Investigation of Thermal-Induced Changes in Molecular Order on Photopolymerization and Performance Properties of a Nematic Liquid-Crystal Diacrylate.

Polymerization shrinkage and associated stresses are the main reasons for dental restorative failure. We developed a series of liquid crystal diacrylates and dimethacrylates which have markedly low polymerization shrinkage. In order to fully understand the effects of temperature-induced changes of molecular order on the photopolymerization process and performance properties of the generated polymers, the photopolymerization of a difunctional acrylate, 2-t-butyl-1,4-phenylene bis (4-(6-(acryloyloxy)hexyloxy)benzoate), which exists in the nematic liquid crystalline phase at room temperature, was investigated as a function of photopolymerization temperature over the nematic to isotropic range. Morphological studies suggested that a mesogenic phase was immediately formed in the polymer even if polymerization in thin films occurred above the nematic-to-isotropic (N→I) transition temperature of the monomer (Tn-i = 45.8 °C). Dynamic mechanical analysis of 2 × 2 mm cross-section bar samples polymerized at 60 °C showed reduced elastic moduli, increased glass transition temperature and formation of a more crosslinked network, in comparison to polymers formed at lower polymerization temperatures. Fractography analysis showed that polymers generated from the nematic liquid crystalline phase underwent a different fracture pattern in comparison to those generated from the isotropic phase. Volumetric shrinkage (2.2%) found in polymer polymerized from the nematic liquid crystalline phase at room temperature was substantially less than the 6.0% observed in polymer polymerized from an initial isotropic phase at 60 °C, indicating that an organized monomer can greatly contribute to reducing cure shrinkage.

A novel antimicrobial orthodontic band cement with in situ-generated silver nanoparticles.

OBJECTIVE: To develop an antimicrobial orthodontic band cement for the prevention of white spot lesions using a novel process that generates silver nanoparticles (AgNP) in situ. MATERIALS AND METHODS: Twenty-seven groups of AgNP-loaded Opal Band Cement (OBC) and two control groups were formulated with varying concentrations of additional benzoyl peroxide (0.5, 1.0, 1.5, or 2.0 wt%) and 2,2-(p-Tolylimino) diethanol (0.5 or 1 wt%). Rockwell15T hardness and near-infrared FTIR were used to assess degree of cure, three-point bending was used to determine modulus and ultimate transverse strength (UTS), and Ag(+) ion release was measured for up to 4 months in vitro using atomic absorption spectroscopy. Antimicrobial activity against Streptococcus mutans and Lactobacillus acidophilus was tested in vitro by counting colony-forming units for up to 28 days. Biocompatibility was evaluated following ISO specifications 7405 (2008), 10993-3 (2003), 10993-5 (2009), and 10993-10 (2010). RESULTS: Most of the experimental groups had hardness, modulus, and UTS values similar to those of the control group. Ag(+) ion release was observed for all AgNP-loaded groups for up to 4 months. Increase in Ag loading increased Ag(+) ion release and in vitro antimicrobial effect. The biocompatibility of the optimal AgNP-loaded OBC was comparable to that of negative controls. CONCLUSION: A novel antimicrobial orthodontic band cement was developed that has comparable mechanical properties to controls, controlled and sustained Ag(+) ion release, significant bacterial inhibition in vitro, and excellent biocompatibility.