RÉSUMÉ
BACKGROUND:Adjustable piezoelectric effect can promote tissue regeneration and repair.Piezoelectric materials are widely used in weight-bearing tissue engineering. OBJECTIVE:To prepare a piezoelectric film material that can promote bone regeneration,and to explore its structural characterization,electrical output performance,biocompatibility,and effect of electrical output on osteogenic differentiation of rabbit bone marrow mesenchymal stem cells. METHODS:Using poly-3-hydroxybutyrateco/4-hydroxybutyrate(P34HB)as raw material,barium calcium stannate titanate powder(Ba0.94Ca0.06Sn0.08Ti0.92O3,BCST)was added according to mass ratios of 0%,5%,10%,15%,and 20%.Dichloromethane was added to solve P34HB,and the thickness of 150-200 μm BCST/P34HB piezoelectric film was prepared by vacuum drying method.After polarization in the oil bath,the surface morphology,crystal phase composition,piezoelectric coefficient and open circuit voltage were tested.The effect of BCST/P34HB electrical output at 110 Hz and 0.25 N force on the proliferation and osteogenic differentiation of rabbit bone marrow mesenchymal stem cells was tested. RESULTS AND CONCLUSION:(1)Scanning electron microscopy,X-ray diffraction,water contact angle,piezoelectric coefficient and electrical output performance tests showed that when the mass ratio of BCST increased to 20%,the BCST/P34HB piezoelectric film had good piezoelectric properties(d33=5.9 pC/N)and electrical output performance(180 mV),which was closer to the suitable range of 500 mV for electrical stimulation.(2)Live and dead staining showed that on the first day of co-culture,15%group and 20%group showed less red fluorescence.On the 5th day of culture,the number of green fluorescence in each group was significantly higher than that on the first day,and the red fluorescence was not observed in the 10%,15%and 20%groups,and only a small amount of red fluorescence was observed in the 0%and 5%groups.(3)On the 1st,3rd and 5th days of co-culture with rabbit bone marrow mesenchymal stem cells,Almar blue staining exhibited that the number of cells in each group showed an increasing trend with the increase of time.On the 5th day of culture,the number of cells in the 20%group was significantly more than that in the 0%group(P<0.05).(4)On day 10 of osteogenic induction,alkaline phosphatase staining results showed that the positive rate of the 20%group was significantly higher than that of the 0%group(P=0.000 1).On day 21,alizarin red staining and quantitative analysis of calcium nodules showed a similar trend to alkaline phosphatase staining.Compared with the 0%group,the 15%group and 20%group showed significant differences(P<0.01,P<0.000 1).(5)The results showed that 20%BCST/P34HB films had good piezoelectric properties,electrical output properties,biocompatibility and the ability of promoting osteogenic differentiation of bone marrow mesenchymal stem cells.
RÉSUMÉ
BACKGROUND:Bone is a remarkable natural material possessing piezoelectric properties.By harnessing the biomimetic piezoelectric effect,tissue engineering materials can be employed to effectively address bone tissue defects and facilitate their repair. OBJECTIVE:Using a solid-phase force chemistry technique,a piezoelectric scaffold with inherent osteogenic properties was meticulously fabricated.This unique scaffold was then assessed for its impact on osteoblast adhesion,proliferation,and osteogenic differentiation. METHODS:Polyvinylidene fluoride(PVDF)powders,along with commercially available NaCl(mass ratios are 60:40,50:50,40:60,and 30:70,respectively),were subjected to solid-phase shear milling technology,resulting in a homogenous mixture.Through a melting process,a substantial material was formed,and subsequent treatment with a pure water solution effectively eliminated the NaCl.Consequently,PVDF piezoelectric foam scaffolds with varying pore sizes were successfully prepared.These materials were categorized as PVDF-40,PVDF-50,PVDF-60,and PVDF-70,denoting the respective mass percentages of NaCl during preparation.The surface morphology,crystal phase composition,thermodynamic behavior,mechanical properties,and piezoelectric properties of each group were meticulously characterized.The four kinds of piezoelectric foam scaffolds were co-cultured with the MG63 osteoblast cell line to evaluate its biocompatibility and potential to promote bone differentiation. RESULTS AND CONCLUSION:(1)The scanning electron microscopy,four groups of scaffolds had multi-level pores.As the NaCl mass fraction in the mixed powder increased,the porosity of the scaffolds increased.X-ray energy dispersion spectrum,X-ray diffraction,Fourier transform infrared spectroscopy,and thermogravimetric analysis collectively revealed the scaffold predominantly comprised the α phase,which inherently lacked piezoelectric properties.However,the application of solid-phase force chemistry successfully stimulated the formation of the β phase,thereby enhancing the scaffold's piezoelectric properties.Notably,the PVDF-60 group exhibited the highest proportion of the β phase among all the tested groups.The results of cyclic compression testing and piezoelectric performance assessment demonstrated that the PVDF-60 group exhibited superior compressive strength and piezoelectric performance compared to the other groups.(2)The findings from scanning electron microscopy and laser confocal microscopy exhibited that MG63 cells adhered well to the surface of the four groups of scaffolds,with good morphology,extended more pseudopods,and secreted a large amount of extracellular matrix.CCK-8 assay revealed that the proliferative absorbance of PVDF-60 cells cultured for 4 days was higher than that of the other three groups(P<0.000 1).Alkaline phosphatase staining and alizarin red staining showed that the expression of alkaline phosphatase and the number of calcified nodules in the PVDF-60 group were higher than those in the other three groups(P<0.01,P<0.000 1).(3)The piezoelectric PVDF foam-based scaffolds demonstrated favorable cytocompatibility.Notably,the PVDF-60 group showed superior mechanical properties,piezoelectric performance,and bone-inducing capabilities.