ABSTRACT
This study investigated the effect of commercially available whitening toothpastes containing charcoal on dentin. Nine charcoal-containing toothpastes were compared with 3 whitening toothpastes (positive control) and distilled water (negative control). Periodontally hopeless molars were cleaned and washed and the occlusal table removed to expose dentin. The teeth were mounted in auto-polymerizing resin and exposed dentine surfaces polished with water-cooled decreasing grits of silica carbide paper up to 1500 grit. Baseline average roughness (Ra) measurements were taken. Specimens were then mounted in an automatic tooth-brushing machine and brushed for 5000 cycles. Repeat Ra measurements were taken. Specimens were brushed in 5000-cycle increments up to 25,000 cycles with Ra measurements being taken at each time point. Between abrasive challenges specimens were stored in distilled water. All toothpaste samples were sputter coated and examined under a scanning electron microscope to qualify the shape and size of the abrasive components of the formulations. Data were analyzed using a two-way analysis of variance with post hoc Bonferroni. The results demonstrated that the abrasive effect, in terms of increasing Ra, on dentin was noted as early as 5000 cycles for all the tested toothpastes (p<0.05). The effect of continued brushing showed an overall cumulative effect on dentine roughness up to 25000 cycles. When toothpastes were compared between groups at each time-point, dentin specimens brushed with Pursito were statistically similar to the control group. At 25,000 cycles all dentin samples were significantly rougher compared to Pursito and the control groups. It may be concluded that all the tested toothpastes have an abrasive effect on dentin surfaces.
Este estudio investigó el efecto sobre la dentina de las pastas dentales blanqueadoras disponibles en el mercado que contienen carbón vegetal. Se compararon nueve dentífricos que contenían carbón vegetal con 3 dentífricos blanqueadores (control positivo) y agua destilada (control negativo). Los molares sin material periodontal se limpiaron y lavaron y se retiró la tabla oclusal para exponer la dentina. Los dientes se montaron en resina autopolimerizable y las superficies expuestas de la dentina se pulieron con papel de carburo de sílice de grano decreciente enfriado con agua hasta grano 1500. Se tomaron medidas de rugosidad promedio (Ra) de referencia. Luego, las muestras se montaron en una máquina automática de cepillado de dientes y se cepillaron durante 5000 ciclos. Se tomaron medidas repetidas de Ra. Las muestras se cepillaron en incrementos de 5000 ciclos hasta 25 000 ciclos y se tomaron medidas de Ra en cada punto de tiempo. Entre periodos abrasivos, las muestras se almacenaron en agua destilada. Todas las muestras de pasta de dientes se recubrieron por pulverización catódica y se examinaron bajo un microscopio electrónico de barrido para calificar la forma y el tamaño de los componentes abrasivos de las formulaciones. Los datos se analizaron utilizando un análisis de varianza de dos vías de Bonferroni post hoc. Los resultados demostraron que el efecto abrasivo, en términos de aumento de Ra, sobre la dentina se notó ya en 5000 ciclos para todas las pastas dentales probadas (p<0,05). El efecto del cepillado continuo mostró un efecto acumulativo general sobre la rugosidad de la dentina hasta 25.000 ciclos. Cuando se compararon las pastas dentales entre los grupos en cada momento, las muestras de dentina cepilladas con Pursito fueron estadísticamente similares al grupo de control. A los 25.000 ciclos, todas las muestras de dentina eran significativamente más ásperas en comparación con Pursito y los grupos controles. Se puede concluir que todas las pastas dentales probadas tienen un efecto abrasivo sobre las superficies dentinarias.