Résumé
This study evaluated the effect of different concentrations of sodium trimetaphosphate (TMP) with and without fluoride (F) on the concentration of calcium (Ca), phosphorus (P) and F in hydroxyapatite (HA). Synthetic HA powder (0.15 g) was suspended (n=6) in solutions (75 mL) of TMP at 0%, 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1.0%, 2.0%, 4.0%, 6.0%, 8.0% and 10% concentrations in the presence and absence of 100 ppm F and subjected to a pH-cycling process. The precipitates were filtrated, dried at 70° C for 24 h and ground onto a fine powder. The concentrations of F (KOH (CaF2) and HCl (FA) soluble), Ca (Arsenazo III), and P (molybdate method) in HA were determined. The Ca P, and Ca/P ratio data were subjected to Tukey's test and the F data were subjected to Student-Newman-Keuls test (p<0.05). The addition of TMP to the samples reduced F deposition to 98% (p<0.001). The groups containing 100 ppm F and 0.4% or 0.6% TMP exhibited a higher Ca concentration than the group containing only 100 ppm F (p<0.05). Furthermore, the HA treated with 0.2% and 0.4% TMP and 100 ppm F showed a higher Ca/P ratio than the other groups (p<0.001). In conclusion, TMP at 0.2%, 0.4% and 0.6% concentrations combined with F seemed to be able to precipitate HA with low solubility. However, especially at high concentrations, TMP interferes with F deposition on HA.
Este estudo avaliou o efeito de diferentes concentrações de trimetafosfato de sódio (TMP) com e sem fluoreto (F) nas concentrações de cálcio (Ca), fósforo (P) e F na hidroxiapatita (HA). Pó de HA sintético (0,15 g) foi suspenso (n=6) em soluções (75 mL) de TMP com concentrações de 0%, 0,1%, 0,2%, 0,4%, 0,6%, 0,8%, 1,0%, 2,0%, 4,0%, 6,0%, 8,0% e 10% na presença ou na ausência de 100 ppm F e foram submetidas ao processo de ciclagem de pH. O precipitado foi filtrado seco a 70°C por 24 h e triturado em um pó fino. As concentrações de F (solúvel em KOH: CaF2, e em HCl: FA), Ca (Arsenazo III) e P (método do molibdato) foram determinadas na HA. Os dados de Ca, P e de proporção Ca/P foram submetidos ao teste de Tukey e os dados de F ao teste Student-Newman-Keuls (p<0,05). A adição de TMP reduziu a deposição de F em 98% (p<0,001). Os grupos contendo 100 ppm F e TMP 0,4% e 0,6% apresentaram maiores concentrações de Ca do que o grupo contendo somente 100 ppm F (p<0,05). Além disso, a HA tratada com 0,2% e 0,4% de TMP e 100 ppm F apresentou maiores proporções Ca/P em relação aos demais grupos (p<0,001). Em conclusão, TMP nas concentrações de 0,2%, 0,4% e 0,6% quando associado ao F é capaz de precipitar uma HA com menor solubilidade. Entretanto, especialmente em altas concentrações, TMP interfere com a deposição de F na HA.
Sujets)
Humains , Cariostatiques/composition chimique , Durapatite/composition chimique , Polyphosphates/composition chimique , Précipitation chimique , Cristallisation , Calcium/analyse , Cariostatiques/administration et posologie , Durapatite/analyse , Fluorures/analyse , Fluorures/composition chimique , Concentration en ions d'hydrogène , Test de matériaux , Phosphore/analyse , Polyphosphates/administration et posologie , Solubilité , Température , Facteurs tempsRésumé
Objetivou-se estudar a influência da adição de polifosfato em lingüiça frescal de frango sobre os padrões físico-químicos esensoriais, avaliando a aceitação dos consumidores e o prazo de vida comercial das formulações. Foram produzidas quatroformulações de lingüiça de frango: uma controle e três com diferentes concentrações de polifosfato: 0,1, 0,3 e 0,5 por cento. Asamostras foram armazenadas sob refrigeração (0±1oC) e submetidas às análises de: atividade de água (aa); teor de umidade;produção de Bases Voláteis Totais (BVT); pH; substâncias reativas ao ácido 2-tiobarbitúrico (TBA) e sensorial. As análisesfísico-químicas foram realizadas, periodicamente, até o 15o dia de armazenamento. A análise sensorial (teste de aceitação emescala hedônica) foi realizada no 1o dia de armazenamento. Além da análise estatística descritiva, realizou-se a análise devariância e posterior teste de comparação entre médias (Tukey). A aa não apresentou diferença significativa (p>0,05) entre asamostras. A produção de BVT nas amostras adicionadas de 0,5 por cento de polifosfato foi menor que nas demais amostras. O pH,nas amostras com 0,5 por cento de polifosfato mantiveram-se estáveis por um período maior em relação aos demais tratamentos. Aumidade foi maior nas amostras controle (70 por cento) que nas adicionadas com 0,5 por cento de polifosfato, o menor percentual (67 por cento),ocorrendo diferença significativa (p<0,05) entre as duas formulações. No teste de aceitação, pôde-se comprovar uma diferençasignificativa (p<0,05) em relação ao atributo suculência entre as amostras controle e as adicionadas de 0,3 por cento de polifosfato.Pôde-se concluir que a utilização do polifosfato melhorou o rendimento do produto final, promovendo o aumento da suculênciae auxiliando na conservação da lingüiça de frango.
The objective was to study the influence of the polyphosphate addition in fresh sausage chicken on the physiochemical andsensorial patterns, evaluating the acceptance of the formulations by the consumers and the period of shelf life. Four formulationsof chicken sausage were produced: a control and three with different polyphosphate concentrations: 0.1; 0.3 and 0.5 percent. Thesamples were stored under cooling (0±1oC) and submitted to the analyses of: water activity (aw); moisture percent; productionof total volatile bases (TVB); pH; substances reactivate to the acid 2-tiobarbitúrico (TBA), and acceptance test. Physiochemicalanalyses were accomplished, periodically, until the 15th day. Sensorial analysis (acceptance test with the use of the hedonicscale) was accomplished in the 1st day. Besides the descriptive statistical analysis, took place, also, variance analysis andsubsequent test of mean comparisons of averages (Tukey). In relation to aw it was observed that there was not significantdifference (p>0.05) for the samples control and treated with different polyphosphate concentrations (0.1; 0.3 and 0.5 percent). Theproduction of TVB in the samples added of 0.5 percent of polyphosphate was smaller than in the other samples. Similar results wereobtained in relation to the pH, staying with approximately 6.21 until the 10th day of the experiment. Significant difference (p<0.05)was observed on moisture in control sample (70 percent) than the samples treated with 0.5 percent of polyphosphate (67 percent). Acceptancetest show a significant difference (p<0.05) in juicy attribute among the control samples and added of 0.3 percent of polyphosphate. Itcan be concluded that polyphosphate improves the income of the final product, promotes the increase of juicy and aids in theconservation of fresh chicken sausage.
Sujets)
Animaux , Additifs alimentaires/administration et posologie , Analyse d'aliment , Viande , Volaille , Polyphosphates/administration et posologieRésumé
Avaliou-se a utilização de coadjuvantes na diminuição da placa bacteriana e formação do cálculo dentário em 16 cães. O delineamento experimental foi casualizado com quatro tratamentos (T) e quatro repetições. Os tratamentos foram: T1- controle, T2- coadjuvante com ação mecânica, T3- coadjuvante com tripolifosfato de sódio e T4- coadjuvante com hexametafosfato de sódio. Após sete dias de adaptação, no dia anterior ao início dos tratamentos, os animais foram submetidos à remoção de cálculo dentário. O experimento teve duração de 21 dias e ao final realizaram-se as medições das placas bacterianas formadas com o uso de marcadores (fucsina). O coadjuvante somente com ação mecânica não foi efetivo em retardar o aparecimento da placa bacteriana. Os coadjuvantes com polifosfatos apresentaram uma ação efetiva e significativa na diminuição da formação do calculo dentário
The use of coadjutants in the decrease of the bacterial plate and formation of the dental calculus was evaluated in 16 dogs. The experimental design was randomized with four treatments (T) and four repetitions. The treatments were the following: 1- control; 2- coadjutant 1 (one) with mechanical action; 3- coadjutant 2 (two) with tripolyphosphate of sodium and 4- coadjutant 3 (three) with hexametaphosphate of sodium. After seven days of adaptation, on the day previous to the beginning of the treatments, the animals were submitted to the removal of dental calculus and after twenty-one days of treatment a measurement of the bacterial plaque formed through the use of markers (fucsin). The coadjutant only with mechanical action was not effective in delaying the appearance of the bacterial plaque. The coadjutant containing polyphosphates presented an effective and significant action decreasing the formation of the dental calculus