RESUMO
The hydrogen absorption properties of metal closo-borate/metal hydride composites, M2B10H10-8MH and M2B12H12-10MH, M = Li or Na, are studied under high hydrogen pressures to understand the formation mechanism of metal borohydrides. The hydrogen storage properties of the composites have been investigated by in situ synchrotron radiation powder X-ray diffraction at p(H2) = 400 bar and by ex situ hydrogen absorption measurements at p(H2) = 526 to 998 bar. The in situ experiments reveal the formation of crystalline intermediates before metal borohydrides (MBH4) are formed. On the contrary, the M2B12H12-10MH (M = Li and Na) systems show no formation of the metal borohydride at T = 400 °C and p(H2) = 537 to 970 bar. 11B MAS NMR of the M2B10H10-8MH composites reveal that the molar ratio of LiBH4 or NaBH4 and the remaining B species is 1 : 0.63 and 1 : 0.21, respectively. Solution and solid-state 11B NMR spectra reveal new intermediates with a B : H ratio close to 1 : 1. Our results indicate that the M2B10H10 (M = Li, Na) salts display a higher reactivity towards hydrogen in the presence of metal hydrides compared to the corresponding [B12H12]2- composites, which represents an important step towards understanding the factors that determine the stability and reversibility of high hydrogen capacity metal borohydrides for hydrogen storage.
RESUMO
Metal hydroborates and their derivatives have been receiving attention as potential solid-state ion conductors for battery applications owing to their impressive electrochemical and mechanical characteristics. However, to date only a fraction of these compounds has been investigated as solid-state electrolytes. Here, MB12H11NH3 (M = Li and Na) hydroborates are synthesized and investigated as electrolyte materials for all-solid-state batteries. The room temperature α-NaB12H11NH3 was structurally solved in P212121 (a = 7.1972(3) Å, b = 9.9225(4) Å, and c = 14.5556(5) Å). It shows a polymorphic structural transition near 140 °C to cubic Fm3Ìm. LiB12H11NH3 and NaB12H11NH3 exhibit cationic conductivities of σ(Li+) = 3.0 × 10-4 S cm-1 and σ(Na+) = 1.2 × 10-4 S cm-1 at 200 °C. Hydration is found to improve ionic conductivity of the hydroborates. It is presumed that modest ionic conductivities could be due to a lack of significant re-orientational dynamics in the crystal structure resulting from the presence of the bulky -NH3 group in the anion.