Engineering performance of tungsten network reinforced copper matrix composites synthesized by selective laser melting and infiltration.

ABSTRACT

To solve poor engineering performance of copper-tungsten alloys operated at high temperatures, 3D network tungsten frameworks were prepared using a selective laser melting (SLM) process, and then copper was melted and diffused into these tungsten network structures to form copper matrix composites with different copper contents (i.e. Cu-10vol%W and Cu-30vol%W). Their mechanical/electrical properties and arc ablation performance were characterized. Results showed the obtained CuW composites were dense with good interfacial bonding, and the connected Cu phases formed a heat conduction channel and improved electrical and thermal conductivities of the composites. Electrical conductivities of Cu-30W and Cu-10W composites were 44.7% and 80.3% IACS, and their thermal conductivities at 25°C were 247.5 and 375.4 W/(m·K), respectively. The W-skeleton grid structure in the composites showed enhanced effects on impact toughness and anti-friction/wear resistance. Tensile strengths of Cu-30W and Cu-10W composites measured at 300°C were 95 MPa and 135 MPa, and their impact toughness values were 11.25 and 15.25 J/cm2, respectively. For the arc ablation performance, the copper phase of CuW composite was identified as the key influencing phase, whereas the W skeleton effectively hindered the spread of arc spots, inhibited quick melting of copper phases, and played effective support and protection functions.

W network reinforced Cu matrix composites were prepared by combining 3D printing technology and fusion technology, which significantly improved the thermal and mechanical properties of Cu matrix composites. We find that the interconnected Cu phases improves the thermal properties of the composites, and the mesh W skeleton improves the mechanical properties.