Résumé
Endocrowns have emerged as a promising option for restoring endodontically treated teeth, offeringa restorable fracture scenario. However, regarding the choice of material and its fracture resistance, there are gaps in the literature regarding the best indication. The objective of this research was to evaluate and compare the effect of restorative materials for CAD-CAM in the manufacture of endocrown restorations, through an in Vitro study on hardness and fracture resistance. For the study, CAD-CAM blocks were transformed into discs 12 mm in diameter and 1.2 mm thick (specimens). Three restorative materials were evaluated and distributed into experimental groups (N=12 specimens): Leucita- Reinforced Ceramic/ IPS Empress CAD (MRleu), Lithium Disilicate/ IPS Emax CAD (MRdis) and Nanoceramic Resin /Lava Ultimate (MRres). These restorative materials were evaluated for morphology (N=1) by Scanning Electron Microscopy (SEM) and surface chemistry (N=1) by dispersive energy spectroscopy (EDS). The specimens were evaluated when the Vikers micro hardness (N=1) with a load of 1kg and 10 indentations, as well as the resistance to biaxial flexion (N=10) at a test speed of 0.5 mm/min. After the fracture occurred, the fragments were examined under a stereomicroscope. The results were tabulated and analyzed using the Minitab statistical program. The results showed that the MRdis material demonstrated superior results in relation to hardness (P=0.000) and biaxial bending resistance (P=0.000), followed by MRleu and finally the MRres. The presence of inorganic particles on an organic matrix and the presence of Zirconium (Zr) stands out in Lava Ultimate. It was concluded that restorative materials for CAD-CAM in the manufacture of Endocrowns restorations have a significant effect on hardness and mechanical strength.Endocrowns have emerged as a promising option for restoring endodontically treated teeth, offeringa restorable fracture scenario. However, regarding the choice of material and its fracture resistance, there are gaps in the literature regarding the best indication. The objective of this research was to evaluate and compare the effect of restorative materials for CAD-CAM in the manufacture of endocrown restorations, through an in Vitro study on hardness and fracture resistance. For the study, CAD-CAM blocks were transformed into discs 12 mm in diameter and 1.2 mm thick (specimens). Three restorative materials were evaluated and distributed into experimental groups (N=12 specimens): Leucita- Reinforced Ceramic/ IPS Empress CAD (MRleu), Lithium Disilicate/ IPS Emax CAD (MRdis) and Nanoceramic Resin /Lava Ultimate (MRres). These restorative materials were evaluated for morphology (N=1) by Scanning Electron Microscopy (SEM) and surface chemistry (N=1) by dispersive energy spectroscopy (EDS). The specimens were evaluated when the Vikers micro hardness (N=1) with a load of 1kg and 10 indentations, as well as the resistance to biaxial flexion (N=10) at a test speed of 0.5 mm/min. After the fracture occurred, the fragments were examined under a stereomicroscope. The results were tabulated and analyzed using the Minitab statistical program. The results showed that the MRdis material demonstrated superior results in relation to hardness (P=0.000) and biaxial bending resistance (P=0.000), followed by MRleu and finally the MRres. The presence of inorganic particles on an organic matrix and the presence of Zirconium (Zr) stands out in Lava Ultimate. It was concluded that restorative materials for CAD-CAM in the manufacture of Endocrowns restorations have a significant effect on hardness and mechanical strength. (AU)
As endocrowns surgiram como uma alternativa favorável para a restauração de dentes tratados endodonticamente, e se apresentam em um cenário de fratura restaurável. No entanto, em relação ao material de escolha e sua resistência à fratura existem lacunas na literature sobre a melhor indicação. O objetivo dessa pesquisa foi avaliar e comparar o efeito de materiais restauradores para CAD-CAM na confecção de restaurações endocrowns, através de um estudo in vitro sobre dureza e resistência à fratura. Para realização do estudo, blocos para CAD-CAM foram transformados em discos com 12 mm de diâmetro e 1,2 mm de espessura (espécimes). Três materiais restauradores foram avaliados e distribuídos em grupos experimentais (N=12 espécimes): Cerâmica Reforçada por Leucita/ IPS Empress CAD (MRleu), Dissilicato de Lítio/ IPS Emax CAD (MRdis) e Resina Nanocerâmica /Lava Ultimate (MRres). Estes materiais restauradores foram avaliados quanto à morfologia (N=1) através de Microscopia Eletrônica de Varredura (MEV) e química superficial (N=1) pela Espectroscopia de energia dispersiva (EDS). Os espécimes foram avaliados quanto à microdureza Vikers (N=1) com uma carga de 1kg e 10 indentações, como também em relação a resistência à flexão biaxial (N=10) em uma velocidade de ensaio de 0,5 mm/min. Os fragmentos após a fratura foram observados em estereomicroscópio. Os dados obtidos foram tabulados e analisados no programa estatístico Minitab. Os resultados observados mostraram que o material MRdis obteve resultados superiores em relação a dureza (P=0,000) e a resistência à flexão biaxial (P=0,000), seguido pelo MRleu e por fim o MRres. Destaca-se na Lava Ultimate a presença de partículas inorgânicas sobre uma matriz orgânica, além da presença de Zircônio (Zr). Conclui-se que materiais restauradores para CAD-CAM na confecção de restaurações Endocrowns apresentam efeito significativo quanto a dureza e resistência mecânica. (AU)
Résumé
Objetivo: avaliar in vitro o polimento sobre resina acrílica quimicamente ativada (RAQA), por meio da rugosidade de superfície (Ra). Materiais e Método: Foram confeccionadas 40 amostras de RAQA, com dimensões de 10 a 10 x 2 mm, e foram divididas em quatro grupos (n=10): ausência do acabamento (AA); Ausência de polimento (AP); Polimento químico (PQ); Polimento com borrachas siliconadas + Escovas (PM). Os espécimes foram avaliados no quanto a rugosidade média (Ra) antes e após o envelhecimento em água destilada em uma estufa por 60 dias. Três medições de Ra (µm), na horizontal foram realizadas e calculada uma média para cada espécime. Os dados foram analisados de forma descritiva e inferencial, ANOVA de medidas repetidas e teste de Tukey com nível de significância de 5%. Resultados: Inicialmente, o grupo AA teve os menores valores de Ra e o grupo AP os maiores valores de rugosidade, com média e desvio padrão respectivamente 0,17 (±0,11) e 0,52 (±0,10). Após o envelhecimento, o grupo AA teve as menores médias e o grupo PQ os maiores valores de Ra, sendo 0,38 (±0,20) e 1,33 (±0,32), respectivamente. Os resultados evidenciaram diferença estatística significante quando as amostras foram submetidas ao acabamento com brocas. Conclusão: A RAQA necessita de polimento após acabamento com brocas, uma vez que a ausência de polimento comprometerá a lisura de superfície do material.(AU)
Objective: to evaluate in vitro polishing on chemically activated acrylic resin (RAQA), using surface roughness (Ra). Materials and Method: 40 RAQA samples were made, measuring 10 to 10 x 2 mm, and divided into four groups (n=10): absence of finishing (AA); Lack of polishing (AP); Chemical polishing (PQ); Polishing with silicone rubbers + Brushes (PM). The specimens were evaluated for their average roughness (Ra) before and after aging in distilled water in an oven for 60 days. Three horizontal Ra (µm) measurements were taken and an average was calculated for each specimen. Data were analyzed descriptively and inferentially, using repeated measures ANOVA and Tukey test with a significance level of 5%. Results: Initially, the AA group had the lowest Ra values and the AP group the highest roughness values, with mean and standard deviation respectively 0.17 (±0.11) and 0.52 (±0.10). After aging, the AA group had the lowest averages and the PQ group the highest Ra values, being 0.38 (±0.20) and 1.33 (±0.32), respectively. The results showed a statistically significant difference when the samples were finished with drills. Conclusion: RAQA requires polishing after finishing with drills, as the lack of polishing will compromise the surface smoothness of the material.(AU)
Sujets)
Résines acryliques/composition chimique , Polissage dentaire/méthodes , Valeurs de référence , Siloxane élastomère , Propriétés de surface , Facteurs temps , Analyse de variance ,Résumé
ABSTRACT The use of removable partial dentures is considered a common and inexpensive treatment option to rehabilitate edentulous areas. The aim of this study was to evaluate the effect of different materials for provisional removable partial dentures, an in vitro study on surface roughness and fracture resistance. Thermopolymerizable acrylic resin and thermoplastic resin specimens with dimensions of 10 x 10 x 2 mm (blocks) (n=10) and with dimensions of 65 x 20 x 3 mm (bars) (n=10 were analyzed for their surface roughness (Ra) and three-point flexural strength test. All specimens were subjected to oven aging for 60 days at 37°C±0.5°C in distilled water. The statistical analysis was performed with a significance level of 5%, and the surface roughness data were submitted to the Two-way Anova statistical test (P < 0.05) and the mechanical strength data were subjected to One-way Anova statistical test (P < 0.05). For roughness, the factor resin type (P = 0.000) and the factor aging (P = 0.000) were statically significant, as well as showing interaction (P = 0.228). The Thermopolymerizable acrylic resin had the lowest mean roughness values compared to the thermoplastic resin and showed no statistical difference after aging. The same scenario was repeated for flexural strength values; Thermopolymerizable acrylic resin was statistically superior to thermoplastic resin (P = 0.000). Thermopolymerized acrylic resin showed lower surface roughness values and higher flexural strength values compared to thermoplastic resin.
RESUMO O uso de próteses parciais removíveis é considerado uma opção de tratamento comum e de baixo custo para reabilitar áreas edêntulas. O objetivo deste estudo foi avaliar o efeito de diferentes materiais para próteses parciais removíveis provisórias, um estudo in vitro sobre rugosidade superficial e resistência à fratura. Espécimes de resina acrílica termopolimerizável e de resina termoplástica com dimensões de 10 x 10 x 2 mm (blocos) (n = 10) e de 65 x 20 x 3 mm (barras) (n = 10) foram analisados em rugosidade superficial média (Ra) e teste de resistência à flexão de três pontos. Todos os espécimes foram submetidos ao envelhecimento em estufa por 60 dias a 37 ° C ± 0,5 ° C em água destilada. A análise estatística se deu com nível de significância de 5%, e os dados de rugosidade superficial foram submetidos ao teste estatístico Anova dois fatores (P <0,05) e os dados de resistência mecânica foram submetidos ao teste estatístico Anova um fator (P <0,05). Para rugosidade, o fator tipo resina (P = 0,000) e o fator envelhecimento (P = 0,000) foram estatisticamente significantes, além de apresentar interação (P = 0,228). A resina acrílica termopolimerizável apresentou menores valores médios de rugosidade em relação à resina termoplástica e não apresentou diferença estatística após envelhecimento. O mesmo cenário foi repetido para valores de resistência à flexão; a resina acrílica termopolimerizável foi estatisticamente superior à resina termoplástica (P = 0,000). A resina acrílica termopolimerizada apresentou menores valores de rugosidade superficial e maiores valores de resistência à flexão em relação à resina termoplástica.
Résumé
Este estudo avaliou o efeito do jateamento com óxido de alumínio prévio à camada de caracterização no comportamento adesivo e mecânico de zircônias de segunda e terceira gerações. Na parte A, foi realizado um estudo de resistência flexural. Para isso, discos de cada zircônia (3Y-TZP, 4Y-PSZ ou 5YPSZ) foram confeccionados. Após polimento e sinterização, os discos foram divididos de acordo com os tratamentos de superfície: Polimento, Jateamento com Al2O3 50 µm e Jateamento com Al2O3 110 µm (n = 30). A superfície tratada de todos os discos recebeu uma fina camada de pigmentação e uma fina camada de glaze. O ensaio de flexão biaxial foi realizado na configuração pistonon-three-balls e as superfícies fraturadas foram observadas em Microscopia Eletrônica de Varredura (MEV). Os dados foram submetidos à Análise de Weibull. Na parte B, avaliou-se o efeito dos diferentes tratamentos de superfície prévio à camada de caracterização no comportamento à fadiga das diferentes zircônias. Discos de 3Y-TZP, 4Y-PSZ e 5Y-PSZ foram confeccionados e distribuídos entre os tratamentos de superfície: Polimento ou Jateamento Al2O3 50 µm (n = 15), que foram realizados conforme a parte A deste estudo. Os discos foram cimentados adesivamente a um análogo de dentina (NEMA G10). Os testes de fadiga foram realizados pelo método stepwise, com aplicação de carga axial por um pistão hemisférico (carga inicial: 400 N, step: 100 N, ciclos/step: 10.000, frequência: 20 Hz). Na parte C, avaliou-se a resistência de união entre as diferentes zircônias e a camada de caracterização. Foram preparados os mesmos grupos descritos na "parte A" (n = 15). Cilindros de stain seguido por glaze foram construídos nas superfícies das zircônias. A resistência de união foi avaliada pelo teste de cisalhamento. Os tipos de falha (adesiva, predominantemente adesiva ou coesiva) foram analisados em estereomicroscópio e MEV. Análises complementares em perfilômetro e goniômetro foram realizadas. Para a parte A, o jateamento com Al2O3 110 µm aos menores valores de resistência à flexão, seguido do jateamento com as partículas de Al2O3 50 µm. Os maiores valores foram observados no grupo que não recebeu jateamento prévio à camada de caracterização. Esses resultados foram observados em todos os materiais. Na parte B, o jateamento com Al2O3 reduziu significativamente a carga e o número de ciclos para falha em fadiga de todos os materiais. Na parte C, os melhores valores de resistência de união foram atribuídos para o tratamento de superfície com Al2O3 110 µm, seguido de jateamento com Al2O3 50 µm e polimento. Dessa forma, o jateamento prévio à camada de caracterização reduz a resistência mecânica de zircônias de segunda geração e melhora a resistência de união entre os dois materiais (AU)
This study evaluated the effect of aluminum oxide sandblasting prior to the characterization layer on the adhesive and mechanical behavior of second- and third-generation zirconia. Part A consisted of a flexural strength study. Discs of each zirconia (3Y-TZP, 4Y-PSZ, or 5Y-PSZ) were prepared. After polishing and sintering, the discs were divided according to the surface treatments: Polishing, Sandblasting with Al2O3 50 µm and Sandblasting with Al2O3 110 µm (n = 30). The treated surface of all discs received a thin layer of stain and a thin layer of glaze. The biaxial bending test was performed in a piston-on-three-balls set-up. The fractured surfaces were observed by Scanning Electron Microscopy (SEM). Data were subjected to Weibull Analysis. In part B, the effect of different surface treatments prior to the characterization layer on the fatigue behavior of different zirconia was evaluated. Discs of 3Y-TZP, 4Y-PSZ and 5Y-PSZ were prepared and divided among the surface treatments: Polishing or Sandblasting Al2O3 50 µm (n = 15), which were performed according to part A of this study. The discs were adhesively cemented to a dentin-analogue (NEMA G10). Fatigue tests were performed using the stepwise method, with an axial load application by a hemispherical piston (initial load: 400 N, step: 100 N, cycles/step: 10,000, frequency: 20 Hz). Part C evaluated the bond strength between the different zirconia and the characterization layer. The same groups described in part A (n = 15) were prepared. Stain cylinders followed by glaze were built on the zirconia surfaces. The bond strength was evaluated by the shear test. The types of failure (adhesive, predominantly adhesive or cohesive) were analyzed using a stereomicroscope and SEM. Complementary analyzes in profilometer and goniometer were carried out. In part A, sandblasting with Al2O3 110 µm led to the lowest flexural strength results, followed by sandblasting with Al2O3 50 µm. Polishing group achieved the highest values. These results were observed in all tested ceramics. In part B, sandblasting with Al2O3 50 µm significantly reduced the fatigue failure load and the number of cycles for fatigue failure. In part C, the highest bond strength results were reached by sandblasting with Al2O3 110 µm, followed by sandblasting with Al2O3 50 µm, and polishing. Therefore, aluminum oxide particles sandblasting diminishes the mechanical behavior of second- and third-generation zirconias and improves the bond strength between the two materials. (AU)
Sujets)
Matériaux dentaires , Essais MécaniquesRésumé
ABSTRACT Objectives: The objective was to evaluate the longevity of ceramic restorative materials in the manufacture of endocrown restorations, through an in vitro study on surface roughness and mechanical strength. Methods: Three restorative materials were evaluated and assigned to experimental groups (n=10 disc specimens): Leucite Reinforced Ceramic, Lithium Disilicate and Nanoceramic Resin. These restorative materials were evaluated for surface before and after aging (n=02 specimens) under a stereomicroscope. The specimens were submitted to the average surface roughness test (Ra) (n=10) in a contact roughness meter before and after aging. As well as the biaxial flexural strength test (n=10), after aging, up to a test speed of 0.5 mm/min. Aging was carried out in a thermocycler, with 5,000 cycles with baths of 5 °C ± 1 ° and 55 °C ± 1 °. Fragments after fracture were observed under a stereomicroscope. The data obtained were tabulated and analyzed using the Minitab statistical program. Results: The surfaces of the specimens do not show changes between the restorative materials and also in relation to aging. For the roughness data, the restorative material factors (p=0.867) and aging (p=0.321) were not statistically significant. The DIS group presented the highest values of fracture resistance (p=0.000), in relation to the LEU and REN groups, which were statistically similar. The same statistical pattern was identified for post-fracture fragment data (p=0.030). Conclusions: The aging factors and restorative material do not interfere with the surface roughness performance. However, the mechanical performance and number of fragments after fracture is affected by the restorative material.
RESUMO Objetivos: Objetivou-se avaliar a longevidade de materiais restauradores cerâmicos na confecção de restaurações endocrowns, através de um estudo in vitro sobre rugosidade superficial e resistência mecânica. Métodos: Três materiais restauradores foram avaliados e distribuídos em grupos experimentais (n=10 espécimes em disco): Cerâmica Reforçada por Leucita, Dissilicato de Lítio e Resina Nanocerâmica. Estes materiais restauradores foram avaliados quanto a superfície antes e após ao envelhecimento (N=2 espécimes) em estereomicroscópio. Os espécimes foram submetidos ao ensaio de rugosidade superficial média (Ra) (N=10) em rugosímetro de contato antes e após o envelhecimento. Como também, ao teste de resistência à flexão biaxial (N=10), após envelhecimento, em uma velocidade de ensaio de 0,5 mm/min. O envelhecimento foi realizado uma termocicladora, sendo 5.000 ciclos com banhos de 5 °C ± 1° e 55 °C ± 1°. Os fragmentos após fratura foram observados em estereomicroscópio. Os dados obtidos foram tabulados e analisados no programa estatístico Minitab. Resultados: As superfícies dos espécimes não mostram alterações entre os materiais restauradores e também em relação ao envelhecimento. Para os dados de rugosidade, os fatores materiais restauradores (p=0,867) e envelhecimento (p=0,321) não foram estatisticamente significativos. O grupo DIS apresentou os maiores valores de resistência à fratura (p=0,000), em relação aos grupos LEU e REN que foram estatisticamente semelhantes. O mesmo padrão estatístico foi identificado para os dados de fragmentos após a fratura (p=0,030). Conclusão: Os fatores envelhecimento e material restaurador não interferem quanto a performance da rugosidade superficial. No entanto, o desempenho mecânico e número de fragmentos após a fratura é afetado pelo material restaurador.
Résumé
Digital dentistry has gained space in several dental specialties. It is possible to achieve excellent results with the digital workflow, which combines the efficiency of the restorative material with a greater marginal adaptation. This study aimed to report a clinical case through the digital workflow, with a faster and clinically acceptable prosthetic resolution. In this clinical case report, digital workflow allowed a faster and clinically acceptable prosthetic resolution. A 45-year-old female patient reported cementation failure of the prosthetic crown on tooth 14. As it was a vital tooth, the tooth received a total crown preparation. In the same clinical session, the patient's mouth was scanned then a capture software obtained a virtual model. After, the design software planned a digital "diagnostic wax-up", so a leucitic ceramic was chosen for the rehabilitation. The ceramic block was milled and receive stain and glaze, dispensing the prosthesis laboratory. Then, the adhesive cementation was performed with a dual-polymerized resin cement. The final crown had ideal adaptation, with no need for interproximal and occlusal adjustments, with an excellent marginal fit. Within the limitations of this study, this case report showed that the digital workflow allowed a favorable result in a shorter working time, which brought back function and aesthetics, without the need for interproximal and occlusal adjustments. (AU)
A odontologia digital vem ganhando espaço em diversas especialidades odontológicas. Com o fluxo de trabalho digital, é possível alcançar excelentes resultados na reabilitação protética, combinando a eficiência do material restaurador com a adaptação marginal proporcionada pela odontologia digital. O objetivo desse estudo foi relatar um caso clínico através do fluxo de trabalho digital, com uma resolução protética mais rápida e clinicamente aceitável. Paciente do sexo feminino, 45 anos, relatou falha de cimentação da coroa protética do dente 26. Por ser um dente vital, o dente recebeu um preparo de coroa total e os dentes foram escaneados e um software de captura obteve um modelo virtual. Posteriormente, o software de projeto planejou um "enceramento diagnóstico" digital, sendo escolhida uma cerâmica leucítica para a reabilitação. O bloco cerâmico foi fresado e recebeu acabamento, maquiagem e glaze pelo próprio dentista, dispensando um técnico laboratorial de prótese dentária. Em seguida, foi realizada cimentação adesiva definitiva. Este relato de caso mostra que, dentro das limitações desse estudo, o fluxo digital permite um resultado favorável em um menor tempo de trabalho, devolvendo a função e estética, sem necessidade de ajustes interproximais e oclusais (AU)
Sujets)
Humains , Femelle , Adulte , Prothèses dentaires , Conception assistée par ordinateur , Dentisterie esthétiqueRésumé
O padrão oclusal pode ser considerado um fator crítico para a longevidade dos componentes do sistema estomatognático como também das reabilitações implantossuportadas. Objetivo: revisar a literatura em relação ao padrão de oclusão mais adequado para reabilitar um paciente edêntulo com prótese Protocolo de Brånemark. Revisão de literatura: nesta revisão, os artigos de estudos clínicos retrospectivos (2 artigos) e in silico (2 artigos) foram incluídos. Considerações finais: padrões de oclusão em prótese Protocolo de Brånemark são um tema muito escasso na literatura; o uso de uma oclusão mutuamente protegida com guia lateral em canino favorece a distribuição da tensão sobre os implantes e o osso alveolar; no entanto, a condição do arco antagonista pode influenciar esta escolha. (AU)
The occlusal pattern can be considered a critical factor for the longevity of the components of the stomatognathic system, as well as of the implantsupported rehabilitations. Objective: to review the literature regarding the most appropriate standard of occlusion to rehabilitate a patient edentulous with Brånemark Protocol prothesis. Literature review: in this review, articles from retrospective clinical studies (02 articles) and in silico studies (02 articles) were included. Final considerations: this literature review shows that standard of occlusion in the Brånemark Protocol prosthesis ns are a very scarce subject in the literature, the use of a mutually protected lateral guiding in canine favors the stress distribution on the implants and alveolar bone, however the condition of the arc antagonist may influence this choice. (AU)
Sujets)
Humains , Pose d'implant dentaire endo-osseux/méthodes , Occlusion dentaire , Prothèse dentaire complète , Conception de prothèse dentaire/méthodes , Rééducation buccale/méthodesRésumé
Objetivo: o tratamento de pacientes desdentados com reabsorção alveolar severa é uma temática desafiadora na reabilitação protética. Identificada por Kelly em 1972, a síndrome da combinação é uma manifestação intraoral encontrada em pacientes totalmente desdentados na arcada superior, em oposição a uma prótese mandibular de extensão distal bilateral. Relato de caso: este estudo revisa e discute, por meio de um caso clínico, as características clínicas presentes em um paciente com manifestações da síndrome da combinação. Além disso, apresenta uma proposta de tratamento reabilita¬dor, restabelecendo a função fonética e a estética do paciente. Considerações finais: diagnosticar a síndrome e estabelecer um plano de tratamento adequado às necessidades do paciente, criando condições clínicas para o restabelecimento da saúde, são imprescindíveis para obter resultado e, assim, impedir o avanço do quadro clínico. (AU)
Objective: treatment of patients with reactivity with respiratory problems. Identified by Kelly in 1972, a combination syndrome and an intraoral manifestation found in fully edentulous patients in the upper arch as opposed to a mandibular prosthesis of bilateral distal extension. Case report: the present study reviews and discusses, through a clinical case, as clinical features present in a patient with manifestations of the combination syndrome, in addition, to present a proposal of rehabilitative treatment, restoring function, phonetics and esthetics to the patient. Final considerations: diagnosing a syndrome and establishing a treatment plan appropriate to the needs of the patient and creating clinical conditions for the reestablishment of health are essential to obtain the result and thus impeding the advancement of the clinical picture. (AU)
Sujets)
Humains , Mâle , Adulte d'âge moyen , Mâchoire édentée/thérapie , Mâchoire partiellement édentée/thérapie , Conception de prothèse dentaire/méthodes , Rééducation buccale/méthodes , Syndrome , Résorption alvéolaire/thérapie , Résultat thérapeutiqueRésumé
Objective: the objective of the present study was to analyzethe polymerization shrinkage gap of different compositeresins. Methods: four commercial brands (n=5)were tested: Z350 (3M/ESPE); Filtek Bulk Fill (3M/ESPE);Surefill (Dentsply); Xtra Base (Voco). Increments of compositeresins were inserted into a circular metal matrixof 7 mm internal diameter and 4 mm high and pressedby two glass plates supported on polyester strips. Afterphotoactivation with a Optilight Plus device (Gnatus),with light intensity of 1000 ± 10mW/cm2, the test sampleswere polished and 24h later, taken to the scanningelectron microscope for analysis of the polymerizationshrinkage gap, measured at 4 points in the sample (3, 6,9, and 12 o'clock). The data were analyzed by analysisof variance (Anova one-way). Results: the highest meanof polymerization shrinkage gap was observed for FiltekZ350 (3M/ESPE), while the lowest mean of gap wasfound for Xtra Base (Voco) brand, with significant differencesbetween the groups. Conclusion: the inorganicfiller content and different associations in the organicmatrices interfered expressively in the polymerizationshrinkage gap.