A comparative study of the metastable equilibrium solubility behavior of high-crystallinity and low-crystallinity carbonated apatites using pH and solution strontium as independent variables.

UNLABELLED: Using solution strontium and pH as independent variables, the metastable equilibrium solubility (MES) behavior of two carbonated apatite (CAP) samples has been examined, a high-crystallinity CAP (properties expected to be similar to dental enamel) and a low-crystallinity CAP (properties expected to be similar to bone mineral). CAP samples were prepared by precipitation/digestion: (CAP A: high-crystallinity, 1.3 wt% CO3, synthesized at 85 degrees C; CAP B: low-crystallinity, 6.4 wt% CO3, synthesized at 50 degrees C). Baseline MES distributions were determined in a series of 0.1 M acetate buffers containing only calcium and phosphate (no strontium) over a broad range of solution conditions. To assess the influence of strontium, MES profiles were determined in a similar fashion with 20, 40, 60, and 80% of the solution calcium being replaced on an equal molar basis by solution strontium. To determine the correct function governing CAP dissolution, ion activity products (IAPs) were calculated from the compositions of buffer solutions based on the hydroxyapatite template (Ca(10-n)Sr(n)(PO4)6(OH)2 (n = 0-10)) and the calcium/hydroxide deficient hydroxyapatite template (Ca(9-n)Sr(n)(HPO4)(PO4)5OH (n = 0-9)). FINDINGS: (a) for CAP A, at high solution strontium/calcium ratios, the MES profiles were essentially superimposable when the solution IAPs were calculated using the stoichiometry of Ca6Sr4(PO4)6(OH)2 and for CAP B by a stoichiometry of Ca7Sr2(HPO4)(PO4)5OH; (b) for CAP A, at low strontium/calcium ratios, the stoichiometry yielding MES data superpositioning was found to be that of hydroxyapatite and for CAP B, that of calcium/hydroxide deficient hydroxyapatite. When other stoichiometries were assumed, good superpositioning of the data was not possible.

Metastable equilibrium solubility behavior of carbonated apatite in the presence of solution strontium.

The purpose of this study was to use the concept of metastable equilibrium solubility (MES) to describe the anomalous solubility behavior of carbonated apatite (CAP) in the presence of solution strontium. A CAP sample (4.8 wt% CO(3), synthesized at 70 degrees C) was prepared by precipitation. Baseline MES distributions were determined in a series of 0.1 M acetate buffers containing only calcium and phosphate (no strontium) over a broad range of solution conditions. In order to assess the influence of strontium, MES profiles were then determined in a similar fashion with 20, 30, 40, 50, 60, 70, and 80% of the solution calcium being replaced on an equal molar basis by solution strontium. From the compositions of the equilibrating buffer solutions, ion activity products (IAPs) of the form Ca(10-n)Sr(n)(PO(4))(6)(OH)(2) (n = 0-10) were calculated in an attempt to determine the correct function governing the dissolution of the CAP preparation. The results demonstrate the following important findings: (a) at high solution strontium/calcium ratios (i.e., when 60% or more of the solution calcium was replaced by strontium), the MES profiles in all the experiments were found to be essentially superimposable when the solution IAPs were calculated using the stoichiometry of Ca(6)Sr(4)(PO(4))(6)(OH)(2), and (b), at low solution strontium/calcium ratios (i.e., when 40% or less of the solution calcium was replaced by strontium), the stoichiometry yielding MES data superpositioning was found to be that of hydroxyapatite. When other stoichiometries were assumed, good superpositioning of the data was not possible.