RESUMO
We present the novel potential application of imine-based covalent organic frameworks (COFs), formed by the direct Schiff reaction between 1,3,5-tris(4-aminophenyl)benzene and 1,3,5-benzenetricarbaldehyde building blocks in m-cresol or acetic acid, named RT-COF-1 or RT-COF-1Ac/RT-COF-1AcB. The post-synthetic treatment of RT-COF-1 with LiCl leads to the formation of LiCl@RT-COF-1. The ionic conductivity of this series of polyimine COFs has been characterized at variable temperature and humidity, using electrochemical impedance spectroscopy. LiCl@RT-COF-1 exhibits a conductivity value of 6.45 × 10-3 S cm-1 (at 313 K and 100% relative humidity) which is among the highest values so far reported in proton conduction for COFs. The mechanism of conduction has been determined using 1H and 7Li solid-state nuclear magnetic resonance spectroscopy. Interestingly, these materials, in the presence of controlled amounts of acetic acid and under pressure, show a remarkable processability that gives rise to quasi-transparent and flexible films showing in-plane structural order as confirmed by X-ray crystallography. Finally, we prove that these films are useful for the construction of proton exchange membrane fuel cells (PEMFC) reaching values up to 12.95 mW cm-2 and 53.1 mA cm-2 for maximum power and current density at 323 K, respectively.
RESUMO
Crosslinked membranes have been synthesized by a casting process using polybenzimidazole (PBI) and poly(vinyl benzyl chloride) (PVBC). The membranes were quaternized with 1,4-diazabicyclo[2.2.2]octane (DABCO) to obtain fixed positive quaternary ammonium groups. XPS analysis has showed insights into the changes from crosslinked to quaternized membranes, demonstrating that the crosslinking reaction and the incorporation of DABCO have occurred, while the 13C-NMR corroborates the reaction of DABCO with PVBC only by one nitrogen atom. Mechanical properties were evaluated, obtaining maximum stress values around 72 MPa and 40 MPa for crosslinked and quaternized membranes, respectively. Resistance to oxidative media was also satisfactory and the membranes were evaluated in single direct ethanol fuel cell. PBI-c-PVBC/OH 1:2 membrane obtained 66 mW cm-2 peak power density, 25% higher than commercial PBI membranes, using 0.5 bar backpressure of pure O2 in the cathode and 1 mL min-1 KOH 2M EtOH 2 M aqueous solution in the anode. When the pressure was increased, the best performance was obtained by the same membrane, reaching 70 mW cm-2 peak power density at 2 bar O2 backpressure. Based on the characterization and single cell performance, PBI-c-PVBC/OH membranes are considered promising candidates as anion exchange electrolytes for direct ethanol fuel cells.