Coating carbon nanotubes with humic acid using an eco-friendly mechanochemical method: Application for Cu(II) ions removal from water and aquatic ecotoxicity.

In this work, industrial grade multi-walled carbon nanotubes (MWCNT) were coated with humic acid (HA) for the first time by means of a milling process, which can be considered an eco-friendly mechanochemical method to prepare materials and composites. The HA-MWCNT hybrid material was characterized by atomic force microscopy (AFM), scanning electron microscopies (SEM and STEM), X-ray photoelectron spectroscopy (XPS), termogravimetric analysis (TGA), and Raman spectroscopy. STEM and AFM images demonstrated that the MWCNTs were efficiently coated by the humic acid, thus leading to an increase of 20% in the oxygen content at the nanotube surface as observed by the XPS data. After the milling process, the carbon nanotubes were shortened as unveiled by SEM images and the values of ID/IG intensity ratio increased due to shortening of the nanotubes and increasing in the number defects at the graphitic structure of carbon nanotubes walls. The analysis of TGA data showed that the quantity of the organic matter of HA on the nanotube surface was 25%. The HA coating was responsible to favor the dispersion of MWCNTs in ultrapure water (i.e. -42mV, zeta-potential value) and to improve their capacity for copper removal. HA-MWCNTs hybrid material adsorbed 2.5 times more Cu(II) ions than oxidized MWCNTs with HNO3, thus evidencing that it is a very efficient adsorbent material for removing copper ions from reconstituted water. The HA-MWCNTs hybrid material did not show acute ecotoxicity to the tested aquatic model organisms (Hydra attenuata, Daphnia magna, and Danio rerio embryos) up to the highest concentration evaluated (10mgL-1). The results allowed concluding that the mechanochemical method is effective to coat carbon nanotubes with humic acid, thus generating a functional hybrid material with low aquatic toxicity and great potential to be applied in environmental nanotechnologies such as the removal of heavy metal ions from water.

Structural organization of cetyltrimethylammonium sulfate in aqueous solution: The effect of Na2SO4.

We used dynamic light scattering (DLS), steady-state fluorescence, time resolved fluorescence quenching (TRFQ), tensiometry, conductimetry, and isothermal titration calorimetry (ITC) to investigate the self-assembly of the cationic surfactant cetyltrimethylammonium sulfate (CTAS) in aqueous solution, which has SO(2-)4 as divalent counterion. We obtained the critical micelle concentration (cmc), aggregation number (N(agg)), area per monomer (a0), hydrodynamic radius (R(H)), and degree of counterion dissociation (alpha) of CTAS micelles in the absence and presence of up to 1 M Na2SO4 and at temperatures of 25 and 40 degrees C. Between 0.01 and 0.3 M salt the hydrodynamic radius of CTAS micelle R(H) approximately 16 A is roughly independent on Na2SO4 concentration; below and above this concentration range R(H) increases steeply with the salt concentration, indicating micelle structure transition, from spherical to rod-like structures. R(H) increases only slightly as temperature increases from 25 to 40 degrees C, and the cmc decreases initially very steeply with Na2SO4 concentration up to about 10 mM, and thereafter it is constant. The area per surfactant at the water/air interface, a0, initially increases steeply with Na2SO4 concentration, and then decreases above ca. 10 mM. Conductimetry gives alpha = 0.18 for the degree of counterion dissociation, and N(agg) obtained by fluorescence methods increases with surfactant concentration but it is roughly independent of up to 80 mM salt. The ITC data yield cmc of 0.22 mM in water, and the calculated enthalpy change of micelle formation, Delta H(mic) = 3.8 kJ mol(-1), Gibbs free energy of micellization of surfactant molecules, Delta G(mic) = -38.0 kJ mol(-1) and entropy TDelta S(mic) = 41.7 kJ mol(-1) indicate that the formation of CTAS micelles is entropy-driven.