Heat-sink free CW operation of injection microdisk lasers grown on Si substrate with emission wavelength beyond 1.3 µm.

High-performance injection microdisk (MD) lasers grown on Si substrate are demonstrated for the first time, to the best of our knowledge. Continuous-wave (CW) lasing in microlasers with diameters from 14 to 30 µm is achieved at room temperature. The minimal threshold current density of 600 A/cm2 (room temperature, CW regime, heatsink-free uncooled operation) is comparable to that of high-quality MD lasers on GaAs substrates. Microlasers on silicon emit in the wavelength range of 1320-1350 nm via the ground state transition of InAs/InGaAs/GaAs quantum dots. The high stability of the lasing wavelength (dλ/dI=0.1 nm/mA) and the low specific thermal resistance of 4×10-3°C×cm2/W are demonstrated.

Single-Exciton Photoluminescence in a GaN Monolayer inside an AlN Nanocolumn.

GaN/AlN heterostructures with thicknesses of one monolayer (ML) are currently considered to be the most promising material for creating UVC light-emitting devices. A unique functional property of these atomically thin quantum wells (QWs) is their ability to maintain stable excitons, resulting in a particularly high radiation yield at room temperature. However, the intrinsic properties of these excitons are substantially masked by the inhomogeneous broadening caused, in particular, by fluctuations in the QWs' thicknesses. In this work, to reduce this effect, we fabricated cylindrical nanocolumns of 50 to 5000 nm in diameter using GaN/AlN single QW heterostructures grown via molecular beam epitaxy while using photolithography with a combination of wet and reactive ion etching. Photoluminescence measurements in an ultrasmall QW region enclosed in a nanocolumn revealed that narrow lines of individual excitons were localized on potential fluctuations attributed to 2-3-monolayer-high GaN clusters, which appear in QWs with an average thickness of 1 ML. The kinetics of luminescence with increasing temperature is determined via the change in the population of localized exciton states. At low temperatures, spin-forbidden dark excitons with lifetimes of ~40 ns predominate, while at temperatures elevated above 120 K, the overlying bright exciton states with much faster recombination dynamics determine the emission.