الملخص
INTRODUCTION: The low pH of sports drinks may cause tooth enamel demineralization. Objective: To measure Vickers hardness of human enamel exposed to sports drinks. METHODS: Human molars were used to collect the enamel samples. Each sample had a test surface (exposed to the drinks) and a control surface (unexposed). The samples were exposed to isotonic drinks Gatorade and Powerade, and to maltodextrin drinks Malto Advanced and Malto Active, for 10 minutes every 12 hours over 30 days. The Vickers microhardness test was conducted with three indentations on each surface. The mean of the indentations within each group was considered in the statistical analysis. Sports drinks variables were analyzed with ANOVA/Tukey (p≤0.01). The independent t-test was used in the comparison between the control and test surfaces of each drink (p ≤ 0.05). RESULTS: Enamel exposure to Gatorade (p = 0.000) Malto Advanced (p = 0.000) and Malto Active (p = 0.000) was seen to significantly reduce microhardness, while the isotonic drink Powerade had no significant effect on enamel (p = 0.248). CONCLUSION: It was concluded that with the exception of the isotonic drink Powerade, all the sports drinks tested caused a reduction in the microhardness of human enamel. Evidence Level III; Therapeutic studies - Investigating the Results of Treatment.
INTRODUÇÃO: O baixo pH de bebidas esportivas pode promover perda mineral do esmalte dental. OBJETIVO: Avaliar a microdureza Vickers do esmalte humano exposto a bebidas esportivas. MÉTODOS: Dentes molares humanos foram usados para coletar as amostras de esmalte. Cada amostra apresentou uma superfície de teste (exposta às bebidas) e uma superfície de controle (não exposta). As amostras foram expostas aos isotônicos Gatorade e Powerade e às maltodextrinas Advanced Series e Malto Active durante 10 minutos de 12/12 horas, durante 30 dias. O teste de microdureza Vickers foi realizado com três indentações em cada superfície. Na análise estatística, foi considerada a média das indentações dentro de cada grupo. As variáveis bebidas esportivas foram avaliadas com ANOVA/Tukey (p ≤ 0,01). Na comparação entre a superfície controle e teste de cada bebida foi utilizado o Teste t para amostras independentes (p ≤ 0,05). RESULTADO: Observou-se que a exposição do esmalte a Gatorade (p = 0,000), Malto Advanced (p = 0,000) e Malto Active (p = 0,000) reduz significativamente a microdureza, enquanto que o isotônico Powerade não produziu efeito significativo sobre o esmalte (p = 0,248). CONCLUSÃO: Concluiu-se que com exceção do isotônico Powerade, todas as bebidas esportivas testadas provocaram redução na microdureza do esmalte dental humano. Nível de Evidência III; Estudos terapêuticos investiga o resultado de um tratamento.
INTRODUCCIÓN: El bajo pH de bebidas deportivas puede favorecer la pérdida mineral del esmalte dental. OBJETIVO: Evaluar el esmalte dureza Vickers humano expuesto a las bebidas deportivas. MÉTODOS: Se utilizaron los dientes molares para la toma de las muestras de esmalte. Cada muestra tenía una superficie de prueba (expuestos a las bebidas) y una superficie de control (no ex-puesta). Las muestras fueron expuestas en isotónica Gatorade y Powerade, y maltodextrinas, y la serie Advanced activo Malto durante 10 minutos 12/12 horas durante 30 días. La prueba de dureza Vickers se realizó con tres muescas en cada superficie. El análisis estadístico fue la media de las muescas dentro de cada grupo. variables de bebidas deportivas se analizaron con ANOVA / Tukey (p≤0,01). La comparación entre la superficie de control y prueba de cada bebida se utilizó la prueba t para muestras independientes (p ≤ 0,05). RESULTADOS: Se observó que la exposición del esmalte Gatorade (p = 0,000) Malto avanzada (p = 0,000) y Malto activo (p = 0,000) reduce significativamente la dureza, mientras que Powerade isotónica ningún efecto significativo sobre el esmalte (p = 0,248). CONCLUSIÓN: Se concluye que con la excepción de Powerade isotónica, todas las bebidas deportivas probados causó una reducción en la dureza del esmalte humano. Nivel de Evidencia; Estudios terapéuticos - Investigación de los resultados del tratamento.
الموضوعات
Humans , Tooth Erosion/etiology , Dental Enamel/chemistry , Energy Drinks/analysis , Energy Drinks/adverse effects , Analysis of Variance , Tooth Demineralization/etiology , Dental Enamel Solubility , Athletic Performance/physiology , Hardness Tests/methodsالملخص
Objective: To evaluate the influence of three methods of finishing and polishing on color stability of a microhybrid composite immersed in different beverages for 7, 15 and 30 days. Material and Methods: 90 samples were prepared and divided into three groups according to surface treatments (polyester matrix, aluminum oxide disc, sandpaper). The samples were divided for each group (n = 6) and immersed in one of the beverages: distilled water, red and white wine, red and white artificial grape juice. Pictures were taken at four time points: 0, 7, 15 and 30 days after contact with the dye. Color measurement was performed by computerized image analysis. La*b* values were obtained and color change (ΔE) was calculated. Results: Comparing beverages, red wine (ΔE =22.11±4.26) and red artificial grape juice (ΔE=8.24±1.70) showed greater color change in polyester matrix group, and finishing with aluminum oxide disc (ΔE=10.73±2.10) significantly prevent color change in red wine group. Conclusion: Aluminum oxide discs are the best option to minimize color changes in resin. White drinks are alternatives to color stability of composite resin. In the study time, composite resin demonstrated progressive discoloration when immersed in red wine and red juice. On the other hand, samples submitted to white beverages showed higher color stability.
الموضوعات
Color , Composite Resins/chemistry , Dental Polishing , Fruit and Vegetable Juices , Pigmentation , Brazil , Statistics, Nonparametric , Surface Propertiesالملخص
Dentes com grande destruição coronária submetidos a tratamento endodôntico devem ser reconstruídos por meio da inserção de um pino intrarradicular, com finalidade de se obter retenção para o material restaurador e melhor distribuição de forças sobre o remanescente dental. A reconstrução coronária desses elementos dentais pode ser realizada com técnicas restauradoras indiretas ou diretas. A evolução das técnicas operatórias e das propriedades físicas, mecânicas e estéticas das resinas compostas tem ampliado suas indicações clínicas, e, quando associadas a pinos intracanais cimentáveis, têm permitido avanços nas reconstruções dentárias. Muitas situações clínicas, que tradicionalmente apresentavam soluções protéticas, hoje podem ser resolvidas através de restaurações diretas com resina composta. Este trabalho apresenta dois casos clínicos onde se realizaram alternativas viáveis de reabilitação de dentes com grande destruição coronária utilizando reconstruções totais diretas com uma resina composta micro-híbrida como material de eleição, associada à utilização de um pino de fibra de vidro e um pino metálico pré-fabricado. Em ambos os casos, foram realizadas as cimentações dos pinos intracanais com cimento ionomérico modificado por resina, seguindo o protocolo tradicional para desobturação dos canais radiculares. Associada ao pino de fibra de vidro foi utilizada a técnica da matriz de silicona como meio para reconstruir a coroa dental, enquanto que junto ao pino metálico lançou-se mão da matriz de Ableh. Concluiu-se que as técnicas descritas constituem procedimentos alternativos, de baixo custo e rápida elaboração, conseguindo suprir as necessidades dos pacientes, demostrando ser uma boa opção para reabilitação de grandes destruições coronárias
Endodontic treated teeth with large coronal destruction need be restored by inserting an intracanalpost in order to obtain retention for the restorative material and a better mastigatory stress distribution along the tooth. Subsequently, dental techniques of direct or indirect restorations may be used. The constant evolution of the physical, mechanical and aesthetic properties of composite resins has expanded its clinical indications and adhesive cemented posts have enabled advances in dental reconstructions. Many clinical situations, which in the recent past had only prosthetic solution, can now be build-up with composite resin direct restorations. This paper presents two case reports where were performed viable alternatives for restoring teeth with major coronal destruction through direct total crown reconstruction, with a micro-hybrid composite resin associated with glass fiber post and prefabricated metal post. Both cases were carried out with adhesive cementation of the post, using a resin modified glass ionomer cement. Associated with the glass fiber post, a silicona matrix technique was used as a mean to reconstruct the tooth crown, while with the metallic post it was used the Ableh matrix. It was concluded that techniques described in this work are alternative low cost and fast procedures, which could meet the needs of patients, being a good option for rehabilitation of dental coronary destruction