RESUMO
There is a dearth of adhesive systems capable of forming stable bonds between restorative materials and tooth surfaces. To address the concern, this study determined the effects of using methacrylate-functionalized boron nitride nanosheets (BNNSs) in a polymeric dental adhesive system. The bisphenol A glycidyl dimethacrylate (BisGMA):2 hydroxyethyl methacrylate (HEMA) (60:40) adhesive monomer blend with a photoinitiator was filled with 0 wt% (control), 0.1 wt%, and 1 wt% BNNSs and light cured. Fourier transform infrared spectroscopy was performed to determine the conversion degree of monomer double bonds (DoC). Water absorption and solubility were measured. Flexural strength and Youngs's modulus were evaluated to determine the mechanical properties of the composite adhesive system. Finally, dentin bond strength degradation and fracture mode were quantified with a microtensile bond test to confirm the bonding ability of the developed adhesive system. Results showed that the incorporation of BNNSs increased DoC (9.8% and 5.4% for 0.1 and 1 wt%, respectively), but it did not affect water sorption (101.9-119.72 (µg/mm3)), solubility (2.62-5.54 (µg/mm3)), Young's modulus (529.1-1716.1 MPa), or microtensile bond strength (46.66-54.72 MPa). Further studies are needed with varying BNNS loading percentages from 0.1 wt% to 1 wt% in order to more comprehensively determine the effect of BNNSs on dental adhesives.
RESUMO
OBJECTIVES: The present in vitro study evaluated the effect of 1-ethyl-3-(3-dimethylaminopropyl) carbodiimide (EDC), a cross-linking agent used as an additional therapeutic primer for luting fiber posts to radicular dentine to prevent hybrid layer degradation. METHODS: Root canal treatment was performed on 80 extracted single-rooted human teeth. A 10-mm post space was prepared and pecimens were randomly assigned to four groups (n=20) according to the bonding system: 1) All Bond 3 (Bisco); 2) All Bond 3 + 0.3M EDC; 3) Prime&Bond XP (Dentsply Sirona); 4) Prime&Bond XP + 0.3M EDC. In groups 2 and 4, EDC was applied on phosphoric acid-etched dentine for 1 min. Fiber posts (RelyX Fiber Post, 3M ESPE) were luted with a dual-cured resin cement (Core-X flow, Dentsply Sirona). Slices were prepared for micro push-out test and interfacial nanoleakage evaluation of the coronal and apical region of the canal space after 24 h and 1 year storage in artificial saliva. In-situ zymography was performed to investigate endogenous matrix metalloproteinase activities within the hybrid layer. Results were statistically analysed with three-way ANOVA test or Chi Square test. Statistical significance was set at α=0.05. RESULTS: No significant influence was identified between the two adhesives. The use of EDC significantly improved fiber post bond strength at 1 year but not at 24 h. Application of 0.3 M EDC prior to bonding significantly reduced gelatinolytic activities within the radicular hybrid layers. CONCLUSIONS: Carbodiimide was effective in preserving fibre post bond strength over time, through reducing the activities of intra-radicular endogenous proteases. CLINICAL SIGNIFICANCE: Inhibition of matrix metalloproteinases using EDC over radicular dentin could play an important role in bond strength preservation. However, the clinical relevance of these findings needs to be proven.