Effect of Cerium on Inclusion Evolution and Pitting Corrosion of Nb-Microalloyed Steel.

Nb-microalloyed steels are widely used in construction engineering fields due to their excellent mechanical properties, but they face serious corrosion problems in service environments. Pitting corrosion is the severest form of corrosion, and the types of inclusions are the leading cause to induce pitting corrosion. A new strategy is proposed to enhance the corrosion resistance of steels by achieving a beneficial transformation of inclusions with Ce treatment. In this paper, two types of Nb-microalloyed steels (0% Ce and 0.0058% Ce steel) were prepared to study the modification effect on inclusions in industrial production. The spherical CaS•C12A7 inclusions were modified to smaller ellipsoidal Ce2O2S inclusions, and the proportion of inclusions (0-2 µm) increased significantly from 27 to 66%, while large inclusions (>6 µm) disappeared. A kinetic model of inclusion evolution was established. The results of electrochemical tests indicated that the corrosion potential was positively shifted, and the corrosion current was reduced after Ce treatment. Additionally, the number of defects in the passivation film was decreased, and the corrosion resistance of the steel was significantly improved. The addition of Ce changed the types of inclusions and reduced the number of pitting nucleation points, which led to a remarkable reduction in the number and size of pitting pits. The mechanism of pitting corrosion induced by different types of inclusions was further investigated, and a pitting corrosion model was modeled based on the immersion experiments. Research results provide theoretical support for enhancing the corrosion resistance of steel.

Degradation Behavior of Medical MgZZC-1 in Various Simulated Body Fluids.

Magnesium-based biodegradable metal bone implants exhibit superior mechanical properties compared to biodegradable polymers for orthopedic and cardiovascular stents. In this study, MgZZC-x (x = 1, 1.2) alloys were screened by in vitro biocompatibility tests in three simulated body fluids under nontoxic conditions. The MgZZC-1 alloys with better biocompatibility were selected to predict the days required for complete degradation. The evolution of degradation products was analyzed, and the mechanism of formation of the product film was inferred. A degradation kinetic model was established to investigate the effect of MEM components on the degradation of the alloys. The results demonstrate that the proteins in MEM can greatly retard the degradation progress by attaching to the surface of MgZZC-1 alloys, which are predicted to degrade completely within 341 days. The carbonate and phosphate buffers were adjusted to pH in MEM solution, delaying the degradation of magnesium alloys. This process in MEM more accurately reflects the actual degradation in the body and is superior to that in Hanks and SBF solutions. This study will promote the application of biodegradable materials in clinical medicine.

Preparation of Superhydrophobic Coating on X80 Steel and Its Corrosion Resistance in Oilfield Produced Water.

Corrosion is an unavoidable issue that steel encounters during service; however, the generic methods employed for corrosion prevention often need high cost or preparation conditions. In this study, a facile chemical replacement deposition method was proposed to realize an anticorrosion superhydrophobic coating on a X80 steel surface. The growth mechanism of the rough structure and its impact on the wettability of the superhydrophobic coating were analyzed. The superhydrophobic coating, deposited for 50 s and modified for 30 min, achieved optimal electrochemical properties and a maximum water contact angle. The immersion test, in the saturated CO2 oilfield produced water, demonstrated the better corrosion resistance of superhydrophobic coating than X80 steel. Correspondingly, a kinetic corrosion model was established to analyze the anticorrosion mechanism. In summary, this method significantly improves the corrosion resistance of X80 steel and is attractive for other industrial fields.

Corrosion Inhibition Mechanism of Water-Soluble Imidazoline on A572 Gr.65 Steel in 3.5 wt % NaCl Solution.

To optimize the economic advantages and corrosion-resisting property of A572 Gr.65 steels, the inhibition effect of water-soluble imidazoline on the sample surface with rare earth was explored in a 3.5 wt % NaCl solution. In this paper, the mechanism of corrosion and the adsorptive behavior of water-soluble imidazoline inhibitors on A572 Gr.65 steels with 47 ppm of rare earth in saltwater solution were discussed, along with the establishment of the adsorption model. Achievements proposed that the inhibition efficiency of water-soluble imidazoline was as high as 95.73% at 80 mg L-1 dosage following an anodic-dominated mixed-type inhibition mechanism. Besides, the scanning electron microscopy and X-ray diffraction analysis revealed that the corrosion inhibitor resulted in a smoother and more stable rust layer with a significant reduction of the γ-FeOOH. Theoretical calculations confirmed that imidazoline formed a unimolecular layer adsorption film on the steel surface, exhibiting adherence to both Langmuir and Frumkin adsorption isotherms, involving physical and chemical adsorption.