In vitro evaluation of freeze-drying chitosan-mineralized collagen/Mg-Ca alloy composites for osteogenesis.

ABSTRACT

Magnesium (Mg) alloy with good mechanical properties and biodegradability is considered as one of the ideal bone repair materials. However, the rapid corrosion of Mg-based metals can pose harm to the function of an implant in clinical applications. In this study, micro-arc oxidation coating was prepared on the surface of the Mg-Ca matrix, then the chitosan and mineralized collagen (nano-hydroxyapatite/collagen; nHAC) were immobilized on the surface of the MAO/Mg-Ca matrix to construct the CS-nHAC/Mg-Ca composites of different component proportions (the ratio of CS to nHAC is 21, 11, and 12, respectively). The corrosion resistance, osteogenic activity, and angiogenic ability were extensively investigated. The results indicated that the CS-nHAC reinforcement materials can improve the corrosion resistance of the Mg matrix significantly and promote the proliferation and adhesion of mouse embryo osteoblast precursor cells (MC3T3-E1) and human umbilical vein endothelial cells (HUVECs). In addition, the CS-nHAC/Mg-Ca composites can not only promote the alkaline phosphatase (ALP) activity and extracellular matrix mineralization of MC3T3-E1 cells but also enhance the migration motility and vascular endothelial growth factor (VEGF) expression of HUVECs. Meanwhile, the 2CS-1nHAC/Mg-Ca composite exhibited the optimum function characteristics compared with other samples. Therefore, considering the improvement of corrosion resistance and biocompatibility, the CS-nHAC/Mg-Ca composites are expected to be a promising orthopedic implant.