Decomposition of methanol-d4 on Rh nanoclusters supported by thin-film Al2O3/NiAl(100) under near-ambient-pressure conditions.

The decomposition of methanol-d4 (CD3OD) on Rh nanoclusters grown by the deposition of Rh vapors onto an ordered thin film of Al2O3/NiAl(100) was studied, with various surface-probe techniques and largely under near-ambient-pressure (NAP) conditions. The results showed a superior reactivity of small Rh clusters (diameter < 1.5 nm) exposed to CD3OD at 5 × 10-3-0.1 mbar at 400 K; the gaseous production of CO and D2 from decomposed methanol-d4 per Rh surface site on the small Rh clusters with diameters of ∼1.1 nm was nearly 8 times that on large ones with diameters of ∼3.5 nm. The promotion of reactivity with decreased cluster size under NAP conditions was evidently greater than that under ultrahigh vacuum conditions. Moreover, the concentration of atomic carbon (C*; where * denotes adsorbate)-a key catalyst poisoner-yielded from the dissociation of CO* from dehydrogenated methanol-d4 was significantly smaller on small clusters (diameter < 1.5 nm). The NAP size effect on methanol-d4 decomposition involved the surface hydroxyl (OH*) from the little co-adsorbed water (H2O*) that was dissociated at a probability dependent on the cluster size. H2O* was more likely dissociated into OH* on small Rh clusters, by virtue of their more reactive d-band structure, and the OH* then effectively promoted the O-D cleavage of methanol-d4, as the rate-determining step, and thus the reaction probability; on the other hand, the OH* limited CO* dissociation on small Rh clusters via both adsorbate and lateral effects. These results suggest that the superior properties of small Rh clusters in both reactivity and anti-poisoning would persist and be highly applicable under "real-world" catalysis conditions.

Decomposition of methanol-d4 on a thin film of Al2O3/NiAl(100) under near-ambient-pressure conditions.

We have studied the decomposition of methanol-d4 on thin film Al2O3/NiAl(100) under near-ambient-pressure conditions, with varied surface-probe techniques and calculations based on density-functional theory. Methanol-d4 neither adsorbed nor reacted on Al2O3/NiAl(100) at 400 K under ultrahigh vacuum conditions, whereas they dehydrogenated, largely to methoxy-d3 (CD3O*, * denoting adsorbates) and formaldehyde-d2 (CD2O*), on the surface when the methanol-d4 partial pressure was increased to 10-3 mbar and above. The dehydrogenation was facilitated by hydroxyl (OH* or OD*) from the dissociation of little co-adsorbed water; a small fraction of CD2O* interacted further with OH* (OD*) to form, via intermediate CD2OOH* (CD2OOD*), formic acid (DCOOH* or DCOOD*). A few surface carbonates were also yielded, likely on the defect sites of Al2O3/NiAl(100). The results suggest that alumina not only supports metal clusters but also participates in reactions under realistic catalytic conditions. One may consider accordingly the multiple functions of alumina while designing ideal catalysts.

Distinct dependence on size of Pt and Rh nanoclusters on graphene/Pt(111) in the decomposition of methanol-d4.

Pt and Rh nanoclusters, grown on deposition of Pt and Rh vapors onto graphene/Pt(111), show separate reactivity toward the decomposition of methanol-d4. The Pt (Rh) clusters had a mean diameter 2.0-3.5 nm (2.1-4.0 nm) and height 0.45-0.94 nm (0.41-0.9 nm) evolving with the coverage; they were structurally ordered, having an fcc phase and growing in (111) orientation, and had lattice constants similar to their bulk values. Methanol-d4 on the Pt clusters did not decompose but desorbed mostly, disparate from that on Pt(111) surface; the disparity arose as the adsorption energies of methanol-d4 on most surface sites of the Pt clusters became smaller than their single crystal counterpart. This size effect, nevertheless, did not apply on the Rh clusters, despite their similar atomic stacking; the Rh clusters showed a reactivity similar to that of the Rh(111) surface because the adsorption energies of methanol-d4 on both Rh clusters and Rh(111) are comparable. The distinct size dependence was rationalized through their electronic structures and charge distribution of Fukui function mapping. Our results suggest that reactive transition metals do not necessarily become more reactive while they are scaled down to nanoscale; their reactivity evolves with their size in a manner largely dependent on their electronic nature.

Dependence on Size of Supported Rh Nanoclusters in the Dehydrogenation of Methanol-d4 Obstructed by CO.

The size effect on the activity of a catalyst has been a focal issue since ideal catalysts were pursued, whereas that on the degradation of a catalyst, by reaction intermediates such as CO, is little discussed. We demonstrate that the dehydrogenation of methanol-d4 on supported Rh nanoclusters precovered with CO (Rh-CO clusters) was obstructed, indicated by a decreased production of CO and D2; the obstructive effect exhibits a remarkable dependence on the cluster size, with a minimum at a cluster diameter near 1.4 nm. The decreased production arose from a decreased reaction probability controlled by the increased activation energy for each dehydrogenation step (including formation of methoxy-d3), adsorption energies of CO, and repulsion from the CO array on the Rh-CO surface. The effects of these factors in deactivating the clusters varied separately with the cluster size. Consequently, the size effect on the CO poisoning should be taken into account in engineering the cluster size to optimize the catalytic performance.

Promoted activity of annealed Rh nanoclusters on thin films of Al2O3/NiAl(100) in the dehydrogenation of Methanol-d4.

Annealed Rh nanoclusters on an ordered thin film of Al2O3/NiAl(100) were shown to exhibit a promoted reactivity toward the decomposition of methanol-d4, under both ultrahigh vacuum and near-ambient-pressure conditions. The Rh clusters were grown with vapor deposition onto the Al2O3/NiAl(100) surface at 300 K and annealed to 700 K. The decomposition of methanol-d4 proceeded only through dehydrogenation, with CO and deuterium as products, on Rh clusters both as prepared and annealed. Nevertheless, the catalytic reactivity of the annealed clusters, measured with the production of either CO or deuterium per surface Rh site from the reaction, became at least 2-3 times that of the as-prepared ones. The promoted reactivity results from an altered support effect associated with an annealing-induced mass transport at the surface. Our results demonstrate a possibility to practically prepare reactive Rh clusters, regardless of the cluster size, that can tolerate an elevated reaction temperature, with no decreased reactivity.