Energy-dispersive X-ray micro Laue diffraction on a bent gold nanowire.

This article reports on energy-dispersive micro Laue (µLaue) diffraction of an individual gold nanowire that was mechanically deformed in three-point bending geometry using an atomic force microscope. The nanowire deformation was investigated by scanning the focused polychromatic X-ray beam along the nanowire and recording µLaue diffraction patterns using an energy-sensitive pnCCD detector that permits measurement of the angular positions of the Laue spots and the energies of the diffracted X-rays simultaneously. The plastic deformation of the nanowire was shown by a bending of up to 3.0 ± 0.1°, a torsion of up to 0.3 ± 0.1° and a maximum deformation depth of 80 ± 5 nm close to the position where the mechanical load was applied. In addition, extended Laue spots in the vicinity of one of the clamping points indicated the storage of geometrically necessary dislocations with a density of 7.5 × 1013 m-2. While µLaue diffraction with a non-energy-sensitive detector only gives access to the deviatoric strain, the energy sensitivity of the employed pnCCD offers absolute strain measurements with a resolution of 1%. Here, the residual strain after complete unloading of the nanowire amounted to maximum tensile and compressive strains of the order of +1.2 and -3%, which is comparable to the actual resolution limit. The combination of white-beam µLaue diffraction using an energy-sensitive pixel detector with nano-mechanical testing opens up new possibilities for the study of mechanical behavior at the nanoscale.

Single-shot full strain tensor determination with microbeam X-ray Laue diffraction and a two-dimensional energy-dispersive detector.

The full strain and stress tensor determination in a triaxially stressed single crystal using X-ray diffraction requires a series of lattice spacing measurements at different crystal orientations. This can be achieved using a tunable X-ray source. This article reports on a novel experimental procedure for single-shot full strain tensor determination using polychromatic synchrotron radiation with an energy range from 5 to 23 keV. Microbeam X-ray Laue diffraction patterns were collected from a copper micro-bending beam along the central axis (centroid of the cross section). Taking advantage of a two-dimensional energy-dispersive X-ray detector (pnCCD), the position and energy of the collected Laue spots were measured for multiple positions on the sample, allowing the measurement of variations in the local microstructure. At the same time, both the deviatoric and hydrostatic components of the elastic strain and stress tensors were calculated.

A new method for polychromatic X-ray µLaue diffraction on a Cu pillar using an energy-dispersive pn-junction charge-coupled device.

µLaue diffraction with a polychromatic X-ray beam can be used to measure strain fields and crystal orientations of micro crystals. The hydrostatic strain tensor can be obtained once the energy profile of the reflections is measured. However, this remains a challenge both on the time scale and reproducibility of the beam position on the sample. In this review, we present a new approach to obtain the spatial and energy profiles of Laue spots by using a pn-junction charge-coupled device, an energy-dispersive area detector providing 3D resolution of incident X-rays. The morphology and energetic structure of various Bragg peaks from a single crystalline Cu micro-cantilever used as a test system were simultaneously acquired. The method facilitates the determination of the Laue spots' energy spectra without filtering the white X-ray beam. The synchrotron experiment was performed at the BM32 beamline of ESRF using polychromatic X-rays in the energy range between 5 and 25 keV and a beam size of 0.5 µm × 0.5 µm. The feasibility test on the well known system demonstrates the capabilities of the approach and introduces the "3D detector method" as a promising tool for material investigations to separate bending and strain for technical materials.