Determination of zinc incorporation in the Zn-substituted gallophosphate ZnULM-5 by multiple wavelength anomalous dispersion techniques.

The location of isomorphously substituted zinc over eight crystallographically different gallium sites has been determined in a single-crystal study of the gallophosphate ZnULM-5, Ga((16-x))Zn(x)(PO(4))(14)(HPO(4))(2)(OH)(2)F(7), [H(3)N{CH(2)}(6)NH(3)](4), 6H(2)O, in an 11 wavelength experiment, using data from Station 9.8, SRS Daresbury. The measurement of datasets around the K edges of both Ga and Zn, as well as two reference datasets away from each absorption edge, was utilized to selectively exploit dispersive differences of each metal atom type in turn, which allowed the major sites of Zn incorporation to be identified as the metal 1 and 3 sites, M1 and M3. The preferential substitution of Zn at these sites probably arises because they are located in double four-ring (D4R) building units which can relax to accommodate the incorporation of hetero atoms. As the crystal is non-centrosymmetric, with space group P2(1)2(1)2, it was also possible to use anomalous differences to corroborate the results obtained from the dispersive differences. These results were obtained firstly from difference Fourier maps, calculated using a phase set from the refined structure from data measured at the Zr K edge. Also, refined dispersive and anomalous occupancies, on an absolute scale, could be obtained using the program MLPHARE, allowing estimates for the Zn incorporation of approximately 22 and 18 at. % at the M1 and M3 sites to be obtained. In addition, f' and f'' values for Ga and Zn at each wavelength could be estimated both from MLPHARE results, and by refinement in JANA2006. The fully quantitative determinations of the dispersive and anomalous coefficients for Ga and Zn at each wavelength, as well as metal atom occupancies over the eight metal atom sites made use of the CCP4's MLPHARE program as well as SHELXL and JANA2006. The results by these methods agree closely, and JANA2006 allowed the ready determination of standard uncertainties on the occupancy parameters, which were for M1 and M3, 20.6 (3) and 17.2 (3) at %, respectively.

Determination of the site of incorporation of cobalt in CoZnPO-CZP by multiple-wavelength anomalous-dispersion crystallography.

Data were collected from a crystal of CoZnPO-CZP {sodium cobalt-zinc phosphate hydrate, Na(6)[Co(0.2)Zn(0.8)PO(4)](6).6H(2)O} using synchrotron radiation at ELETTRA at the inflection point and 'white line' for both the cobalt and zinc K edges, and at 1.45 Å, a wavelength remote from the K edges of both metals. The data were processed using the programs DENZO and SCALEPACK. The CCP4 program suite was used for the scaling of data sets and the subsequent calculation of dispersive difference Fourier maps. Optimal scaling was achieved by using a subset of reflections with little or no contribution from the metal atoms (i.e. which were essentially wavelength independent in their intensities) and using weights based on the sigma's to obtain an overall scale factor in each case. Phases were calculated with SHELXL97 based on the refined structure using a much higher resolution and complete Cu Kalpha data set. An occupancy of 100% by zinc at the two metal-atom sites was assumed. The dispersive difference Fourier map calculated for zinc gave two peaks above the background of similar heights at the expected metal-atom sites. The peak height at the Zn1 site was a little higher than at the Zn2 site. The dispersive difference Fourier map calculated for cobalt gave just one peak above the background, at the Zn1 site, and only a small peak at the Zn2 site, thus indicating that incorporation of cobalt takes place mainly at one site. Refinement of the zinc occupancies using MLPHARE reinforces this conclusion. The chemical environment of each site is discussed.

Development of natural zeolites for their use in water-treatment systems.

This paper gives an overview of research and patents concerning the use of natural zeolites in water-treatment systems in the last ten years. Furthermore, nanocomposite materials made of natural zeolites and organic and polymeric materials are also mentioned as an effective solution in water treatment. An additional emphasis is put on a variety of possibilities for further application of natural zeolite materials for environment protection and preservation.

Mesoporous aluminophosphate thin films with cubic pore arrangement.

Mesoporous aluminophosphate thin films with 3D cubic (Im3m) pore arrangement were synthesized for the first time. Thin films were templated with block copolymer nonionic templates Pluronic F127 and F108 and deposited on a glass substrate by dip-coating. In situ SAXS investigations show the formation of a highly ordered mesostructure upon the dip-coating process, which remains stable up to at least 670 K. A cubic mesostructure was observed also by TEM. Template removal process was monitored by TG and FT-IR. A transition from an amorphous aluminophosphate gel to a well-defined aluminophosphate framework was observed by MAS NMR.