The present work evaluates the water oxidation catalytic activity of a Mn-based metal-organic framework (MOF), which we envisioned to reduce the oxygen evolution reaction (OER) overpotential because of its high electrical conductivity, facilitated by solvent-encapsulated structural features. The presence of Mn centers induces interesting magnetic features in the MOF, which exhibits impressive cryogenic magnetic refrigeration with a ΔSM value of 29.94 J kg-1 K-1 for a field change of ΔH = 5T at 2.3 K. To the best of our knowledge, the ΔSM value of the current system ranked the highest position among the published examples. The crystal structure aligns perfectly with the thematic expectations and features as many as ten metal-coordinated water molecules, forming an extensive web of a hydrogen-bonded network while facing toward the porous channel filled with another set of much-anticipated entrapped lattice water molecules. Such structural features are expected to manifest high proton conductivity, and detailed investigation indeed yields the best value for the system at 1.57 × 10-4 S/cm at 95% humidity and 85 °C. In order to evaluate the thematic notion of a one-to-one relationship between OER and improved electrical conductivity, extensive electrocatalytic water splitting (WS) investigations were carried out. The final results show highly encouraging WS ability of the Mn-MOF, showing the electrocatalytic surface area value of the active species as 0.0686 F/g with a turnover frequency value of 0.043 [(mol. O2) (mol. Mn-MOF)-1 s-1]. Another fascinating aspect of the current communication is the excellent synergy observed between the experimental WS outcomes and the corresponding theoretical data calculated using density functional theory (DFT). Consequently, a plausible mechanism of the overall OER and the role of the Mn-MOF as a water oxidation catalyst, along with the importance of water molecules, have also been derived from the theoretical calculations using DFT.