RESUMO
Research involved in developing alternative energy sources has become a necessity to face global warming. In this context, superconductivity is an appealing solution to enhance clean electrical energy provided that lower production costs can be attained. By implementation of chemical solution deposition techniques and high-throughput growth methods, low-cost nanostructured epitaxial cuprate superconductors are timely candidates. Here, we present a versatile and tunable solution method suitable for the preparation of high-performance epitaxial cuprate superconducting films. Disregarding the renowned trifluoroacetate route, we center our focus on the transient liquid-assisted growth (TLAG) that meets the requirement of being a greener chemical process together with ultrafast growth rates beyond 100 nm/s. We developed a facile, fast, and cost-effective method, starting from the synthesis of metal-propionate powders of Y, Ba, and Cu of high purity and high yields, being the precursors of the fluorine-free solutions, which enable the chemical and microstructural nanoscale homogeneity of YBa2Cu3O7-x (YBCO) precursor films. These solutions present endured stability and enable precise tunability of the composition, concentration, porosity, and film thickness. Homogeneous precursor films up to thicknesses of 2.7 µm through eight layer multidepositions are demonstrated, thus establishing the correct basis for epitaxial growth using the fast kinetics of the TLAG process. YBCO films of 500 nm thickness with a critical current density of 2.6 MA/cm2 at 77 K were obtained, showing the correlation of precursor film homogeneity to the final YBCO physical properties.
RESUMO
Transient liquid assisted growth (TLAG) is an ultrafast non-equilibrium growth process mainly governed by kinetic parameters, which are only accessible through fast in situ characterizations. In situ synchrotron X-ray diffraction (XRD) analysis and in situ electrical resistivity measurements are used to derive kinetic diagrams of YBa2 Cu3 O7- x (YBCO) superconducting films prepared via TLAG and to reveal the unique peculiarities of the process. In particular, diagrams for the phase evolution and the YBCO growth rates have been built for the two TLAG routes. It is shown that TLAG transient liquids can be obtained upon the melting of two barium cuprate phases (and not just one), differentiated by their copper oxidation state. This knowledge serves as a guide to determine the processing conditions to reach high performance films at high growth rates. With proper control of these kinetic parameters, films with critical current densities of 2-2.6 MA cm-2 at 77 K and growth rates between 100-2000 nm s-1 are reached. These growth rates are 1.5-3 orders of magnitude higher than those of conventional methods.