa do Dente , MolhabilidadeRESUMO
Microleakage can be related to margin misfit. Also, traditional microleakage techniques are time-consuming. This study evaluated the existence of correlation between in vitro margin fit and a new microleakage technique for complete crowns cemented with 3 different luting agents. Thirty human premolars were prepared for full-coverage crowns with a convergence angle of 6 degrees, chamfer margin of 1.2 mm circumferentially, and occlusal reduction of 1.5 mm. Ni-Cr cast crowns were cemented with either zinc phosphate (ZP) (S.S. White), resin-modified glass-ionomer (RMGI) (Rely X Luting Cement) or a resin-based luting agent (RC) (Enforce). Margin fit (seating discrepancy and margin gap) was evaluated according to criteria in the literature under microscope with 0.001 mm accuracy. After thermal cycling, crowns were longitudinally sectioned and microleakage scores at tooth-cement interface were obtained and recorded at ×100 magnification. Margin fit parameters were compared with the one-way ANOVA test and microleakage scores with Kruskal-Wallis and Dunn's tests (alpha=0.05). Correlation between margin fit and microleakage was analyzed with the Spearman's test (alpha=0.05). Seating discrepancy and marginal gap values ranged from 81.82 µm to 137.22 µm (p=0.117), and from 75.42 µm to 78.49 µm (p=0.940), respectively. Marginal microleakage scores were ZP=3.02, RMGI=0.35 and RC=0.12 (p<0.001), with no differences between RMGI and RC scores. The correlation coefficient values ranged from -0.27 to 0.30 (p>0.05). Conclusion: Margin fit parameters and microleakage showed no strong correlations; cast crowns cemented with RMGI and RC had lower microleakage scores than ZP cement.
Assuntos
Humanos , Coroas , Cimentação/métodos , Planejamento de Prótese Dentária , Cimentos Dentários/química , Infiltração Dentária/classificação , Dente Pré-Molar/patologia , Ligas de Cromo/química , Resinas Compostas/química , Ligas Dentárias/química , Cimentos de Ionômeros de Vidro/química , Teste de Materiais , Cimentos de Resina/química , Propriedades de Superfície , Temperatura , Fatores de Tempo , Preparo Prostodôntico do Dente/métodos , Cimento de Fosfato de Zinco/químicaRESUMO
O presente trabalho teve como objetivo avaliar a fidelidade mor-fodimensional de troquéis confeccionados com dois gessos tipo IV (Vel-Mix® e Durone®), através do uso de um dispositivo constituído de uma coroa metálica usinada que se adapta com alta precisão a um troquel-padrão original, que simulava um dente preparado para receber uma coroa total. Os troquéis foram obtidos a partir de moldes de dois elastômeros (a silicona de adição Express® e a silicona de condensação Zetaplus / Orawash®), usando-se as técnicas de dupla moldagem e de casquete, cuja polimerização ocorreu com material imerso em água a 37°C. Em ambas as técnicas, a espessura da pasta fluida foi de 0, 2mm. A verificação do grau de adaptação da coroa-padrão aos troquéis foi realizada com auxílio do microscópio de profundidade. De acordo com a análise estatística realizada, conclui-se que: 1) os diferentes tipos de gessos não exerceram influência significante na alteração dimensional; 2) para o material Zetaplus / Oranwash, a técnica do casquete ofereceu menores distorções; 3) para o material, Express, a técnica da dupla-moldagem teve um melhor comportamento que a de casquete; 4) não houve diferença estatisticamente significante entre os dois materiais de moldagem em combinação com as respectivas técnicas de moldagem citadas anteriormente.
The present work aimed to evaluates the morfo-dimensional fidelity of die stones made with two type IV gypsum (Vel-Mix and Durone), with the aid of a customized device comprised of a usinat-ed metallic crown that adapts with high precision to an original die, simulating this device a prepared tooth to receive a full crown. The die stones were obtained from molds of two silicone impression materials (one polyvinylsiloxane, Express, and one condensation silicone, Zetaplus / Orawash). Impressions were obtained by either the putty-wash technique or by a single tooth acrylic tray. The impression materials were allowed to set in water at 37°C. In both techniques, the thickness of the flowing paste was of 0.2 mm. Adaptation was verificaded from the respective die stone obtained from impression with the use of a depth microscope. After proper statistical analysis, the following conclusion could be drawn: 1) no influence was observed decived from the different gypsum material; 2) for the material Zetaplus / Oranwash, the single tooth acrylic tray impression technique resulted in better adaptation; 3) for Express the putty-wash technique molding resulted in better adaptation; 4) there were no statistycally significant differences between the two impression materials associated with the both techniques conditions aforementioned.
Assuntos
Elastômeros de Silicone , Teste de Materiais , Técnica de Moldagem OdontológicaRESUMO
INTRODUCTION: Disinfection of dentin surfaces is desirable so long as it does not interfere with subsequent bonding of adhesive resins. OBJECTIVE: To test the null hypothesis that bond strengths to dentin are not affected by previous application of an iodine disinfecting solution. MATERIALS AND METHODS: Twenty-four extracted non-carious molars were selected. Occlusal enamel was removed producing a flat dentin substrate. Test teeth were all treated with 2 percent Iodine disclosing/disinfecting solution (I2DDS) for 20 sec and rinsed for 20 sec followed by the application of self- or total- etching bonding systems, generating five adhesive groups (n=3): Single Bond; ; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. The control groups (n=3 per adhesive) had no disclosing/disinfectant application prior to adhesive application. A 4-mm thick resin restoration was built up on each tooth for microtensile testing. Statistical analyses between experimental and control groups were performed by student's t-test (alpha= 0.05). RESULTS: In general, experimental groups (previously treated with I2DDS) showed significantly lower bond strength values when compared with their respective controls (p<0.05), except for group Prime &Bond I2 that did not significantly differ from its control (p>0.05). CONCLUSION: Acetone-base adhesive systems seem not to be affected by the application of I2DDS prior to etching and bonding procedures.
INTRODUÇÃO: A desinfecção das superfícies de dentina é desejada desde que não haja interferência na adesão dos agentes adesivos. OBJETIVO: Testar a hipótese nula de que a resistência adesiva não é afetada pela aplicação prévia de uma solução desinfetante de iodo. MATERIAL AND MÉTODO: Vinte e quatro molares hígidos foram selecionados. O esmalte oclusal destes dentes foi removido, e sobre as superfícies planas de dentina expostas foi aplicada da solução desinfetante de Iodo a 2 por cento (I2DDS), que permaneceu sobre a superfície por 20 s e foi lavada por 20 s com água deionizada. Sobre as superfícies desinfetadas foram aplicados um dos seguintes sistemas adesivos (n=3): Single Bond; Prime & Bond NT; Clearfil SE Bond; Opti-Bond Plus. Os grupos controle (n=3) não tiveram a supeficie de dentina tratada com I2DDS antes dos precedimentos adesivos. Em todos os grupos, após hibridização da dentina, foi construída uma "restauração" de resina composta com cerca de 4 mm de espessura. Após 7 dias de armazenagem em água destilada, os dentes foram secionados de modo a originarem espécimes a serem submetidos ao teste de microtração (palitos). Análise estatística para comparação dos dados foi realizada pelo teste t de student (alfa=0,05). RESULTADOS: De forma geral, os grupos experimentais (tratados com I2DDS) apresentraram resistência adesiva significativamente menor do que os respectivos grupos controle (p<0.05), exceção se fez apenas para o grupo P&BI2, que não diferiu significativamente de seu grupo controle P&BC (p>0.05). Assim, a hipótese nula deve ser rejeitada para os adesivos a base de etanol e/ou a base de água, mas aceita para o adesivo a base de acetona. CONCLUSÃO: O uso da solução experimental de iodo previamente à realização dos procedimentos adesivos afetou a efetividade da união à dentina apenas quando do emprego de sistemas adesivos a base de etanol e/ou água.
Assuntos
Adesivos Dentinários , Dentina , Desinfetantes , Iodo , Sensibilidade da DentinaRESUMO
Este estudo avaliou a resistência de união de dois sistemas adesivos ao esmalte e à dentina após a aplicação de agente clareador sobre a união compósito-dente. Dezesseis terceiros molares humanos foram usados nos procedimentos restauradores. Single Bond (SB) e Clearfil SE Bond (CB) foram aplicados no esmalte e na dentina de acordo com as instruções dos fabricantes. Um bloco de compósito foi construído nas superfícies tratadas com os adesivos. Os dentes restaurados foram seccionados em fatias com espessura de 0,7 mm, que receberam constrição na interface de união num formato de ampulheta, com área de secção transversal de ± 0,5 mm2. Os espécimes foram distribuídos em 8 grupos (n = 10) de acordo com os fatores em estudo: substrato dental (esmalte e dentina); sistema adesivo (SB e CB) e tratamento (peróxido de carbamida a 10% e controle). O agente clareador (Opalescence) foi aplicado na interface de união por 6 horas durante 14 dias e, após o tratamento diário, os espécimes foram armazenados em saliva artificial. Os espécimes não clareados foram mantidos em saliva artificial por 14 dias. Os espécimes foram testados e os dados foram analisados pela ANOVA (três fatores) e pelo teste Tukey (p < 0,05). A resistência à tração do esmalte tratado com o adesivo CB foi reduzida após aplicação do peróxido de carbamida, entretanto, a resistência de união em dentina para ambos os adesivos não foi modificada. Os resultados sugerem que o clareamento afeta a resistência de união do CB ao esmalte, mas nenhuma influência foi observada em dentina.
Assuntos
Humanos , Bis-Fenol A-Glicidil Metacrilato , Colagem Dentária , Esmalte Dentário/efeitos dos fármacos , Dentina/efeitos dos fármacos , Peróxidos/farmacologia , Cimentos de Resina , Ureia/análogos & derivados , Análise de Variância , Combinação de Medicamentos , Esmalte Dentário/ultraestrutura , Dentina/ultraestrutura , Microscopia Eletrônica de Varredura , Saliva Artificial , Resistência à Tração , Clareamento Dental/métodos , Ureia/farmacologiaRESUMO
Este trabalho focaliza os aspectos que podem afetar a permeabilidade de resinas adesivas na matriz de dentina desmineralizada durante o desenvolvimento do processo adesivo. Os efeitos da umidade de superfície, respectivamente aos sistemas adesivos e aos problemas relacionados com a formaçäo incompleta da camada híbrida säo apresentados
Assuntos
Dentina , Hibridização Genética , Adesivos Dentinários , Permeabilidade DentáriaRESUMO
Fatores como o modo de ativação, a técnica restauradora e a configuração cavitária podem afetar a resistência adesiva à dentina. Este estudo avaliou os efeitos dos modos de ativação e das técnicas restauradoras na resistência de união compósito/dentina na parede vestibular de restaurações classe I. O esmalte oclusal dos dentes foi removido para expor uma superfície dentinária planificada. Cavidades oclusais (4 x 3 x 3 mm) foram preparadas em dentina. O adesivo Single Bond foi aplicado de acordo com as instruções do fabricante, e o compósito TPH Spectrum, inserido através de três diferentes técnicas: oblíqua incremental, horizontal incremental ou incremento único. O compósito foi ativado utilizando o método contínuo (600 mW/cm² por 40 s) ou "Soft-Start" (250 mW/cm² por 10 s + 600 mW/cm² por 30 s). O grupo controle foi obtido pela união somente à parede vestibular planificada (fator C = 1). Os dentes foram armazenados por 24 h em água a 37ºC e preparados para o ensaio de microtração (0,5 mm/min). Os espécimes apresentaram na secção transversal uma área de união de aproximadamente 0,8 mm². Os resultados foram analisados pela ANOVA (dois fatores), pelos testes de Tukey e Dunnett (a = 0,05). A técnica incremental seguida da ativação com ambas as formas de fotopolimerização produziu maiores valores de resistência de união que a técnica de incremento único (p < 0,05). A resistência de união sempre foi menor quando a restauração foi confeccionada em cavidade (p < 0,05), exceto quando foram utilizadas ativação com "Soft-Start" e técnicas incrementais. A resistência de união às paredes cavitárias é dependente da técnica de inserção e do modo de ativação da resina composta.
Assuntos
Humanos , Dentina , Colagem Dentária/métodos , Restauração Dentária Permanente/métodos , Cimentos de Resina , Análise de Variância , Preparo da Cavidade Dentária , Resistência à TraçãoRESUMO
Este estudo avaliou in vitro, durante 28 dias, a propriedade de liberaçäo de flúor de cimentos de ionômero de vidro (CIV) restauradores e outros materiais que contêm flúor. Os resultados mostraram que o padräo de liberaçäo de flúor foi semelhante para todos os CIV testados, sendo que houve uma liberaçäo inicial acentuada, seguida por um rápido declínio, tendendo a uma estabilizaçäo após 7 dias. Os CIV liberaram mais flúor do uma resina composta e um selante de cicatrículas e fissuras. Dentre todos os materiais, o Vitrion R foi o que mais liberou flúor
Assuntos
Cimentos de Ionômeros de Vidro/análise , Cimentos de Ionômeros de Vidro/farmacocinética , Flúor/farmacocinética , Selantes de Fossas e Fissuras , Resinas Compostas , Materiais DentáriosRESUMO
Os autores descrevem a resolução clínica de um caso de amelogênese imperfeita utilizando ionômero de vidro e resina composta
Assuntos
Amelogênese Imperfeita/reabilitação , Resinas Compostas/uso terapêutico , Estética Dentária , Cimentos de Ionômeros de Vidro , Hipoplasia do Esmalte Dentário/terapiaRESUMO
Neste trabalho, os autores fazem uma revisäo da literatura a respeito dos condicionadores de esmalte e dentina para uso com os cimentos de ionômero de vidro. Discutem os pontos que säo discordantes entre os autores, tirando algumas conclusöes que säo interesse clínico
Assuntos
Esmalte Dentário , Dentina , Cimentos de Ionômeros de VidroRESUMO
A resistência de uniäo a dentina DO Scotchbond MP e Variglass foi determinada utilizando-se um novo método do ensaios por micro-traçäo. Esta nova metodologia permite testar a resistência adesiva a pequenas áreas através do desgaste de secçäo transversal dos espécimes até 0,5 milímetros quadrados. A principal observaçäo deste estudo foi que a resistência a traçäo foi dependente da superfície da área adesiva. As superfícies adesivas variaram de 0,5 a 5,0 milímetros quadrados o que é muito menor do que as superfícies adesivas utilizadas rotineiramente em testes de laboratório. Uma relaçäo inversa entre a resistência a traçäo e a área de superfície adesiva foi observada para ambos os materiais. Quando utilizaram-se as menores áreas, Scotchbond MP atingiu valores de até 46 MPa e Variglass resultou em valores de até 34 MPa
Assuntos
Humanos , Masculino , Feminino , Adesivos Dentinários/análise , Resistência à Tração , Cimentos de Ionômeros de Vidro/análise , Resinas Compostas/análise , Materiais Dentários/análiseRESUMO
Dentin bars of approximately 0.7 X 0.7 X 5.0 mm were obtained from the crown of human third molars. The specimens had their ends covered with nail varnish and were subjected to demineralization in 0.5 M EDTA for 72 hours. The specimens were stressed in tension, griped by their mineralized ends. The load/displacement data was transformed to stress/strain data using the original cross-sectional area and the length of the demineralized area (gauge-length). A low strain (0-2%) and the maximum moduli were calculated for specimens tested in water (control), dehydrated in acetone and in HEMA and air-dried. All dehydration procedures caused significant stiffening of the collagen netword. Air-dried specimens were the most stiffer, followed by acetone-dehydrated and HEMA-dehydrated specimens. The stiffening effect of organic solvents on acid-etched dentin, may alter the permeability of the collagen network to adhesive resins
Assuntos
Humanos , Permeabilidade da Dentina , Elasticidade , Desmineralização do Dente , Acetona/farmacologia , Ácido Edético/farmacologia , Ar , Desidratação , Dentina/efeitos dos fármacosRESUMO
Este estudo comparou as quantidades e os padröes de liberaçäo de flúor de materiais dentários restauradores em água deionizada, por um período de 14 dias. Os resultados mostraram que os materiais diferiram na quantidade de flúor liberado, sendo que o Chelon Fil liberou as maiores quantidades de flúor durante todo o período avaliado, seguido pelo Vitremer, Chelon Silver e VariGlass. Todos os materiais apresentaram o mesmo padräo de liberaçäo de flúor, sendo esta significantemente maior nas primeiras 24 horas após a mistura
Assuntos
Flúor/análise , Materiais Dentários/análise , Cimentos de Ionômeros de Vidro/química , Restauração Dentária PermanenteRESUMO
Foi estudado o efeito do condicionamento da dentina resistëncia à remoçäo por traçäo de restauraçöes mistas de cimento ionomérico e resina composta. Os autores utilizaram como agentes de limpeza da dentina, ácido poliacrílico, soluçäo ITS, ácido tänico, soluçäo de hidróxido de cálcio e água. Os resultados evidenciaram que näo houve diferença significante entre os grupos, embora os espécimes que foram condicionados com ácido poliacrílico, tenham apresentado valores mais elevados nos testes de resistência à traçäo
Assuntos
Humanos , Restauração Dentária Permanente , Dentina , Cimentos de Ionômeros de VidroRESUMO
Os autores ralizaram uma investigaçäo clínica para avaliar a capacidade de inibiçäo de cáries do cimento de sílico-fosfato em comparaçäo com o amálgama. Foram realizadas restauraçöes de classe I nos pré-molares de 30 pacientes que apresentavam cáries incipientes oclusais, exclusivamente. Os pacientes estäo sendo controlados através de radiografias interproximais e clinicamente para verificar o aparecimento de novas lesöes cariosas. Nos resultados de 1 ano näo se observou diferença significante entre os materiais testados
Assuntos
Criança , Adolescente , Humanos , Masculino , Feminino , Cárie Dentária/prevenção & controle , Cimento de Silicato/farmacologia , Amálgama DentárioRESUMO
Os autores avaliaram a influência do verniz cavitário na infiltraçäo marginal de restauraçöes de amálgama realizadas com liga convencional (Velvalloy) e com liga de alto teor de cobre (Dispersalloy) nos períodos de 24 horas, 7 dias e 28 dias. Os resultados demonstraram que, na comparaçäo entre os 3 períodos de teste, a infiltraçäo foi menor no período de 28 dias. A análise dos grupos em estudo nos levou a concluir que o verniz cavitário näo tem influência na infiltraçäo marginal de ligas de amálgama convencional e de alto teor de cobre em períodos curtos de tempo