Résumé
Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer's instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used
Sujets)
Titane , Agents de collage dentinaire , Perméabilité de la dentine , FluoruresRésumé
Objetivo: O objetivo desse estudo foi investigar a permeabilidade dentinária e a oclusão tubular de materiais dessensibilizantes de uso em consultório. Métodos: Blocos de dentina bovina foram obtidos e imersos em EDTA 0,5 M para promover a abertura dos túbulos dentinários. Os materiais testados foram: verniz placebo (PLA); verniz fluoretado (FLU); verniz de NaF 5% + 5% trimetafosfato de sódio nanoparticulado (TMP); sistema adesivo universal (SBU); verniz contendo partículas S-PRG (SPRG); solução de Biosilicato (BIOS) e solução de amelotina (AMTN). Os materiais foram aplicados e os espécimes submetidos ao desafio erosivo-abrasivo. A permeabilidade dentinária foi avaliada em T0 (inicial), T1 (após a aplicação dos materiais) e T2 (após o desafio erosivo-abrasivo). As imagens confocais foram usadas para avaliar o comprimento e o número dos túbulos ocluídos e as imagens de microscopia eletrônica de varredura (MEV) para avaliar o número de tubulos abertos. Os dados de permeabilidade e MEV foram analisadas pelo teste ANOVA duas medidas repetidas e pós teste de Tukey. O comprimento e número de túbulos dentinários ocluídos foram analisadas pelo teste ANOVA um critério e pós teste de Tukey, Kruskal-Wallis e pós teste de Dunn's, respectivamente. Os testes de correlação de Spearman e Pearson também foram realizados. O nível de significância foi de 5%. Resultados: O grupo AMTN mostrou os menores valores de permeabilidade em T1 e a seguinte ordem decrescente ocorreu em T2: AMTN=SBU>BIOS=SPRG>TMP>FLU>PLA. O grupo SBU teve o maior comprimento médio de túbulos dentinários ocluídos. O grupo AMTN teve maior número de túbulos dentinários ocluídos do que PLA e FLU e os menores valores de túbulos dentinários abertos foram observados para os grupos AMTN e SBU. Uma correlação significativa foi encontrada entre as análises realizadas. Significância: O sistema adesivo universal e a proteína amelotina foram mais efetivos em reduzir a permeabilidade dentinária através da oclusão dos túbulos dentinários(AU)
Objectives: The aim of this study was to investigate the dentin permeability and tubule occlusion of in-office desensitizing materials. Methods: Bovine dentin blocks were obtained and immersed in 0.5 M EDTA to open dentinal tubules. The materials tested were: placebo varnish (PLA); fluoride varnish (FLU); NaF 5% + 5% nanoparticulate sodium trimetaphosphate varnish (TMP); universal adhesive system (SBU); S-PRG filler-containing varnish (SPRG); Biosilicate solution (BIOS) and amelotin solution (AMTN). The materials were applied, and specimens were submitted to an erosive-abrasive challenge. Dentin permeability was evaluated at T0 (initial), T1 (after application of materials) and T2 (after erosive-abrasive challenge). Confocal images were used to evaluate length and number of dentinal tubules occluded and images from scanning electron microscopy (SEM) to evaluate opened dentinal tubules. Permeability and SEM data were evaluated by two-way repeated measures ANOVA and Tukey tests. The length and number of dentinal tubules occluded were evaluated by one-way ANOVA and Tukey, Kruskal-Wallis and Dunn's tests, respectively. Spearman and Pearson correlation tests were also used. The significance level was 5%. Results: AMTN group showed the lowest permeability value in T1 and the following decreasing order occurred in T2: AMTN=SBU>BIOS=SPRG>TMP>FLU>PLA. SBU group had the highest mean value of dentinal tubules occluded lengths. AMTN group had greater number of dentinal tubules occluded than PLA and FLU and the lowest values of opened dentin tubules were observed for AMTN and SBU groups. A significant negative correlation was found between the analysis. Significance: Universal adhesive system and the AMTN solution were more effective to reduce dentin permeability by occluding dentin tubules(AU)
Sujets)
Perméabilité de la dentine , Agents désensibilisants dentinaires , Phosphates , Fluorures topiques , Isolation de cavité dentaire , Dentine , Hypersensibilité dentinaireRésumé
Abstract Objective To evaluate the efficacy of Nd:YAG laser associated with calcium-phosphate desensitizing pastes on dentin permeability and tubule occlusion after erosive/abrasive challenges. Methodology Dentin specimens were exposed to 17% ethylene diamine tetra-acetic acid (EDTA) solution for 5 min and randomly allocated into five groups: G1, control (no treatment); G2, Nd:YAG laser (1 W, 10 Hz, 100 mJ, 85 J/cm2); G3, Laser + TeethmateTM Desensitizer; G4, Laser + Desensibilize Nano P; and G5, Laser+Nupro®. Specimens underwent a 5-day erosion-abrasion cycling. Hydraulic conductance was measured post-EDTA, post-treatment, and post-cycling. Post-treatment and post-cycling permeability (%Lp) was calculated based on post-EDTA measurements, considered 100%. Open dentin tubules (ODT) were calculated at the abovementioned experimental moments using scanning electron microscopy and ImageJ software (n=10). Data were analyzed using two-way repeated measures ANOVA and Tukey's test (α=0.05). Results G1 presented the highest %Lp post-treatment of all groups (p<0.05), without significantly differences among them. At post-cycling, %Lp significantly decreased in G1, showed no significant differences from post-treatment in G3 and G4, and increased in G2 and G5, without significant differences from G1 (p>0.05). We found no significant differences in ODT among groups (p>0.05) post-EDTA. At post-treatment, treated groups did not differ from each other, but presented lower ODT than G1 (p<0.001). As for post-cycling, we verified no differences among groups (p>0.05), although ODT was significantly lower for all groups when compared to post-EDTA values (p<0.001). Conclusion All treatments effectively reduced dentin permeability and promoted tubule occlusion after application. Combining Nd YAG laser with calcium-phosphate pastes did not improve the laser effect. After erosive-abrasive challenges, treatments presented no differences when compared to the control.
Sujets)
Lasers à solide/usage thérapeutique , Agents désensibilisants dentinaires , Microscopie électronique à balayage , Calcium/pharmacologie , Dentine , Perméabilité de la dentineRésumé
O objetivo deste estudo foi avaliar a rugosidade, a obliteração dos túbulos dentinários e a permeabilidade da dentina erodida e escovada com diferentes dentifrícios. Noventa dentes bovinos foram seccionadas em blocos, sendo que em trinta a hemiface foi protegida com verniz ácido resistente e sessenta foram submetidos ao teste de permeabilidade. Os espécimes foram divididos de acordo com os dentifrícios: sem flúor (SF), com fluoreto de sódio (NaF) e com fluoreto de estanho (SnF2). Em seguida, os blocos foram submetidos a um protocolo erosivo-abrasivo por 5 dias. As análises de rugosidade superficial e obliteração dos túbulos dentinários (n=10) foram realizadas nas hemifaces controle e teste do mesmo espécime e a análise da permeabilidade (n=20) foi realizada novamente. Os dados foram submetidos aos testes de ANOVA a dois critérios medidas repetidas e pós teste de Tukey (p≤0,05). Os grupos NaF e SnF2 apresentaram maior rugosidade comparando-se ao SF. O grupo SF apresentou a maior quantidade de túbulos abertos quanto comparado aos demais. Não houve diferença significativa na permeabilidade pós-ciclagem entre os dentifrícios SF e NaF, contudo o dentifrício SnF2 apresentou maior permeabilidade comparando-se aos demais. Ambos os dentifrícios contendo flúor tiveram oclusão efetiva dos túbulos dentinários; contudo, os efeitos da presença de fluoreto de estanho na permeabilidade podem ser neutralizados pela abrasão deste dentifrício(AU)
The aim of this study was to evaluate the roughness, dentin tubule occlusion and permeability of eroded dentin brushed with different toothpastes. Ninety bovine teeth were sectioned in blocks. The hemiface of thirty specimens was protect with acid resistant varnish and sixty were submitted to permeability test. The specimens were divided according to the dentifrices: without fluoride (WF), sodium fluoride (NaF) and stannous fluoride (SnF2). Then, the blocks were submitted to erosive-abrasive protocol for 5 days. The analysis of surface roughness and dentin tubule occlusion (n=10) were performed on control and test hemifaces of the same sample and permeability analysis (n=20) was again performed. Data were analyzed by two-way RM ANOVA and Tukey tests (p≤0.05). NaF and SnF2 groups presented higher roughness when compared with WF. WF group presented larger number of opened tubules compared to the others. No significant differences were found between WF and NaF for permeability; however, SnF2 presented higher hydraulic conductance compared to other dentifrices. In conclusion, both fluoride-containing toothpastes had promising tubule occlusion; however, the effects on permeability of stannous formulation may be counteracted by the effects of abrasion from this dentifrice(AU)
Sujets)
Abrasion dentaire , Érosion dentaire , Dentifrices , Perméabilité de la dentine , Agents désensibilisants dentinaires , Fluorure de sodium , Fluorures d'étain , Pâtes dentifrices , Dentine , FluoruresRésumé
RESUMEN Introducción: La permeabilidad dentinaria es conocida como el paso de fluidos, iones, partículas, moléculas y bacterias a través de la dentina bajo ciertas condiciones. Objetivo: Determinar la influencia de la aplicación activa con un aplicador mejorado de un adhesivo dentinario sobre la conductancia hidráulica dentinaria humana, in vitro. Métodos: Estudio experimental in vitro en 40 terceros molares libres de caries, con indicación de exodoncia, provenientes de pacientes sanos entre 15 y 30 años, previo consentimiento informado. Posteriormente se limpiaron, desinfectaron y conservaron para ser incluidos en bloques de resina epóxica. Luego se realizaron cortes transversales y se obtuvieron discos dentinarios de 1,5 mm de espesor y 25 mm de diámetro. Se dividieron en dos grupos de 20 unidades cada uno, se sometieron a grabado con ácido ortofosfórico al 37 por ciento, y se lavaron y secaron. Sobre una balanza de precisión se les aplicó adhesivo dentinario fotopolimerizable, registrando la fuerza ejercida. En el grupo 1 se usó un microbrush en la aplicación y en el grupo 2 un aplicador mejorado diseñado especialmente. Posteriormente cada muestra fue sometida a una cámara de difusión para obtener la tasa de flujo y luego calcular la conductancia hidráulica, la cual otorga información acerca de la permeabilidad de la dentina. Resultados: los resultados obtenidos fueron levemente menores en el grupo 2, sin embargo, experimentaron una distribución normal. Conclusiones: no existen diferencias significativas, al ser analizados estadísticamente bajo diversas pruebas, en los valores de conductancia hidráulica. Tampoco se pudo establecer una relación inversa entre la fuerza de aplicación de un adhesivo en forma activa con un aplicador mejorado y la conductancia hidráulica, por lo cual no se aconseja el uso de dicho instrumento(AU)
ABSTRACT Introduction: Dentin permeability is defined as the passage of fluids, ions, particles, molecules and bacteria through the dentin under certain conditions. Objective: Determine the effect of the active application of a dentin adhesive with an improved applicator on human dentin hydraulic conductance in vitro. Methods: An in vitro experimental study was conducted of 40 caries-free third molars with an indication of exodontia from healthy patients aged 15-30 years, prior informed consent. The molars were cleaned, disinfected and preserved to be included in epoxy resin blocks. Cross-sectional cuts were then made to obtain dentin discs 1.5 mm thick and 25 mm in diameter. These were divided into two 20-unit groups, were subjected to etching with 37 percent orthophosphoric acid, and were washed and dried. On a precision scale photopolymerizable dentin adhesive was applied, recording the force exerted. Application was performed with a Microbrush applicator in Group 1 and with an improved dedicated applicator in Group 2. The samples were then placed in a diffusion chamber to determine flow rate and subsequently estimate hydraulic conductance, thus obtaining information about dentin permeability. Results: Results were slightly lower in Group 2, but they displayed normal distribution. Conclusions: Statistical analysis with various tests did not find any significant differences in hydraulic conductance values, nor could an inverse relation be established between the force of active application of an adhesive with an improved applicator and hydraulic conductance. Therefore, use of that instrument is not advised(AU)
Sujets)
Humains , Collage dentaire/méthodes , Perméabilité de la dentine/physiologieRésumé
Abstract To synthesize Nano eggshell-titanium-dioxide (EB@TiO2) biocomposite and to evaluate its effectiveness in occluding opened dentine tubules. EB@TiO2 was synthesized and characterized using X-ray diffraction (XRD), and Transmission Electron Microscope (TEM). Sixteen simulated bovine dentine discs were prepared and randomly assigned into four groups according to the following treatment (n = 4): Group 1: No treatment; Group 2: eggshell powder; Group 3: EB@TiO2; Group 4: Sensodyne. These were then agitated in a solution of 1g powder and 40mL water for 3hours. Thereafter, each dentine discs from the respective groups were post-treated for 5 min with 2wt% citric acid to test their acid resistant characteristics. Scanning Electron Microscope (SEM) was used to observe the effectiveness of occluded dentine pre-and post-treatment. The cytotoxicity of the synthesized EB@TiO2 was tested using NIH 3T3 assay. ANOVA was used to evaluate the mean values of the occluded area ratio and the data of MTS assay. This was followed by a multi-comparison test with Bonferroni correction (α = .05). The XRD confirmed that EB@TiO2 was successfully modified through ball-milling. The TEM revealed the presence of both spherical and irregular particle shape powders. The SEM result showed that EB@TiO2 could effectively occlude open dentine tubules. Equally, the result demonstrated that EB@TiO2 exhibited the highest acid resistant stability post-treatment. NIH 3T3 assay identified that EB@TiO2 had little effect on the NIH 3T3 cell line even at the highest concentration of 100µg/ml. This study suggests that the application of EB@TiO2 effectively occluded dentine tubules and the occlusion showed a high acid resistant stability.
Sujets)
Animaux , Bovins , Souris , Phosphates/pharmacologie , Titane/composition chimique , Perméabilité de la dentine/effets des médicaments et des substances chimiques , Hypersensibilité dentinaire/thérapie , Coquille de l'oeuf/composition chimique , Nanocomposites/composition chimique , Agents désensibilisants dentinaires/pharmacologie , Fluorures/pharmacologie , Nitrates/pharmacologie , Titane/analyse , Titane/pharmacologie , Reminéralisation des dents , Microscopie électronique à balayage , Cellules NIH 3T3 , Association médicamenteuse , Coquille de l'oeuf/ultrastructure , Nanocomposites/analyse , Nanocomposites/usage thérapeutiqueRésumé
Objetivo: Determinar el grado de confiabilidad de un modelo de dentina humana para evaluar la calidad de oclusión de los túbulos dentinarios luego del uso de dos agentes desestabilizantes que contienen oxalato de potasio. Materiales y métodos: Se obtuvieron dos secciones horizontales en forma de discos de dentina de 0,8 mm de espesor de cada uno de 21 terceros molares sanos extraídos por razones periodontales, ortodóncicas o quirúrgicas. El barro dentinario de las superficies coronaria y pulpar de los discos se eliminó con ácido fosfórico al 35% y posterior lavado con suero fisiológico y secado. De cada molar se separó un disco para el grupo 1 (n=20). Los segundos discos de cada molar se destinaron al grupo 2 (n=20). Y los dos discos del molar restante no recibieron tratamiento (controles negativos). El ensayo se realizó en dos etapas. En la primera, las superficies coronarias de los discos del grupo 1 se trataron con Klepp Desensitizer, mientras que en el grupo 2 se empleó BisBlock Desensitizer. Posteriormente, se metalizaron con oro-paladio y se observaron en un microscopio electrónico de barrido. En la segunda etapa, los discos se retiraron del microscopio, se invirtieron de posición, y la superficie pulpal ubicada en posición superior se lavó con suero, se secó, se metalizó y se observó nuevamente con el microscopio. Con el objeto de realizar el análisis químico de los agentes desestabilizantes, se obtuvieron otros dos discos a partir de un molar adicional y se prepararon ambos siguiendo el mismo protocolo que en los discos experimentales. Uno de ellos se trató con Klepp Desensitizer, y el otro, con BisBlock Desensitizer. Finalmente, las superficies pulpares de ambos discos adicionales se metalizaron con carbón y se examinaron mediante un análisis de energía dispersiva de rayos X. Resultados: En la primera etapa del ensayo, la superficie coronaria de los 20 discos de cada grupo se encontraba cubierta por una capa uniforme de cristales precipitados a partir de ambos agentes desestabilizantes. En la segunda etapa, la superficie pulpar de los 20 discos del grupo 1 reveló que todos los túbulos dentinarios estaban totalmente ocluidos por los cristales en nueve (n=9) casos. Lo mismo ocurrió en ocho (n=8) discos del grupo 2. En ambos casos los cristales ocluyeron totalmente los túbulos hasta una profundidad de 0,8 mm. En 11 (n=11) y 12 (n=12) discos de los grupos 1 y 2 respectivamente se observaron túbulos parcialmente ocluidos o bien una combinación de estos con túbulos vacíos. Las diferencias entre grupos no fueron significativas (P>0,05). En los controles negativos todos los túbulos se encontraban vacíos. El análisis de energía dispersiva de rayos X reveló que los cristales precipitados a partir de ambos agentes desestabilizantes dentro de los túbulos contenían importantes concentraciones de calcio y trazas de potasio. Conclusiones: El modelo ensayado parecería ser adecuado para comparar ex vivo la calidad de protección de la superficie dentinaria producida por los agentes desestabilizantes a base de oxalato de potasio (AU)
Sujets)
Humains , Hypersensibilité dentinaire , Oxalates , Composés du potassium , Pulpe dentaire , Perméabilité de la dentine , Microscopie électronique à balayage , Interprétation statistique de donnéesRésumé
Introdução: com a necessidade de terapêuticas antimicrobianas complementares, a terapia fotodinâmica (PDT) vem mostrando resultados promissores na inativação de microrganismos no interior dos canais radiculares. Objetivo: o objetivo deste trabalho foi analisar a capacidade de penetração do fotossensibilizante azul de metileno na massa dentinária nos níveis cervical, médio e apical dos canais radiculares de dentes humanos, comparando diferentes aplicações da solução. Métodos: a amostra foi composta de 20 dentes pré-molares unirradiculares, distribuídos em quatro grupos, preparados utilizando-se instrumentos rotatórios de NiTi e irrigação com HCT20. Cada grupo recebeu suas respectivas aplicações do fotossensibilizante, sendo de 5 minutos o tempo de ação da solução dentro do canal: Grupo 1 = azul de metileno a 2%; Grupo 2 = azul de metileno a 2% associado ao detergente lauril-sulfato de sódio a 0,125%; Grupo 3 = azul de metileno a 2% com agitação sônica; Grupo 4 = azul de metileno a 2% associado ao detergente lauril-sulfato de sódio a 0,125% com agitação sônica. Os dentes foram, então, seccionados transversalmente nos níveis cervical, médio e apical e observados em microscópio cirúrgico. Resultados: os resultados foram analisados estatisticamente pela aplicação do teste ANOVA, teste de Levene e teste de Tukey (p < 0,05). O valor médio da penetração no nível cervical variou de 0,55 a 0,75mm; no nível médio, variou de 0,30 a 0,48mm; e no nível apical, variou de 0,17 a 0,24mm entre os grupos. Conclusões: independentemente da natureza do solvente e do uso ou não da agitação sônica, nas condições testadas não houve diferenças estatisticamente significativas entre os grupos.
Sujets)
Humains , Percolation dentaire , Perméabilité de la dentine , Endodontie , Bleu de méthylène , Photothérapie dynamique/statistiques et données numériques , Liquides d'irrigation endocanalaireRésumé
Abstract Objective The aim of this in vitro study was to investigate the effect of two desensitizing agents and water on hydraulic conductance in human dentin. Material and Methods GLUMA Desensitizer PowerGel (GLU) contains glutaraldehyde (GA) and 2-hydroxyethyl methacrylate (HEMA), and Teethmate Desensitizer (TD) is a powder comprising tetracalcium phosphate (TTCP) and dicalcium phosphate anhydrous (DCPA) that is mixed with water. Deionized water was used as a negative control (CTR). Thirty discs with a thickness of 1.2 mm were cut from the coronal dentin of the third molars and cleaned with 0.5 M EDTA (pH 7.4). After being mounted in a split-chamber device, the discs were pressurized with water at 1 kPa and 3 kPa in order to measure flow rates with a highly sensitive micro-flow sensor and to calculate hydraulic conductance as a baseline value (BL). Following the application of GLU, TD, and CTR (n=10), hydraulic conductance was remeasured with intermittent storage in water after 15 min, 1 d, 1 w, and 1 m. Reduction in permeability (PR%) was calculated from hydraulic conductance. Data were statistically analyzed using nonparametric methods (α<0.05). Representative discs were inspected by SEM. Results PR% for GLU and TD were 30-50% 15 min and 1 m after their application. Post hoc tests indicated that PR% of CTR was significantly greater than those of GLU and TD at all time points tested. The PR% of GLU and TD were not significantly different. SEM examinations showed noncollapsed collagen meshes at the tubular entrances after GLU, and crystalline precipitates occluding the tubular orifices after TD, whereas CTR specimens showed typical patterns of etched dentin. Conclusions The present study on hydraulic conductance in dentin discs treated with two chemically different desensitizing agents and water as a control demonstrated that both products may be characterized as effective.
Sujets)
Humains , Phosphates de calcium/composition chimique , Glutaraldéhyde/composition chimique , Dentine/effets des médicaments et des substances chimiques , Perméabilité de la dentine/effets des médicaments et des substances chimiques , Agents désensibilisants dentinaires/composition chimique , Méthacrylates/composition chimique , Propriétés de surface , Facteurs temps , Test de matériaux , Eau/composition chimique , Microscopie électronique à balayage , Répartition aléatoire , Acide édétique/composition chimique , Statistique non paramétriqueRésumé
Objetivo: avaliar in vitro a efetividade de aplicações sucessivas de diferentes produtos utilizados para o tratamento da hipersensibilidade dentinária cervical na redução da permeabilidade dentinária, assim como avaliar a resistência destes produtos a desafios ácidos. Material e métodos: foram utilizados 72 terceiros molares humanos íntegros para a preparação de 72 amostras, que foram ligadas a um sistema de pressão hidráulica para mensurar a permeabilidade dentinária após os seguintes passos: 1) preparação da amostra; 2) tratamento com ácido fosfórico a 37% durante 30 segundos; 3) cinco aplicações dos produtos testados; 4) primeiro desafio ácido; 5) segundo desafio ácido; e 6) terceiro desafio ácido. As amostras foram divididas aleatoriamente em seis grupos (n=12), de acordo com os tratamentos propostos: Desensibilize Nano P, Clinpro XT, dentifrício Colgate Sensitive Pró-Alívio, dentifrício Duraphat, dentifrício Sensodyne Repair e após restauração com resina composta (grupo-controle). Conclusão: que todos os produtos testados foram capazes de promover a redução da permeabilidade dentinária significativamente, sendo que os grupos Clinpro XT, Desensibilize Nano P e controle mantiveram esses níveis reduzidos estatisticamente até o terceiro desafio ácido, enquanto que os dentifrícios Duraphat, Sensodyne Repair e Colgate Sensitive Pró-Alívio mantiveram essas reduções estatisticamente significativas até o segundo desafio ácido.
Objective: to evaluate in vitro the effectiveness of successive applications of different products used for the treatment of cervical dentinal hypersensitivity, reducing dentin permeability, as well as to evaluate the resistance of these products, acids challenges. Material and methods: 72 intact human third molars were used for the preparation of 72 samples were bound to a hydraulic pressure system to measure the dentin after the following steps: 1) sample preparation; 2) treatment with 37% phosphoric acid for 30 seconds; 3) 5 applications of the products tested; 4) first challenge acid; 5) second challenge acid; 6) third challenge acid. The samples were randomly divided into 6 groups (n=12) according to the proposed treatments: Desensibilize Nano P, Clinpro XT, toothpaste Colgate Sensitive Pro-Relief, Duraphat toothpaste, toothpaste Sensodyne Repair and after restoration with composite resin (control group). Conclusion: all products tested were able to significantly promote the reduction of dentin, and the Clinpro XT groups Desensibilize Nano P and control these reduced levels remained statistically to the third challenge acid, while toothpaste Duraphat, Sensodyne Repair and Colgate Sensitive Pro-Relief kept these statistically significant reductions to the second challenge acid.
Sujets)
Humains , Dentine , Perméabilité de la dentine/effets des médicaments et des substances chimiques , Hypersensibilité dentinaire/traitement médicamenteux , Préparations pharmaceutiques en odontologie/administration et posologieRésumé
The aim of this ex vivo study was to evaluate changes in pH andcalcium ion diffusion through root dentin from calcium hydroxide(Ca (OH)2) and mineral trioxide aggregate (MTA) pastes at 7,30 and 60 days; and the relationship between pH and iondiffusion. Thirtytwo human premolars were used. Crowns weresectioned and root canals instrumented and filled in with thefollowing preparations: 1) Ca(OH)2 + distilled water (n=7); 2)Ca(OH)2 + 0.1% chlorhexidine gluconate (n=7); 3) MTA +distilled water (n=7); 4) MTA + 0.1% chlorhexidine gluconate(CHX) (n=7); 5) distilled water (n=2) (control); 6) 0.1%chlorhexidine gluconate (n=2) (control). The apex and coronaryopening were sealed with IRM. Roots were placed in Eppendorftubes with 1 ml distilled water at 37°C and 100% humidity. Atbaseline, 7, 30 and 60 days, pH was measured with pH meter,and calcium ion content in the solution was analyzed by atomicabsorption spectrophotometry. The data were statisticallyanalyzed using ANOVA, simple linear regression analysis andPearsons correlation test. The highest pH values were achievedwith calcium hydroxide pastes at 60 days (p ≤ 0.05). Calciumions were released in all groups. The calcium hydroxide pastewith distilled water at 60 days had the highest calcium ion value(p ≤ 0.01). There was a positive correlation between calcium andpH values.
El objetivo de este estudio ex vivo fue evaluar los cambios en elpH y la difusión a través de la dentina radicular de iones calcioa partir de pastas de hidróxido de calcio (Ca (OH)2) y trióxidomineral agregado (MTA), durante 7, 30 y 60 días; y la relaciónentre el pH y la difusión de iones. Se utilizaron 32 premolareshumanos. Las coronas fueron seccionadas, los conductos radicu lares fueron instrumentados y obturados con las siguientespreparaciones: 1) Ca (OH)2 + agua destilada (n = 7); 2)Ca (OH)2 + gluconato de clorhexidina (CHX) al 0,1% (n = 7);3) MTA + agua destilada (n = 7); 4) MTA + gluconato declorhexidina al 0,1% (n = 7); 5) agua destilada (n = 2) (control);6) gluconato de clorhexidina al 0,1% (n = 2) (control). El ápicey la apertura coronaria se sellaron con IRM. Las raíces secolocaron en tubos Eppendorf con 1 ml de agua destilada a37 °C y 100% de humedad. Se midió el pH inicial y a los 7, 30 y60 días, con pHmetro, y se analizó el contenido de iones calcioen la solución por espectrofotometría de absorción atómica. Losdatos fueron analizados estadísticamente con ANOVA, análisisde regresión lineal y correlación de Pearson. Los valores de pHmás altos se obtuvieron con las pastas de hidróxido de calcio alos 60 días (p ≤ 0,05). Todos los grupos mostraron liberación deiones calcio. La pasta de hidróxido de calcio con agua destiladamostró el valor más alto de iones calcio a los 60 días (p ≤ 0,01).Hubo una correlación positiva entre los valores de pH y calcio.
Sujets)
Humains , Hydroxyde de calcium/composition chimique , Concentration en ions d'hydrogène , Oxydes/composition chimique , Produits d'obturation des canaux radiculaires/classification , Analyse de variance , Chlorhexidine/composition chimique , Perméabilité de la dentine , Eau Distillée , Interprétation statistique de données , Spectrophotométrie atomique/méthodesRésumé
Objetivo: avaliar in vitro a efetividade do biosilicato adicionado ao flúor gel acidulado e do próprio flúor gel acidulado, na redução da permeabilidade dentinária antes e após desafios ácidos. Material e métodos: 240 espécimes de dentina radicular foram aleatoriamente divididos em dois grupos, que diferiram quanto ao tratamento da superfície (Biosilicato + flúor gel ou flúor gel), e dez subgrupos, que diferiram nos desafios ácidos (sucos naturais de limão, laranja, abacaxi, uva e acerola, Gatorade (limão), Coca-Cola, suco industrializado de laranja, vinagre e vinho branco). Os espécimes foram conectados a um aparelho de pressão hidráulica para medir a permeabilidade dentinária após as seguintes etapas: I) condicionamento com ácido fosfórico a 37% por 30 segundos; II) tratamento com biosilicato ou flúor gel; III) desafios ácidos da dieta, sendo essa última fase repetida duas vezes, somando desafios ácidos. Resultados: após análise estatística com os testes de Mann-Whitney, Kruskall-Wallis e Wilcoxon, ambos os produtos diminuíram estatisticamente a permeabilidade dentinária (p < 0,001), porém, o Biosilicato adicionado ao flúor gel promoveu uma permeabilidade residual menor do que o flúor gel (p < 0,001). Porém, quase todas as substâncias ácidas promoveram aumento gradativo da permeabilidade (p < 0,05), com exceção entre o segundo e terceiro desafio ácido com vinho branco nos espécimes tratados com Biosilicato. Conclusão: ambos foram efetivos em diminuir a permeabilidade, no entanto, os desafios ácidos resultaram no aumento gradativo da permeabilidade.
Objective: to evaluate in vitro the effectiveness of the biosilicate added to acidified gel fluoride and the acidifi ed fluorine gel itself, in the reduction of dentin permeability before and after acidic challenges. Material and methods: 240 specimens of root dentin were randomly divided into two groups, differing in surface treatment (Biosilicate + fl uorine gel or fl uorine gel), and ten subgroups, differing in acidic challenges (natural juices of lemon, orange, pineapple, Grape, and acerola, Gatorade (lemon), Coca-Cola, industrialized orange juice, vinegar and white wine). The specimens were connected to a hydraulic pressure apparatus to measure the dentin permeability after the following steps: I) conditioning with 37% phosphoric acid for 30 seconds, II) treatment with biosilicate or fluoride gel, III) acidic challenges of the diet, this last phase being repeated twice, adding acidic challenges. Results: after statistical analysis with the Mann- Whitney, Kruskall-Wallis, and Wilcoxon tests, both products had a statistically significant decrease in dentin permeability (p < 0.001), but Biosilicate added to fluoride gel promoted a lower residual permeability than fluoride gel analysis (p < 0.001). However, almost all the acidic substances promoted a gradual increase of the permeability (p < 0.05), except for the second and third acid challenges with white wine in the specimens treated with Biosilicate. Conclusion: both were effective at decreasing permeability, however, acidic challenges resulted in the gradual increase of root dentin permeability.
Sujets)
Humains , Adolescent , Adulte , Matériaux biocompatibles , Perméabilité de la dentine , Hypersensibilité dentinaire , FluorRésumé
Abstract The morphology, microhardness and dentin permeability of the furcation region of maxillary premolars were evaluated. Ten premolars were cut lengthwise and the furcation region was delimited. In one group (n=10) microhardness was measured in the buccal, central and palatal regions, in the outer middle and inner layers of the furcation, and in the buccal and palatal regions adjacent to the furcation. Knoop hardness was tested with 10 g load for 15 s. Data were analyzed statistically by ANOVA and Tukey-Kramer test (a=0.05). In the other group (n=10) confocal microscopy was used to study dentin morphology. Other 10 specimens were instrumented with ProTaper and immersed in 10% copper sulfate for analysis of permeability under light microscopy. About microhardness, there was no significant difference (p>0.05) among the buccal (39.9±3.1), central (39.5±4.4) and palatal (39.7±5.0) regions of the furcation, or between these regions and the adjacent buccal (39.1±5.8) and palatal (39.7±5.8) regions (p>0.05). The inner layer (42.3±3.7) had significantly higher microhardness (p<0.05) than the outer layer (37.1±3.9). There was a tendency of calcification of the dentinal tubules from the outer towards the inner layer. The percentage of stained area was 12.45±2.0%, restricted to the outer layer. The buccal, central and palatal regions of the furcation as well as the buccal and palatal adjacent regions had similar microhardness values. In conclusion, the inner dentin layer is harder than the outer dentin layer. The dentinal tubules are sinuous and intertwine towards the middle layer. Dye penetration is restricted to the outer layer.
Resumo Estudou-se a morfologia, microdureza e permeabilidade dentinária da furca de pré-molares superiores. Dez pré-molares tiveram a porção oclusal da coroa e os terços radiculares médio e apical removidos. Cortou-se longitudinalmente o remanescente e delimitou-se a furca. As hemi-secções foram distribuídas em dois grupos. Num (n=10), mediu-se a microdureza nas regiões vestibular, central e palatina, nas camadas externa, média e interna e nas porções vestibular e palatina adjacentes à furca. Utilizou-se dureza Knoop, carga de 10 g por 15 s. Os dados foram analisados pelo teste ANOVA e Tukey-Kramer (a=0.05). No outro grupo (n=10) utilizou-se microscopia confocal para estudo da morfologia da dentina. Outros 10 espécimes foram instrumentados com Protaper e NaOCl a 1% e imersos em sulfato de cobre a 10% para análise da permeabilidade. Após preparo histológico os espécimes foram analisados em fotomicroscópio. Não houve diferença significante (p>0,05) entre a microdureza das regiões vestibular (39,9±3,1), central (39,5±4,4) e palatina (39,7±5,0), nem entre essas regiões e as adjacentes vestibular (39,1±5,8) e palatina (39,7±5,8) (p>0,05). A camada interna (42,3±3,7) é mais dura que a externa (37,1±3,9) (p<0,05). Há uma tendência dos canalículos calcificarem no sentido da camada externa para a interna. A porcentagem de área corada foi de 12,45±2.0 e restrita à camada externa. As regiões vestibular, central e palatina da furca, bem como as adjacentes vestibular e palatina apresentaram microdureza semelhante entre si. A camada interna apresentou-se mais dura que a externa. Os canalículos dentinários eram sinuosos e se entrelaçaram em direção à camada média. A penetração de corantes se restringiu à camada externa.
Sujets)
Humains , Prémolaire , Perméabilité de la dentine , Essais de dureté , MaxillaireRésumé
Abstract The objective of this study was to evaluate the effects of diode laser and a desensitizing dentifrice on dentin permeability. Fifty-two root dentin fragments were obtained (5 × 5mm) and treated with 24% EDTA gel. The samples were divided into 4 groups (n = 13): G1, control (no treatment); G2, diode laser (λ = 908 nm, 1.5 W, continuous mode, 20s); G3, application of abrasive dentifrice for 1 minute (Elmex Sensitive Professional (International Gaba); and G4, application of abrasive dentifrice for 1 minute followed by irradiation with diode laser. Ten samples per group were immersed in 2% methylene blue solution for 4h. The specimens were washed, longitudinally sectioned, observed under optical microscopy, photographed and assessed based on the degree of dye leakage. The remaining samples were observed under scanning electron microscopy (SEM). The leakage data were subjected to ANOVA test, followed by Tukey's t-test (α = 5%). Groups 2, 3 and 4 showed less dye penetration than the control group (p < 0.05), but were similar among each other. SEM images showed that dentinal tubules were open in G1, and fused and occluded in G2. Group 3 showed dentinal tubules that were occluded by the metal ions from the toothpaste. G4 presented similar characteristics to G3, and the presence of fused dentin. The diode laser and the dentifrice were effective in reducing dentinal permeability, and the combination of the two treatments did not show better results than either one used alone.
Sujets)
Animaux , Bovins , Racine dentaire/effets des médicaments et des substances chimiques , Dentifrices/composition chimique , Dentine/effets des médicaments et des substances chimiques , Perméabilité de la dentine/effets des médicaments et des substances chimiques , Hypersensibilité dentinaire/traitement médicamenteux , Agents désensibilisants dentinaires/composition chimique , Propriétés de surface/effets des médicaments et des substances chimiques , Propriétés de surface/effets des radiations , Facteurs temps , Racine dentaire/effets des radiations , Microscopie électronique à balayage , Répartition aléatoire , Reproductibilité des résultats , Dentine/effets des radiations , Perméabilité de la dentine/effets des radiations , Thérapie laser/méthodes , Lasers à semiconducteur/usage thérapeutiqueRésumé
Este estudo possui duas partes distintas: 1. in vivo (randomizado e longitudinal) que teve como objetivo avaliar protocolos de tratamento para hipersensibilidade dentinária com laser de baixa potência (com diferentes dosagens), laser de alta potência e agente dessensibilizante, por um período de 12 e 18 meses; e 2. in vitro que teve como objetivo analisar a perda de estrutura de dois dentifrícios distintos (Colgate Total 12 e Colgate Pró Alívio) e analisar a permeabilidade dentinária dos tratamentos da etapa 01, associados aos dentifrícios, após diferentes ciclos de abrasão. Na parte in vivo, as lesões cervicais não cariosas de 32 voluntários, previamente submetidos aos critérios de elegibilidade ou exclusão, foram divididas em nove grupos (n=10): G1: Gluma Desensitizer (Heraeus Kulzer), G2: Laser de baixa potência com baixa dosagem (Photon Lase, DMC) (três pontos de irradiação vestibulares e um ponto apical: 30 mW, 10 J/cm2, 9 seg por ponto com o comprimento de onda de 810nm). Foram realizadas três sessões com um intervalo de 72 horas), G3: Laser de baixa potência com alta dosagem (um ponto cervical e um ponto apical: 100 mW, 90 J/cm2, 11 seg por ponto com o comprimento de onda de 810nm. Foram realizadas três sessões com um intervalo de 72 horas), G4: Laser de baixa potência com baixa dosagem + Gluma Desensitizer, G5: Laser de baixa potência com alta dosagem + Gluma Desensitizer, G6: Laser de Nd:YAG (Power LaserTM ST6, Lares Research®), em contato com a superfície dental: 1,0W, 10 Hz e 100 mJ, ? 85 J/cm2, com o comprimento de onda de 1064nm, G7: Laser de Nd:YAG + Gluma Desensitizer, G8: Laser de Nd:YAG + Laser de baixa potência com baixa dosagem, G9: Laser de Nd:YAG + Laser de baixa potência com alta dosagem...
O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice e exploração com sonda após 12 e 18 meses do tratamento. Na parte 02, in vitro, foram utilizados terceiros molares humanos não irrompidos e recém-extraídos. Todos foram limpos e tiveram suas raízes separadas das coroas. As raízes foram seccionadas em quadrados de dentina com dimensões de 4x4x2 mm, os quais foram embutidos em resina Epoxi e devidamente polidos até uma curvatura de 0,3 ?m, analisados em perfilometria ótica. Estes foram imersos em solução de EDTA 17% por 2min para abertura dos túbulos e armazenados em uma solução de Soro Fetal Bovino diluído em salina tamponada com fosfato. Os espécimes foram divididos aleatoriamente em 12 grupos (n=10) G1: Sem tratamento de superfície, sem dentifrício; G2: Nd:YAG/sem dentifrício; G3: Gluma/sem dentifrício; G4: Nd:YAG + Gluma/sem dentifrício; G5: Sem tratamento de superfície/Colgate Total 12; G6: Nd:YAG/Colgate Total 12; G7: Gluma/Colgate Total 12; G8: Nd:YAG + Gluma/Colgate Total 12; G9: Sem tratamento de superfície/Colgate Pró Alívio; G10: Nd:YAG/Colgate Pró Alívio; G11: Gluma/Colgate Pró Alívio; G12: Nd:YAG + Gluma/Colgate Pró Alívio. Em seguida, as superfícies receberam a aplicação de fitas adesivas nas duas margens, mantendo uma área central de teste exposta de 4 x 1 mm, onde foram realizados os tratamentos de superfície e os ciclos de abrasão correspondentes a 1, 7, 30 e 90 dias de escovação (52 ciclos, 210 segundos de contato com o slurry; 361 ciclos, 1470 segundos de contato com o slurry; 1545 ciclos, 6300 segundos de contato com o slurry; 4635 ciclos, 18900 segundos de contato com o slurry, respectivamente). A cada etapa de abrasão, foi realizada análise em Perfilometria Ótica. Para as analises de permeabilidade e Microscopia Eletrônica de Varredura, foram utilizadas amostras circulares de 6 mm de diâmetro e 1 mm de espessura de dentina...
This study has two distinct parts: in vivo (randomized and longitudinal) that aimed to assess different protocols for the treatment of dentin hypersensitivity with low power laser (with different doses), high power laser and a desensitizing agent, for a period of 12 and 18 months; and an in vitro part that aimed to analyze the loss of structure of two toothpastes (Colgate Total 12 and Colgate Pro Relief) and analyze dentin permeability and micrographs after different abrasion cycles. In the in vivo part, the lesions from 32 patients, that were submitted to the inclusion and exclusion criterias, were divided into nine groups (n = 10): G1: Gluma Desensitizer (Heraeus Kulzer), G2: Low power laser with low dose (Photon Lase, DMC, three points of irradiation in vestibular portion and an apical point: 30 mW, 10 J/cm2, 9 sec per point with the wavelength of 810nm, with three sessions with an interval of 72 hours) G3: low power laser with high dose (one pointin the cervical area, and one apical point: 100 mW, 90 J/cm2, 11 sec per point with the wavelength of 810nm in three sessions with an interval of 72 hours), G4: Low power laser with low dose + Gluma Desensitizer, G5: Low power laser with high dose + Gluma Desensitizer, G6: Nd:YAG laser (Power LaserTM ST6, Research® in contact: 1.0W, 10 Hz and 100 mJ, ? 85 J/cm2, with the wavelength of 1064nm,), G7: Nd:YAG laser + Gluma Desensitizer, G8: Nd:YAG laser + low power laser with low dose G9: Nd:YAG laser + low power laser with high dose. The level of sensitivity of each volunteer was assessed by visual analogue scale of pain (VAS) with the aid of air from the triple syringe and exploration probe, 12 and 18 months after treatment. In the in vitro part, unerupted and recently extracted human third molars were used...
Sujets)
Humains , Abrasion dentaire/complications , Abrasion dentaire/diagnostic , Perméabilité de la dentine , Hypersensibilité dentinaire/complications , Hypersensibilité dentinaire/diagnosticRésumé
Este estudo possui duas partes distintas: 1. in vivo (randomizado e longitudinal) que teve como objetivo avaliar protocolos de tratamento para hipersensibilidade dentinária com laser de baixa potência (com diferentes dosagens), laser de alta potência e agente dessensibilizante, por um período de 12 e 18 meses; e 2. in vitro que teve como objetivo analisar a perda de estrutura de dois dentifrícios distintos (Colgate Total 12 e Colgate Pró Alívio) e analisar a permeabilidade dentinária dos tratamentos da etapa 01, associados aos dentifrícios, após diferentes ciclos de abrasão. Na parte in vivo, as lesões cervicais não cariosas de 32 voluntários, previamente submetidos aos critérios de elegibilidade ou exclusão, foram divididas em nove grupos (n=10): G1: Gluma Desensitizer (Heraeus Kulzer), G2: Laser de baixa potência com baixa dosagem (Photon Lase, DMC) (três pontos de irradiação vestibulares e um ponto apical: 30 mW, 10 J/cm2, 9 seg por ponto com o comprimento de onda de 810nm). Foram realizadas três sessões com um intervalo de 72 horas), G3: Laser de baixa potência com alta dosagem (um ponto cervical e um ponto apical: 100 mW, 90 J/cm2, 11 seg por ponto com o comprimento de onda de 810nm. Foram realizadas três sessões com um intervalo de 72 horas), G4: Laser de baixa potência com baixa dosagem + Gluma Desensitizer, G5: Laser de baixa potência com alta dosagem + Gluma Desensitizer, G6: Laser de Nd:YAG (Power LaserTM ST6, Lares Research®), em contato com a superfície dental: 1,0W, 10 Hz e 100 mJ, ? 85 J/cm2, com o comprimento de onda de 1064nm, G7: Laser de Nd:YAG + Gluma Desensitizer, G8: Laser de Nd:YAG + Laser de baixa potência com baixa dosagem, G9: Laser de Nd:YAG + Laser de baixa potência com alta dosagem.
O nível de sensibilidade de cada voluntário foi avaliado através da escala visual analógica de dor (VAS) com auxílio do ar da seringa tríplice e exploração com sonda após 12 e 18 meses do tratamento. Na parte 02, in vitro, foram utilizados terceiros molares humanos não irrompidos e recém-extraídos. Todos foram limpos e tiveram suas raízes separadas das coroas. As raízes foram seccionadas em quadrados de dentina com dimensões de 4x4x2 mm, os quais foram embutidos em resina Epoxi e devidamente polidos até uma curvatura de 0,3 ?m, analisados em perfilometria ótica. Estes foram imersos em solução de EDTA 17% por 2min para abertura dos túbulos e armazenados em uma solução de Soro Fetal Bovino diluído em salina tamponada com fosfato. Os espécimes foram divididos aleatoriamente em 12 grupos (n=10) G1: Sem tratamento de superfície, sem dentifrício; G2: Nd:YAG/sem dentifrício; G3: Gluma/sem dentifrício; G4: Nd:YAG + Gluma/sem dentifrício; G5: Sem tratamento de superfície/Colgate Total 12; G6: Nd:YAG/Colgate Total 12; G7: Gluma/Colgate Total 12; G8: Nd:YAG + Gluma/Colgate Total 12; G9: Sem tratamento de superfície/Colgate Pró Alívio; G10: Nd:YAG/Colgate Pró Alívio; G11: Gluma/Colgate Pró Alívio; G12: Nd:YAG + Gluma/Colgate Pró Alívio. Em seguida, as superfícies receberam a aplicação de fitas adesivas nas duas margens, mantendo uma área central de teste exposta de 4 x 1 mm, onde foram realizados os tratamentos de superfície e os ciclos de abrasão correspondentes a 1, 7, 30 e 90 dias de escovação (52 ciclos, 210 segundos de contato com o slurry; 361 ciclos, 1470 segundos de contato com o slurry; 1545 ciclos, 6300 segundos de contato com o slurry; 4635 ciclos, 18900 segundos de contato com o slurry, respectivamente). A cada etapa de abrasão, foi realizada análise em Perfilometria Ótica. Para as analises de permeabilidade e Microscopia Eletrônica de Varredura, foram utilizadas amostras circulares de 6 mm de diâmetro e 1 mm de espessura de dentina...
This study has two distinct parts: in vivo (randomized and longitudinal) that aimed to assess different protocols for the treatment of dentin hypersensitivity with low power laser (with different doses), high power laser and a desensitizing agent, for a period of 12 and 18 months; and an in vitro part that aimed to analyze the loss of structure of two toothpastes (Colgate Total 12 and Colgate Pro Relief) and analyze dentin permeability and micrographs after different abrasion cycles. In the in vivo part, the lesions from 32 patients, that were submitted to the inclusion and exclusion criterias, were divided into nine groups (n = 10): G1: Gluma Desensitizer (Heraeus Kulzer), G2: Low power laser with low dose (Photon Lase, DMC, three points of irradiation in vestibular portion and an apical point: 30 mW, 10 J/cm2, 9 sec per point with the wavelength of 810nm, with three sessions with an interval of 72 hours) G3: low power laser with high dose (one pointin the cervical area, and one apical point: 100 mW, 90 J/cm2, 11 sec per point with the wavelength of 810nm in three sessions with an interval of 72 hours), G4: Low power laser with low dose + Gluma Desensitizer, G5: Low power laser with high dose + Gluma Desensitizer, G6: Nd:YAG laser (Power LaserTM ST6, Research® in contact: 1.0W, 10 Hz and 100 mJ, ? 85 J/cm2, with the wavelength of 1064nm,), G7: Nd:YAG laser + Gluma Desensitizer, G8: Nd:YAG laser + low power laser with low dose G9: Nd:YAG laser + low power laser with high dose. The level of sensitivity of each volunteer was assessed by visual analogue scale of pain (VAS) with the aid of air from the triple syringe and exploration probe, 12 and 18 months after treatment. In the in vitro part, unerupted and recently extracted human third molars were used.
Sujets)
Abrasion dentaire/complications , Abrasion dentaire/diagnostic , Perméabilité de la dentine , Hypersensibilité dentinaire/complications , Hypersensibilité dentinaire/diagnosticRésumé
O objetivo deste trabalho foi avaliar in vitro a ação do trimetafosfato de sódio microparticulado (TMPm) ou nanoparticulado (TMPn) associado ao fluoreto (F) em formulações de dentifrícios na obliteração dos túbulos dentinários (TD), concentração mineral e condutância hidráulica. Blocos de dentina radicular bovina (4×4×2 mm) foram planificados e os TD desobliterados com solução de ácido fosfórico a 37%. Para o estudo da avaliação da obliteração dos túbulos e concentração mineral, os blocos (n=20/grupo) foram submetidos à escovação mecânica (2x/dia) durante 7 dias com dentifrícios: placebo, 1100 ppm F, 1100 ppm F associado a 3% TMPm, 1100 ppm F associado a 3% TMPn. Ao final dos tratamentos, dez blocos por grupo foram imersos em ácido cítrico (pH 3,2), durante 1 minuto. O número, diâmetro e área de TD desobstruídos foram quantificados utilizando microscopia eletrônica de varredura (MEV) e a % atômica dos elementos químicos (Ca, P, C, N e O) dos precipitados presentes nos TD foi determinada por energia dispersiva de raios-X. Foi avaliada a concentração mineral da dentina (gHAp × cm-3) utilizando um microtomógrafo com resolução espacial de 1,5 µm. Os dados foram submetidos à análise de variância (2-critérios) seguida pelo teste de StudentNewman-Keuls (p<0,05). Os dentifrícios contendo TMPm e TMPn produziram maior obliteração dos TD e maior concentração mineral quando comparados com outros grupos. Não foram observadas diferenças significativas entre 1100 TMPm e 1100 TMPn ou entre placebo e 1100 ppm F; porém o grupo 1100 ppm F apresentou maior concentração mineral quando comparado ao placebo. A proporção Ca/P foi maior nos grupos com TPM; o ataque ácido reduziu a proporção Ca/P para todos os grupos. A % de C e N foi significativamente menor para 1100 TMPm e 1100 TMPn antes do ataque ácido, mas aumentou depois. A % atômica de O foi maior antes do ataque ácido para grupos com TMP. Para o estudo da condutância hidráulica, determinou-se inicialmente a condutância máxima da dentina e os blocos (n=15/grupo) foram submetidos à escovação mecânica como descrito previamente. Após os tratamentos dos blocos, em 5 blocos de cada grupo foi analisada a superfície da dentina utilizando MEV. Nos demais blocos (n=10/grupo) foi determinada a condutância hidráulica pós-tratamento. Em seguida, os blocos foram imersos em ácido cítrico (pH 3,2) por 1 minuto e a condutância determinada novamente. Os dados foram submetidos à análise de variância (2-critérios) de medidas repetidas seguida pelo teste Student-Newman-Keuls (p<0,05). Todos os tratamentos apresentaram uma redução da condutância hidráulica. Uma redução significativa na condutância foi observada nos tratamentos com dentifrícios contendo TMP. Após o ataque ácido houve um aumento da condutância hidráulica em todos os grupos, exceto o grupo com TMPm. Os grupos com TMP produziram maior obliteração dos TD quando comparados aos outros grupos. Os dentifrícios contendo TMPm apresentaram precipitados com aglomerados maiores quando comparado ao TMPn. Concluiu-se que a adição de TMP microparticulado ou nanoparticulado a dentifrícios contendo 1100 ppm F levou a maior obliteração dos túbulos dentinários, maior concentração mineral e menor condutância hidráulica quando comparada ao 1100 ppm F(AU)
The objective of this study was to evaluate in vitro the effect of TMP microparticles (TMPm) or nanoparticles (TMPn) associated with fluoride (F) in toothpaste formulations on the obliteration of dentinal tubules (DT), mineral concentration and hydraulic conductance. Bovine root dentin blocks (4×4×2 mm) were ground flat and the DT were unobstructed by phosphoric acid 37%. For study of evaluation of the tubules obliteration and mineral concentration, the blocks (n=20/group) were submitted to mechanical brushing (2x/day) during 7 days with toothpastes: placebo, 1100 ppm F, 1100 ppm F associated with 3% TMPm, 1100 ppm F associated with 3% TMPn. After that, ten blocks of each group were immersed in citric acid (pH 3.2) for 1 minute. The number, diameter and area of unobstructed DT were quantified using scanning electron microscopy (SEM) and atomic % of chemical elements (Ca, P, C, N and O) from precipitates in DT were determined by energy-dispersive X-ray. Dentin mineral concentration (gHAp × cm-3) was evaluated utilizing Micro-CT at 1.5 µm of spatial resolution. Data were submitted to 2-way ANOVA, followed by Student-Newman-Keuls test (p<0.05). Toothpastes containing TMPm and TMPn promoted higher obliteration of DT and greater mineral concentration when compared to other groups. No significant differences were observed between 1100 TMPm and 1100 TMPn, or between placebo and 1100 ppm F; however 1100 ppm F group had higher mineral concentration compared to placebo. Higher Ca/P ratios were observed in the groups treated with TMP; the acid challenge reduced Ca/P ratio for all groups. The atomic % of C and N was significantly lower for 1100 TMPm and 1100 TMPn before acid challenge, but increased afterwards. The atomic % of O was higher before before acid challenge to TMP groups. For study of hydraulic conductance was determined initially the maximum hydraulic conductance of the dentin and the blocks (n=15/group) were subjected to mechanical brushing as described previously. After treatment of the blocks, in 5 blocks of each group was analyzed the dentin surface using SEM. In other blocks (n=10/group) was determined the post-treatment hydraulic conductance. After that, the blocks were submitted to citric acid (pH 3.2) by 1 minute, and the conductance determined again. The data was submitted to 2-way ANOVA repeated measures, followed by Student-Newman-Keuls test (p<0.05). All treatments showed a reduction in hydraulic conductance. A significant reduction in conductance was observed in the treatments with TMP toothpastes. After acid challenge, there was an increase of the hydraulic conductance in all groups, except TMPm group. The TMP groups produced higher obliteration of the DT when compared to the others. The toothpastes containing TMPm showed precipitates with bigger clusters when compared to TMPn. It was concluded that addition of TMP microparticles or nanoparticles to toothpastes containing 1100 ppm F led to greater obliteration of the dentinal tubules, higher concentration mineral and lower hydraulic conductance when compared to 1100 ppm F(AU)
Sujets)
Dentifrices , Dentine , Fluorures , Phosphates , Perméabilité de la dentine , NanoparticulesRésumé
<p><b>OBJECTIVE</b>To investigate the effect of epigallocatechin-3-gallate (EGCG) on biomodification of demineralized dentine substrate, in its permeability, hydrophobicity, and inhibition ability to collagen enzymatic degradation.</p><p><b>METHODS</b>The dentine substrates were treated with simulated pulpal pressure created by mixtures of 0.02%, 0.1% EGCG/bovine serum albumin (BSA) in acidic environment (pH4.4) for 48 h. A fluid-transport model was used to measure the fluid permeability through demineralized dentine substrate. Positive replicas of dentine substrate were fabricated before and after being subjected to acidic environment for scanning electron microscope (SEM) examination. The blank group contained no EGCG and the positive group were treated with Gluma desensitizer. Static contact angle measurements on demineralized dentin and 0.1% EGCG primed dentin were performed by contact angle analyzer. The priming time were 60 s, 120 s, 0.5 h, 1 h. Dentine specimens bonded with Adper single bond 2 were subjected to 100 mg/L collagenase and observed under SEM. Resin-bonded specimens (with 0.02%, 0.1%, 0.5% EGCG priming, or without EGCG priming) were created for micro-tensile bond strength evaluation (MTBS). Resin-bonded specimens after thermol cycling were created for MTBS evaluation.</p><p><b>RESULTS</b>The fluid permeability in the blank control group increased ([151.3±22.3]%), the fluid permeability in 0.1% EGCG/BSA group decreased ([23.7±6.3]%). Compared to the blank control group, the contact angle of 120 s, 0.5 h, 1 h groups increased by 31.0%, 53.5%, 57.8% in deep dentin and 37.4%, 59.3%, 62.4% in shallow dentin. The SEM examination showed that 0.1% and 0.5% EGCG priming for 120 s significantly increased dentin collagen's resistance to collagenase. The immediate MTBS of 0.1% and 0.5% EGCG groups were (29.4±4.8) and (19.8± 4.9) MPa. After thermol cycling, the MTBS of 0.1% and 0.5% EGCG groups were (19.9±5.1) and (15.3± 6.3) MPa.</p><p><b>CONCLUSIONS</b>Under acidic environment (pH4.4), the 0.1% EGCG can reduce dentine permeability under acidic environment. The 0.1% EGCG can increase hydrophobicity of dentin substrate, and strengthen dentin substrate's resistance to collagenase hydrolysis, thus increased the resin-dentin bonding durability.</p>
Sujets)
Mordançage à l'acide , Catéchine , Pharmacologie , Collagène , Chimie , Collagenases , Pharmacologie , Résines composites , Collage dentaire , Ciments dentaires , Pulpe dentaire , Dentine , Chimie , Perméabilité de la dentine , Agents de collage dentinaire , Glutaraldéhyde , Pharmacologie , Concentration en ions d'hydrogène , Hydrolyse , Méthacrylates , Pharmacologie , Microscopie électronique à balayage , Pression , Céments résine , Sérumalbumine bovine , Pharmacologie , Résistance à la traction , Facteurs tempsRésumé
Introdução: todo canal radicular instrumentado, seja por métodos manuais ou rotatórios, apresentará a formação de uma lama de detritos sobre a parede dentinária, sendo esta composta tanto por matéria orgânica quanto inorgânica, denominada de smear layer. Em relação a sua remoção ou manutenção das paredes do canal, diversos autores apresentaram opiniões e resultados divergentes, gerando dúvidas aos clínicos em relação à conduta mais adequada a ser empregada no tratamento endodôntico. Objetivo: este trabalho, por meio de uma revisão de literatura, visa fornecer uma resposta clara, capaz de melhorar o prognóstico do tratamento. Metodologia: para isso, foram utilizados 25 trabalhos desde o ano de 1975 a 2014, coletados por meio das bases de dados PubMed e Web of Science, com as palavras chaves: "smear layer", "smear layer removal", "smear layer permeability", "smear layer bacteria" e "smear layer sealing". Conclusão: baseado na metodologia proposta pode-se concluir que a remoção da smear layer é a melhor conduta a ser tomada durante o tratamento endodôntico, pois proporciona uma ação antimicrobiana mais eficiente das substâncias irrigadoras e medicações intracanais, além de permitir um melhor selamento entre dentina e material obturador, reduzindo as chances de uma infiltração.
Introduction: the root canal instrumentation, either by manual or mechanicals methods, will result in a formation of debris layer on dentin surface composted by organic and inorganic tissues, denominated smear layer. Due to the several divergent opinion about its removal or maintenance into the root canal, the clinicians may have a doubt for the most appropriate conduct to be performed in endodontics treatments. Objective: this article aimed collect the mains results obtained by different authors to provide a clear answer capable of improving the treatment prognosis. Methods: for this, were used 25 articles since 1975 to 2014 collected by date base PubMed and Web of Science with the keywords "smear layer", "smear layer removal", "smear layer permeability", "smear layer bacteria" and "smear layer sealing". Conclusion: based in the informations obtained in this review, its was concluded that the smear layer removal can, not only, improve the antimicrobial action of the irrigants agents and intracanal medicaments, but also provide a most efficient sealing of the fillingmaterial to dentine wall, reducing the chances to occur a leak in its interface.
Sujets)
Humains , Mâle , Femelle , Boue dentinaire , Perméabilité de la dentine , Pronostic , EndodontieRésumé
The aim of this study was to evaluate the demineralization and hydrogen peroxide (HP) penetration in teeth with incipient lesions submitted to bleaching treatment. For analysis of HP penetration, sound and demineralized enamel/dentin discs were placed in artificial pulp chambers containing acetate buffer solution. After bleaching treatment, this solution was subjected for analysis of optical density by spectrophotometry and the disc surfaces were analyzed with scanning electron microscopy (SEM) and polarized light microscopy (PLM). The remaining discs were subjected for cross-sectional hardness analysis at different depths. Data were analyzed by repeated measures ANOVA and PLSD Fisher test (a=0.05). It was observed that previously demineralized teeth showed greater HP penetration (p<0.05). The bleaching treatment caused changes to a depth of 20 µm in sound enamel and up to 90 µm in demineralized enamel. SEM and PLM images revealed that the bleaching treatment caused superficial changes that were considerably more accentuated in previously demineralized teeth. It may be concluded that the enamel mineralization level influences HP penetration and the bleaching agent contributed to increase the demineralization depth.
O objetivo deste estudo foi avaliar a desmineralização e a penetração do peróxido de hidrogênio (HP) em dentes com lesões incipientes submetidos ao tratamento clareador. Para analisar a penetração do peróxido de hidrogênio, discos de esmalte/dentina hígidos e desmineralizados foram posicionados em câmaras pulpares artificiais contendo solução tampão de acetato. Após o tratamento clareador, esta solução foi submetida à análise da densidade óptica no espectrofotômetro e as superfícies dos discos foram analisadas por meio de microscopia eletrônica de varredura (MEV) e microscopia de luz polarizada (MLP). Os discos restantes foram submetidos à análise de microdureza transversal em diferentes profundidades. Os dados foram submetidos aos testes ANOVA e teste PLSD Fisher (= 5%). Observou-se que os dentes previamente desmineralizados mostraram maior penetração de HP (p<0,05). O tratamento clareador causou alterações em uma profundidade de 20 μm em esmalte hígido e até 90 μm em esmalte desmineralizado. As imagens obtidas em PLM e MEV mostraram que o tratamento clareador promove alterações superficiais no esmalte, sendo mais pronunciadas em dentes previamente desmineralizados. Foi concluído que o nível de mineralização do esmalte influencia a penetração do PH e que o agente clareador contribuiu para o aumento da profundidade de desmineralização.