RESUMO
Objective: Evaluate the protective effect of artificial saliva formulations associated or not with mucin on dentin. Materials and Methods: Bovine dentin specimens were randomly allocated to 10 groups (n = 20) according to the artificial saliva tested and the presence or absence of mucin: Amaechi et al. (1998); Klimek et al. (1982); Vieira et al. (2005) and Eisenburger et al. (2001) and deionized water (control). Samples were submitted to an erosive cycle consisting of two immersions of 120 min in the saliva, followed by 1 min in hydrochloric acid solution, and new storage in saliva for 120 min. Surface loss (µm) was measured before and after the cycle. Data were analyzed using 2-way ANOVA and Tukey's test (p < 0.05). Results: A significant difference was observed for the saliva formulation but not for the presence of mucin. The deionized water provided the highest surface loss and the Eisenburger's saliva formulation the lowest. The groups testing the Amaechi, Klimek, and Vieira saliva did not present significant differences. Conclusion: Eisenburger's saliva formulation provides a higher protective effect against dentin erosion. The presence of mucin did not increase the erosion-preventive effect of artificial saliva formulations. (AU)
Objetivo: Avaliar o efeito protetor de formulações de saliva artificial associadas ou não à mucina sobre a dentina submetida a erosão. Material e Métodos: Espécimes de dentina bovina foram alocados em 10 grupos (n = 20) de acordo com a saliva testada e a presença ou ausência de mucina: . Amaechi et al. (1998); Klimek et al. (1982); Vieira e cols. (2005), Eisenburger et al (2001) e agua deionizada (controle). As amostras foram submetidas a um ciclo erosivo composto por duas imersões de 120 min na saliva, seguidas de 1 min em solução de ácido clorídrico e novo armazenamento na saliva por 120 min. A perda de superfície (µm) foi medida antes e depois do ciclo. Os dados foram analisados usando ANOVA 2 fatores e teste de Tukey (p <0,05). Resultados: Foi observada diferença significativa para a formulação de saliva, mas não para a presença de mucina. A água deionizada proporcionou a maior perda de superfície e a formulação de saliva de Eisenburger a menor. Os grupos que testaram a saliva Amaechi, Klimek e Vieira não apresentaram diferenças significativas entre si. Conclusão: A formulação de saliva de Eisenburger fornece o maior efeito protetor contra a erosão dentinária e a presença de mucina não aumentou o efeito preventivo de erosão de formulações de saliva artificial (AU).
Assuntos
Saliva Artificial , Erosão Dentária , Desgaste dos Dentes , MucinasRESUMO
Objective: to investigate the antimicrobial effects of toothpastes containing bioactive surface pre-reacted glass particles (S-PRG) on S. mutans biofilms adherence, initial colonization and maturation. Material and Methods: a reference UA 159 and a clinical S. mutans (SM6) strain were used. Bovine enamel specimens were randomly allocated into the groups (n=5): toothpastes containing 0%; 1%; 5%; 20%; 30% S-PRG; positive control dentifrice (NaF+triclosan); and negative control (distilled water). For biofilm development, samples were placed in a 24-well plate containing artificial saliva (4h), followed by adding 1mL of artificial saliva, BHI broth and 225µL of S. mutans suspension. Treatments with toothpastes were applied previously or after 4h and 24h of biofilm formation. Samples were incubated for 48h at 37°C in 5%CO2 and biofilm was detached and seeded in Petri dishes for determining the number of viable cells. Data were analyzed by ANOVA and Tukey test (5%). Results: significantly lower microorganisms' adherence (p<0.05) was obtained for all S-PRG toothpastes, with similar results to NaF+triclosan for SM6 and 20 and 30%S-PRG groups exhibiting higher inhibition effect than the NaF+Triclosan for UA159. Antibacterial effect on the early-stage biofilm was also observed for the S-PRG groups, but was not superior to the NaF+Triclosan toothpaste. For the mature biofilm, the effective antimicrobial potential of S-PRG toothpastes was observed only for the SM6 clinical strain, but was not higher than the positive control. Conclusion: experimental S-PRG toothpastes were effective to inhibit S. mutans biofilm growth by exhibiting antimicrobial activity, being promising agents to prevent cariogenic biofilm development (AU)
Objetivo: investigar o efeito de dentifrícios contendo S-PRG sobre a colonização inicial e maturação de biofilmes de S. mutans. Material e Métodos: uma cepa de referência (UA 159) e uma cepa clínica de S. mutans (SM6) foram utilizadas. Espécimes de esmalte bovino foram alocados nos grupos (n=5): dentifrícios contendo 0%; 1%; 5%; 20% e 30%S-PRG; controle positivo (NaF+triclosan); e controle negativo (água destilada). Os espécimes foram inseridos em uma placa de 24 poços contendo saliva artificial (4h), seguido por adição de 1mL de saliva artificial, BHI, 225µL de suspensão de S. mutans e foram tratados com suspensões de dentifrícios antes ou depois de 4 e 24h da formação do biofilme. Os espécimes foram incubados por 48h e o biofilme foi removido dos espécimes e semeado em placas de Petri para contagem de UFC/mL. Os dados foram analisados por ANOVA e teste de Tukey (5%). Resultados: houve diminuição na adesão de microrganismos para os grupos tratados com S-PRG (p<0.05). Para SM6, os dentifrícios contendo S-PRG apresentaram resultados semelhantes ao NaF+triclosan e para a cepa UA159 o dentifrício com 30%S-PRG apresentou efeito superior. Efeito antimicrobiano no biofilme recém-formado (4h) foi observado para os grupos contendo S-PRG, mas não foi observado efeito superior ao NaF+Triclosan. Para o biofilme maduro, efeito antimicrobiano do S-PRG foi observado apenas para a cepa clínica, mas não superior ao efeito do NaF+Triclosan. Conclusão: dentifrícios contendo S-PRG foram eficazes na inibição do desenvolvimento de biofilmes de S. mutans, sendo promissores agentes para prevenir o desenvolvimento de biofilme cariogênico. (AU)
Assuntos
Animais , Bovinos , Streptococcus mutans , Biofilmes , Esmalte Dentário , Placa Dentária , DentifríciosRESUMO
Resumo Este estudo desenvolveu e testou géis experimentais contendo íons fluoreto (F-) e estanho (Sn2+) para o controle da erosão dentária. Os espécimes polidos, de esmalte e dentina, foram previamente erodidos (solução de ácido cítrico a 1%, 10 min) e alocados aleatoriamente em 5 grupos (n = 10): Placebo - gel de hidroxipropilmetilcelulose (HMC); F + Sn + HMC - 7.500 ppm F- / 15.000 ppm Sn2+; F + HMC - 7.500 ppm F-; Gel de flúor fosfato acidulado comercial (12.300 ppm F-); e Controle - sem tratamento. Após o tratamento (aplicado por 60 s), os espécimes foram submetidos a uma ciclagem de erosão-remineralização (5 min em solução de ácido cítrico a 0,3%, 60 min em saliva artificial, 4 × / dia, 20 dias). A perda de superfície (SL, em µm) foi determinada após o 5º, 10º e 20º dias de ciclagem (α = 0,05). Para o esmalte, após 5 e 10 dias, o F + Sn + HMC apresentou a menor PS, não diferindo do gel comercial. Após 20 dias, não foram encontradas diferenças entre os grupos comercial, F + HMC e F + Sn + HMC. O placebo não diferiu do controle em nenhum momento, e ambos os grupos apresentaram a maior PS, comparado aos demais grupos. Para dentina, no 5º dia , F + Sn + HMC, F + HMC e comercial não diferiram significativamente, apresentando menor PS que o grupo controle e placebo. No 10º dia, F+Sn+HMC e comercial apresentaram a menor PS comparado ao grupo controle e placebo. No 20º dia, apenas o gel comercial apresentou PS menor que o controle e o placebo. Assim, o gel experimental F + Sn + HMC foi capaz de controlar a progressão da erosão dentária.
Abstract: This study synthesized and tested experimental gels containing fluoride (F-) and stannous (Sn2+) ions for the control of dental erosion. Enamel and dentin polished specimens were eroded (1% citric acid solution, 10 min) and randomly allocated into 5 groups (n=10): Placebo - Hydroxypropyl Methylcellulose (HMC) gel; F+Sn+HMC - 7,500 ppm F- / 15,000 ppm Sn2+; F+HMC - 7,500 ppm F-; Commercial acidulated phosphate fluoride gel (12,300 ppm F-); and Control - no treatment. After treatment (applied for 60 s), specimens underwent an erosion-remineralization cycling (5 min in 0.3% citric acid solution, 60 min in artificial saliva, 4×/day, 20 days). Surface loss (SL, in µm) was determined after the 5th, 10th and 20th days of cycling (α=0.05). For enamel, after 5 and 10 days, F+Sn+HMC presented the lowest SL, which did not differ from the commercial gel. After 20 days, no differences were found between commercial, F+HMC, and F+Sn+HMC groups. Placebo did not differ from the control at any time points, and both groups presented the highest SL when compared to the other groups. For dentin, on the 5th day, F+Sn+HMC, F+HMC and commercial did not differ significantly, showing lower SL than the control and the placebo. On the 10th day, F+Sn+HMC and commercial presented the lowest SL compared to control and placebo. After 20 days, only the commercial gel showed lower SL than the control and placebo. Thus, the experimental F+Sn+HMC gel was able to control the progression of tooth erosion.
RESUMO
Abstract Objectives To analyze the effect of 5 toothpastes containing different percentages of S-PRG fillers compared to NaF toothpaste and NaF varnish on the dentin hydraulic conductance (Lp). Methodology Dentin disks (1.0±0.2 mm thickness) were cut from third molars, and their Lp values were evaluated using Flodec. The specimens were allocated into 7 groups (n=8). The minimum (smear layer) and the maximum (after acid etching) Lp values were recorded. Lp was also assessed after treatment with either a 0wt.%, 1wt.%, 5wt.%, 20wt.%, or 30wt.% S-PRG toothpaste, a NaF toothpaste, or a NaF varnish. Toothpastes were applied by brushing for 15 s, allowing it to settle for 1 min, and rinsing with deionized water. The NaF varnish was applied for 4 min and was removed with a probe. Specimens were exposed to citric acid (6%, pH 2.1, 1 min) and their final Lp was recorded. The pH of all products was recorded (n=3) and specimens from each group were analyzed by Laser Scanning Confocal Microscopy (LSCM). Data were subjected to 2-way repeated measures ANOVA and post-hoc Bonferroni (a=0.05). Results The highest Lp reduction was noticed for the 5wt.% S-PRG toothpaste, NaF toothpaste, and NaF varnish. However, the toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG were similar to all toothpastes but differed from the NaF varnish. After erosion, all groups retrieved their maximum Lp values, except for the NaF varnish. The LSCM evidenced deposits on the surface of specimens treated with 5%, 20%, and 30% S-PRG-based toothpastes and NaF toothpaste. Even more deposits were observed for the NaF varnish. After the erosive challenge, the deposits were diminished in all groups. Conclusion Toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG fillers behaved similarly to a conventional NaF toothpaste, even after an erosive challenge. The NaF varnish promoted better reduction of the Lp, but its effect was also diminished after erosion.
RESUMO
Objective: The present study compared the effect of whitening mouthrinses (WM) on the color change of stained resin composites (RC). Material and Methods: Cylindrical specimens (6mm-diameter and 1mm-thickness) were prepared with the following RC (n=60/group): Filtek Z350XT (Z350- methacrylate-based), Admira Fusion (AD- ormocer-based), TPH3 (TPH- methacrylate-based), and Beautifil II (BII- giomer/methacrylate-based). The initial color was assessed with reflectance spectrophotometer using CIE L*a*b* system. The specimens were immersed in staining broth during 14 days, submitted to color evaluation (ΔE1) and randomly allocated in 4 subgroups (n=15), according to WM adopted: Listerine Whitening (LW-2% hydrogen peroxide), Plax Whitening (PW-1.5% hydrogen peroxide), Bromelain/papain (BP-experimental solution), and Deionized water (DW-negative control). The whitening cycle consisted of RC immersion in WM for 1 min and in artificial saliva for 30 min, simulating 12 weeks, and final color assessment was performed (ΔE2). Color change data were analysed by ANOVA and Tukey's tests (α=5%). Results: After staining, TPH showed the lowest ΔE1 values and Z350 showed the highest color change (p=0.001). The whitening effect promoted by LW was significantly higher than color alteration obtained with PW (ΔE2), and BII showed the highest color change values (ΔE2) after whitening cycle. Conclusion: LW exhibited the greatest whitening potential on stained RC, mainly with the Giomer (Beautifill II) and the Ormocer-based (Admira Fusion) materials. Bromelain/papain solution showed no whitening effect on stained RC. (AU)
Objetivo: O presente estudo comparou o efeito de enxaguatórios clareadores (EC) na alteração de cor de resinas compostas (RC) previamente manchadas. Material e Métodos: Espécimes cilíndricos (6mm de diâmetro e 1mm de espessura) foram preparados com as seguintes RC (n=60/grupo): Filtek Z350XT (Z350- metacrilato), Admira Fusion (AD- ormocer), TPH3 (TPH- metacrilato), e Beautifil II (BII- giomer/metacrilato). A cor inicial foi mensurada com espectrofotômetro de reflectância utilizando o sistema CIE L*a*b*. Os espécimes foram imersos em um caldo de manchamento durante 14 dias, submetidos a avaliação de cor (ΔE1) e alocados aleatoriamente em 4 subgrupos (n=15), de acordo com EC adotado: Listerine Whitening (LW-peróxido de hidrogênio a 2%), Plax Whitening (PW- peróxido de hidrogênio a 1,5%), Bromelina/papaína (BP-solução experimental), e Água deionizada (AD- controle negativo). O ciclo clareador consistiu na imersão da RC no EC por 1 min e na saliva artificial por 30 min, simulando 12 semanas, e a cor final foi mensurada (ΔE2). Os dados de alteração de cor foram analisados pelos testes ANOVA e Tukey (α=5%). Resultados: Após o manchamento, TPH apresentou o menor valor de ΔE1 e Z350 apresentou a maior alteração de cor (p=0,001). O efeito clareador promovido pelo LW foi significativamente maior que o obtido com o PW (ΔE2) e BII teve a maior alteração de cor (ΔE2) após o ciclo clareador. Conclusão: LW exibiu maior potencial clareador nas RC manchadas. BII apresentou maior alteração de cor em resposta à ação clareadora de ambos enxaguatórios à base de peróxido de hidrogênio testados.(AU)
Assuntos
Resinas Compostas , Clareadores Dentários , Cerâmicas Modificadas Organicamente , Peróxido de HidrogênioRESUMO
Abstract Objective To evaluate the effect of a toothpaste containing calcium silicate/sodium phosphate/fluoride associated or not to the boost serum (BS) against erosive tooth wear (ETW) on enamel and dentin. Methodology Bovine enamel and dentin specimens were subjected to an erosion-abrasion cycling model (1% citric acid - pH 3.6 -2 min / artificial saliva - 60 min, 4×/day, 5 days). Toothbrushing was performed for 15 s (2 min exposed to slurry), 2×/day, with the toothpastes (n=10): control without fluoride (Weleda), Arg/Ca/MFP (Colgate Pro-Relief), Si/PO4/MFP (Regenerate-Unilever), and Si/PO4/MFP/BS (Si/PO4/MFP with dual BS - Advanced Enamel Serum-Unilever). The effect of treatments on the eroded tissues was assessed by surface microhardness in the first day, and surface loss (SL) resulting from ETW was evaluated by profilometry (μm) after three and five days. Additional dentin specimens (n=5/group) were subjected to 20,000 brushing cycles to verify the abrasivity of the toothpastes. Data were subjected to ANOVA and correlation tests (5%). Results For enamel, no difference in microhardness was observed among the treated groups, and similar SL was obtained after 5 days. For dentin, Si/PO4/MFP/BS resulted in higher microhardness values, but none of the groups presented significantly lower SL than the control. There was no significant correlation between SL and abrasiveness. Conclusion The calcium silicate/sodium phosphate toothpaste and serum increased microhardness of eroded dentin, but they did not significantly reduce enamel and dentin loss compared to the non-fluoride control toothpaste. The abrasiveness of the toothpastes could not predict their effect on ETW.
Assuntos
Animais , Bovinos , Cremes Dentais , Fluoretos , Fosfatos , Silicatos , Compostos de Cálcio , Esmalte Dentário , DentinaRESUMO
Objective: To evaluate the efficacy of different fluoride varnishes on white spot lesions (WSL) remineralization. Material and Methods: Polished bovine enamel specimens were obtained (n = 60) and had their initial surface Knoop microhardness (SMH) determined. WSL were created and the SMH was measured again. Then, specimens were allocated into six groups: C Control (without varnish); BF Bifluorid 12 (6% NaF + 6% CaF2); DP Duraphat (5% NaF); PF Profluorid (5% NaF); FP - Fluor Protector (0.2% NaF + 0.9% difluorsilane); CW - Clinpro White Varnish (5% NaF + 5% TCP). After varnishes application, specimens were immersed in artificial saliva for 24 h. Then, pH-cycling was performed for 8 days and SMH was measured. Data were analyzed by one-way ANOVA and Tukey's test. Results: Non-significant differences were observed among the groups at baseline (p = 0.187) and after WSL formation (p = 0.999). After treatments, significant differences were observed among the groups (p = 0.001). Mean % of alteration (SD) and results of Tukey test were: C- 92.40 (12.10)a; PF- 88.66 (10.66)a; FP- 85.90 (14.49)ab; BF- 67.85 (17.86)bc; CW- 66.60 (18.48)c; DP- 58.62 (8.69)c. Conclusion: Bifluorid 12, Clinpro White Varnish, and Duraphat showed higher efficacy than artificial saliva in promoting the remineralization of WSL, nevertheless, none of the treatments were able to recover sound enamel baseline microhardness (AU)
Objetivo: Avaliar a eficácia de diferentes vernizes fluoretados na remineralização de lesões de mancha branca (LMB). Material e métodos: Espécimes de esmalte bovino polido (n = 60) foram submetidos à análise de microdureza superficial Knoop (KMH) inicial. Foram então criadas LMB artificialmente e os espécimes foram alocados em seis grupos: C Controle (sem aplicação de verniz); BF Bifluorid 12 (6% NaF + 6% CaF2); DP Duraphat (5% NaF); PF Profluorid (5% NaF); FP - Fluor Protector (0.2% NaF + 0.9% difluorsilano); CW - Clinpro White Varnish (5% NaF + 5% TCP). Após a aplicação dos vernizes, os espécimes ficaram imersos em saliva artificial por 24h e uma ciclagem de pH foi realizada por 8 dias. Após a ciclagem, KMH final foi realizada. Os dados foram analisados por ANOVA e teste de Tukey (5%). Resultados: Não foi observada diferença significante para os grupos após a KHM inicial (p = 0.187) e após a formação de LMB (p = 0.999). Após os tratamentos, diferenças significativas foram observadas entre os grupos (p = 0.001). Valores de média de % de alteração superficial (desvio-padrão) e resultados do teste de Tukey foram: C- 92.40 (12.10)a; PF- 88.66 (10.66)a; FP- 85.90 (14.49)ab; BF- 67.85 (17.86)bc; CW- 66.60 (18.48)c; DP- 58.62 (8.69)c. Conclusão: Os vernizes Bifluorid 12, Clinpro White Varnish e Duraphat apresentaram maior eficácia na remineralização das LMB quando comparados à saliva artificial, entretanto, nenhum dos produtos testados foi capaz de recuperar os valores iniciais de microdureza. (AU)
Assuntos
Animais , Bovinos , Fluoretos Tópicos , Cárie Dentária , FlúorRESUMO
Introdução: as anemias adquiridas ocasionadas pela deficiência de diversos micronutrientes têm a deficiência de ferro como principal causa. Das causas congênitas, as hemoglobinopatias, doença falciforme e talassemias são as mais prevalentes. Objetivo: identificar a frequência das anemias falciforme, ferropriva e talassemia, no Hemocentro de Maringá, Paraná. Método: trata-se de estudo transversal realizado prospectivamente a partir dos registros de atendimentos de crianças de zero a dez anos de idade incompletos e sua correlação com idade e sexo, de 2017 e 2018. Resultados: no grupo como um todo, observou-se maior número de lactentes (41,67%) e proporção semelhante entre sexos. A anemia ferropriva foi a mais frequente, seguida da beta talassemia minor, da anemia falciforme e do traço falciforme. Analisando a correlação dos tipos de anemia com sexo (Brown-Forsythe test) e idade (Bartlett's test) obteve-se diferença estaticamente significante (p<0,0001) entre essas variáveis e os tipos de anemia. Conclusão: chama atenção o percentual elevado de anemia ferropriva encaminhando para atenção secundária. Sugerem-se outros estudos, que possam elucidar os fatores etiológicos da elevada proporção de casos de anemia ferropriva, principalmente em lactentes, os quais devem receber profilaxia para prevenção desse tipo de anemia.
Introduction: Acquired anemia caused by the deficiency of several micronutrients has iron deficiency as the main cause. Of the congenital causes, hemoglobinopathies, sickle cell disease and thalassemia are the most prevalent. Objective: To identify the frequency of sickle cell anemia, iron deficiency and thalassemia in the Maringá Hemocenter, Paraná. Method: This was a cross-sectional study conducted prospectively from the records of care of children from zero to ten years old and its correlation with age and gender, from 2017 and 2018. Results: in the group as a whole, we observed higher number of infants (41.67%) and similar sex ratio. Iron deficiency anemia was the most frequent, followed by Beta Thalassemia Minor, Sickle Cell Anemia and Sickle Cell Trace. Analyzing the correlation of anemia types with sex (Brown-Forsythe test) and age (Bartlett's test), a statistically significant difference (p <0.0001) was found between these variables and anemia types. Conclusion: the high percentage of iron deficiency anemia calls for secondary attention. Other studies are suggested that may elucidate the etiological factors of the high proportion of iron deficiency anemia cases, especially in infants, who should receive prophylaxis to prevent this type of anemia.
Assuntos
Humanos , Criança , Talassemia , Anemia Ferropriva , Menores de Idade , Anemia FalciformeRESUMO
The aim of this study was to evaluate the effects of ultraviolet artificial aging on color, fluorescence, gloss, and translucency of different composite resins. Seventy-five cylindrical-shaped specimens (6 mm in diameter and 1 mm thick) of four different composites: Admira Fusion (VOCO), TPH3 (DENTSPLY), GrandioSO (VOCO) and Filtek™ Z350 XT (3M/ESPE), were built. Enamel samples obtained from bovine incisors were prepared with the same dimensions and used as a control group. Assessments of color, translucency, fluorescence, and gloss were performed at baseline and after artificial aging. Specimens were immersed in artificial saliva and submitted to artificial aging (UV light for 300h). Data were analyzed using one-way ANOVA and Tukey's post hoc test (=0.05). After aging, all resin composites presented significant alterations, mainly Filtek™ Z350 XT. Fluorescence decreased in all resin composites and enamel. Gloss was reduced in all groups, too, with major rates for TPH3 and GrandioSO, which was similar to the enamel reduction. Translucency did not present a significant difference for the resin composites, although there was a reduction in the enamel. After artificial aging resin composites became darker, less fluorescent, less glossy, and with no alteration in translucency.
O objetivo deste estudo foi avaliar os efeitos do envelhecimento artificial ultravioleta na cor, fluorescência, brilho e translucidez de diferentes resinas compostas. Foram confeccionados setenta e cinco espécimes de forma cilíndrica (6 mm de diâmetro e 1 mm de espessura) de quatro compósitos diferentes: Admira Fusion (VOCO), TPH3 (DENTSPLY), GrandioSO (VOCO) e Filtek ™ Z350 XT (3M / ESPE). As amostras de esmalte obtidas a partir de incisivos bovinos foram preparadas com as mesmas dimensões e utilizadas como grupo controle. As avaliações de cor, translucidez, fluorescência e brilho foram realizadas na primeira leitura e após o envelhecimento artificial. Os espécimes foram imersos em saliva artificial e submetidos ao envelhecimento artificial (luz UV por 300h). Os dados foram analisados usando ANOVA e teste post hoc de Tukey ( = 0,05). Após o envelhecimento, todos os espécimes apresentaram alterações significativas, principalmente para a resina Filtek ™ Z350 XT. A fluorescência diminuiu em todos os materiais e no esmalte. O brilho foi reduzido em todos os grupos, também, com taxas maiores para TPH3 e GrandioSO, que foi semelhante à redução do esmalte. A translucidez não apresentou diferença significativa em todos os materiais testados, embora tenha havido uma redução no esmalte. Após o envelhecimento artificial, os compósitos de resina ficaram mais escuros, menos fluorescentes, menos brilhosos e sem alteração na translucidez.
Assuntos
Dente , Resinas Compostas , Odontologia , Estética Dentária , Cor , Esmalte Dentário , FluorescênciaRESUMO
Abstract INTRODUCTION: Hantavirus cardiopulmonary syndrome (HCPS) is rare in Northeastern Brazil. METHODS: Prospective surveillance was conducted over a two-year period in Alagoas State, Northeastern Brazil. The prevalence of anti-hantavirus N-antigen IgM and IgG in human serum samples was determined by enzyme-linked immunosorbent assay testing. RESULTS: High avidity IgG was found in nine of 476 serum samples tested (from 102 patients with clinical manifestations compatible with HCPS, 124 patients with leptospirosis, and 250 healthy rural workers). CONCLUSIONS: Serologic evidence of past hantavirus infection in residents of Alagoas State indicates that hantaviruses are present in northeastern Brazil, even in areas silent for HCPS.
Assuntos
Humanos , Masculino , Feminino , Lactente , Pré-Escolar , Criança , Adolescente , Adulto , Idoso , Adulto Jovem , Imunoglobulina G/sangue , Infecções por Hantavirus/diagnóstico , Anticorpos Antivirais/sangue , População Rural , Brasil/epidemiologia , Ensaio de Imunoadsorção Enzimática , Vigilância da População , Prevalência , Estudos Prospectivos , Orthohantavírus/imunologia , Infecções por Hantavirus/epidemiologia , Pessoa de Meia-IdadeRESUMO
Introduction:This study serves as a warning to dentists and researchers that dual-cured resin cements may not polymerize completely under some prosthetic crowns. Objective: The aim of this study was to analyse the polymerization degree of dual-cured resin cements under prosthetic barrier, by microhardness test. Material and method: Three cements (Bistite II, RelyX ARC and Variolink II) were light-cured through different barriers, placed between the cement and the light source: G1: without barrier; G2: composite resin (Cesead); G3: Inceram alumina; G4: IPS Empress; G5: Inceram zirconia; G6: tooth fragment. Photopolymerization was carried out using a halogen light unit (650 mW/cm2); microhardness was evaluated using the Microhardness Tester FM 700, under a load of 50gf with a dwell time of 15s, at two evaluation times (30min and 24h). Result: The results were submitted to ANOVA and Tukey tests (5%). Both Inceram alumina and Inceram zirconia ceramic barriers hindered polymerization. Bistite, followed by RelyX and Variolink, exhibited the highest microhardness values (p< 0.05). As the highest values were obtained without a barrier, it was determined that the barrier, followed by the tooth, influenced microhardness. Both Empress and Cesead had the smallest microhardness values but with no statistically significant difference between them. Conclusion: The barrier negatively affected the microhardness of dual-cured resin cements; evaluation time did not affect microhardness values for most of the conditions tested. There is a limited effect of the chemical activator on the polymerization of some dual-cured cements, and their performance is product specific.
Introdução: Este trabalho serve como um alerta para dentistas e pesquisadores, que alguns cimentos resinosos duais podem não polimerizar completamente sob alguns tipos de coroas protéticas. Objetivo: Analisar o grau de polimerização de cimentos resinos duais, sob barreiras protéticas, por teste de microdureza. Material e método: Três cimentos: Bistite II, RelyX ARC e Variolink II, foram fotopolimerizados através da interposição de vários tipos de barreiras, interpostas entre o cimento e a fonte de luz, formando os grupos: G1: sem barreira; G2: Resina composta Cesead; G3: Inceram alumina/Allceram; G4: IPS Empress; G5: Inceram zircônia/Allceram; G6: fragmento dental. Utilizou-se a luz halógena (650 mW/cm2) para fotoativação e a microdureza foi avaliada: 50gf durante 15s (MicrohardnessTester FM 700), em dois períodos (30min e 24h) pós ativação. Os dados foram submetidos à ANOVA e teste de Tukey (5%). As interposições de Inceram alumina e Inceram zircônia resultaram na polimerização deficiente dos cimentos, impossibilitando a realização dos ensaios. Resultado: Para o fator cimento, o Bistite revelou a maior microdureza, seguido do RelyX e do Variolink (p< 0,05). A barreira influenciou a microdureza, sendo que os maiores valores foram obtidos sem barreira, seguida do dente. Empress e Cesead proporcionaram os menores valores de microdureza e não diferiram entre si. Conclusão: A barreira afetou negativamente a microdureza dos cimentos resinosos duais; o período de avaliação não afetou os valores de microdureza para quase todas as condições testadas; existe um fator limitante do ativador químico na polimerização de alguns cimentos resinosos duais, e seu desempenho é dependente do produto.
Assuntos
Cimentos de Resina , Coroas , Polimerização , Análise de Variância , CimentaçãoRESUMO
Abstract It has been reported, in the last decades, a significant decrease in physical activity (PA) levels, with a consequent increase in obesity and metabolic risk factors among youth. The aims of this study were to describe PA levels, the prevalence of overweight/ obesity and metabolic risk factors, and to examine the association between PA and body mass index (BMI) with metabolic risk among Portuguese youth. The sample comprises 212 Portuguese adolescents (12-16 years old). Height and weight were measured. PA was estimated with the Bouchard questionnaire (3 days recall), as well as with the use of a pedometer (used for 5 consecutive days). Metabolic risk factors comprised fasting glucose, triglycerides, HDL-cholesterol, systolic blood pressure and waist circumference. Subjects were classified as normal weight, overweight or obese according to BMI; the maturational status was indirectly estimated with the maturity offset procedure. A continuous metabolic risk score was computed (zMR) and PA values were divided into tertiles. Quisquare test, t-test and ANOVA were used in statistical analyses. SPSS 18.0 and WinPepi softwares were used and p<0.05. A moderate to high prevalence of overweight/obesity and HDL-cholesterol was found, as well as a high prevalence of high blood pressure and low to moderate PA levels among Portuguese youth. The relationship between BMI and zMR showed that obese adolescents have higher zMR when compared to normal weight or overweight adolescents. This finding suggests that increased levels of PA and reduction in the prevalence of overweight/obesity may have a positive role against the development of metabolic risk factors.
Resumo Tem-se verificado, nas últimas décadas, uma redução substancial nos níveis de atividade física (AF), com o consequente aumento da prevalência de sobrepeso/obesidade e fatores de risco metabólico entre jovens. O presente estudo teve por objetivos identificar os níveis de AF e as prevalências de sobrepeso/obesidade e risco metabólico, e associar o índice ponderal com os níveis de AF e risco metabólico em jovens portugueses. A amostra foi composta por 212 jovens portugueses (12-16 anos). Estatura e peso foram mensurados. AF foi estimada a partir do recordatório de 3 dias de Bouchard e pelo uso do pedômetro (durante 5 dias). Os indicadores de risco metabólico considerados foram: glicose, triglicerídeos, HDL-colesterol, tensão arterial sistólica e perímetro da cintura. Os sujeitos foram classificados consoante índice ponderal a partir do índice de massa corporal, enquanto que o estatuto maturacional foi estimado a partir do offset maturacional. Score contínuo de risco metabólico (zRM) foi calculado, e a AF foi dividida em tercis. Os testes estatísticos utilizados foram o Qui-quadrado, teste t independente e ANOVA, as análises foram conduzidas no SPSS 18.0 e WinPepi (p<0,05). Observou-se uma prevalência moderada a elevada de sobrepeso/obesidade e HDL-colesterol, uma elevada prevalência de risco para tensão arterial, e níveis de AF baixos a moderados entre jovens portugueses. A relação entre índice ponderal e zRM mostrou que adolescentes obesos apresentam maior zRM comparativamente aos adolescentes normoponderais ou com sobrepeso. Incrementos nos níveis de AF e redução da prevalência de sobrepeso/obesidade podem ter um papel relevante na redução de fatores de risco metabólico.
Assuntos
Humanos , Masculino , Feminino , Criança , Adolescente , Peso Corporal , Metabolismo/fisiologia , Atividade Motora , Fatores de RiscoRESUMO
Objetivo: Avaliar a resistência de união entre a resina composta e diferentes substratos de esmalte: hígido, esmalte desmineralizado submetido ou não a remineralização, e desmineralizado infiltrado com Icon (DMG). Material e Métodos: 120 dentes bovinos, cujas raízes foram removidas e o esmalte vestibular foi lixado. Os espécimes foram divididos em: Grupo A, controle, (n=24) que recebeu os procedimentos adesivos e restauradores para posterior teste de microtração; Grupo B (n=96), onde os corpos de prova (cdps) permaneceram imersos em solução desmineralizadora para produzir lesões subsuperficiais de cárie artificial, sendo subdividido em 4: B1, cdps somente desmineralizados; B2, cdps imersos em saliva artificial (8 semanas); B3, cdps imersos em solução de fluoreto 0,05% (1 minuto diariamente por 8 semanas); B4, cdps infiltrados com material resinoso (Icon, DMG). Todos os grupos receberam aplicação do sistema adesivo Clearfil S3 Bond Plus (Kuraray) ou Single Bond Universal (3M ESPE), seguida da resina composta Filtek Z 350 XT (3M ESPE). Os espécimes foram submetidos a ciclagem térmica e seccionados em prismas com dimensões aproximadas de 1mm² de base e submetidos ao teste de microtração. Resultados: os dados foram submetidos à ANOVA e ao Teste de Tukey (α= 5%).As médias em Mpa (±desvio padrão) foram: Clearfill S3 Bond Plus: Grupo Controle (17,17±3,52); B1 (11,60±0,74); B2 (6,83±1,87); B3 (8,38±1,59) e B4 (27,00±1,76); Single Bond Universal: Grupo Controle (26,26±3,19); B1 (10,94±2,00); B2 (11,05±1,74); B3 (15,63±1,25) e B4 (22,60±2,29). Conclusão: a superfície infiltrada com Icon não interferiu negativamente na resistência de união da resina composta ao esmalte e os grupos que foram desmineralizados e remineralizados com flúor e saliva artificial apresentaram valores estatisticamente inferiores aos demais.
Objective: To evaluate the bond strength between resin composite and differentenamel substrates: sound enamel; demineralized enamel submitted or not to remineralization; and demineralized enamel infiltrated with an infiltrating resin. Materials and Methods: 120 bovine teeth were selected, the root portion was removed and the enamel finished. Specimens were divided into the following groups:(A) Control (n=24): adhesively treated and restored; (B) (n=96): the samples were immersed in a demineralization solution to create white spot lesions and divided into four subgroups: (B1)demineralized enamel; (B2) samples were stored in artificial saliva (8 weeks); (B3) samples were stored in a 0.05% sodium fluoride solution (1 minday/8 weeks); (B4) samples were treated with an infiltrantresin (Icon, DMG). The groups were treated with one of the following adhesives: Clearfil S3 Bond Plus (Kuraray) or Single Bond Universal (3M ESPE), followed by the resin composite application (Filtek Z 350 XT, 3M ESPE). The specimens were submitted to thermalcycling aging (10,000 ×; 2±5ºC, 50±55ºCand 37°±2°C). The specimens were sectioned into prism shapes with ~1mm² of base and submitted tomicrotensile test. The collected data were submitted to ANOVA and Tukey´s test (α= 5%). Results: The Means (±SD) in MPawere: Clearfill S3 BondPlus: Control (17.17±3.52); B1 (11.60±0.74); B2 (6.83±1.87); B3 (8.38±1.59) and B4 (27.00±1.76);Single Bond Universal: Control (26.26±3.19); B1 (10.94±2.00); B2 (11.05±1.74); B3 (15.63±1.25) and B4 (22.60±2.29). Conclusion: The surfaceinfiltrated withaninfiltrating resin(Icon) did not negatively affect the bond strength between resin composite and enamel. The demineralized and remineralized groups with sodium fluoride and artificial saliva presented statistically lower results when compared to the other groups
Assuntos
Animais , Bovinos , Cárie Dentária , Esmalte DentárioRESUMO
INTRODUÇÃO: O processo de cicatrização é imediato e dinâmico, com o objetivo de restaurar a continuidade anatômica e funcional, e devem existir condições para esse processo, o que inclui um estado nutricional adequado. Dentre as fórmulas de suplementação existentes, as imunomoduladoras têm sido implicadas na melhora do processo cicatricial e das condições clínicas dos pacientes tratados. Foi avaliada a influência da dieta imunomoduladora (Impact®) sobre diferentes variáveis do processo de cicatrização cutânea. MÉTODO: Ratos adultos e nutridos foram divididos aleatoriamente em quatro grupos, a serem suplementados com a dieta em estudo e com a dieta controle. Dois grupos receberam as respectivas dietas apenas pré-operatoriamente e os outros dois grupos as receberam no perioperatório. Os ratos foram submetidos a três tipos de lesões cutâneas. Foram avaliados os seguintes aspectos: evolução dos pesos, evolução das áreas cruentas, tensiometria das feridas incisionais, taxas de reepitelização e parâmetros histológicos. RESULTADOS: Não houve diferença na evolução dos pesos. Houve melhores índices de fechamento de feridas excisionais nos grupos suplementados com Impact®, a partir do quinto dia de pós-operatório (p=0,02). Os grupos suplementados com a dieta em estudo obtiveram melhores resultados em tensiometria (p = 0,03), taxas de reepitelização (0,04), contagem diferencial de células (p<0,001) e quantidade de colágeno total (p<0,001). CONCLUSÕES: A dieta em estudo (Impact®) promove melhores taxas de fechamento de feridas cruentas, reepitelização mais rápida, cicatrizes com maior resistência tênsil e maiores quantidades de colágeno total nas feridas. Não houve diferença em nenhum dos parâmetros analisados em comparação dos grupos suplementados com Impact® pré e perioperatoriamente.
INTRODUCTION: The wound healing process is immediate and dynamic in order to restore anatomical and functional continuity, and there must be conditions for this process, which include a normal nutritional state. Among the existing supplemental formulas, immuno-enhancing diets have been proposed to improve the wound healing process and patients' clinical conditions. The influence of an immunomodulating diet (Impact®) on different variables of the skin healing process was evaluated. METHOD: Healthy adult rats were randomly divided into four groups of diet supplementation or control. Two groups received their diets only pre-operatively while the other two groups received theirs perioperatively. Rats were subjected to three types of skin lesions. We evaluated the following aspects: changes in weight, development of raw areas, tensiometry of incisional wounds, re-epithelialization rates, and histological parameters. RESULTS: There was no difference in weight changes. There was better closing rates of excisional wounds in groups supplemented with Impact® beginning on the fifth day after surgery (p = 0.02). The groups receiving the dietary supplements obtained the best results in tensiometry (p = 0.03), re-epithelialization rates (p = 0.04), differential cell counts (p < 0.001), and total amount of collagen (p < 0.001). CONCLUSIONS: The study diet (Impact®) promoted better closure rates of raw wounds, faster re-epithelialization, scars with a greater tensile strength, and greater amounts of total collagen in wounds. There was no difference in any of the parameters analyzed compared with the groups supplemented with Impact® pre- and perioperatively.
Assuntos
Animais , Ratos , História do Século XXI , Ratos , Cicatrização , Ferimentos e Lesões , Estudo Comparativo , Estudo de Avaliação , Dieta , Ciências da Nutrição , Imunomodulação , Ratos/fisiologia , Ratos/lesões , Cicatrização/imunologia , Ferimentos e Lesões/complicações , Dieta/métodos , Ciências da Nutrição/métodos , Imunomodulação/imunologiaRESUMO
Objective: The aim of this study was to evaluate the influence of glass fiber reinforcement and resin viscosity on the resistance to fracture of adhesive fixed partial prosthesis (AFPP). Materials & Methods: A stainless steel molding was constructed simulating oclusal preparation for AFPP on a maxillary first pre-molar (4 x 4 x 2 mm) and molar (6 x 4 x 2 mm), with a proximal slot (2 x 1 x 4 mm) and with 7 mm of distance between them. These moldings were duplicated in polyurethane (n = 60) and divided into two groups according to the resin viscosity: G - Grandio SO (VOCO) (n = 30) and GHF Grandio SO Heavy flow (VOCO) (n= 30). These groups were subdivided into three subgroups according to the glass fiber reinforcement used (n = 10): Subgroup N without glass fiber reinforcement; Subgroup V GRANDTEC (VOCO); subgroup S everStick C & B (Stick Tech). Four increments divided into 2 layers, 2 in the lower part and 2 in the upper part of the preparations were light-cured according to the manufacturers instructions. A vertical load was applied on the center of the pieces at a speed of 1mm/min. Data were obtained in Kgf and submitted to two-way ANOVA and Tukey test (α = 0.05). Results: ANOVA showed significant differences for glass fiber reinforcement. Subgroup N (24.45 ± 3.60)a was significantly different from subgroup S (32.54 ± 6.94) b and subgroup V (37.18 ± 5.33) c. Conclusion: The glass fibers tested were capable of improving the resistance to fracture of AFPP. GRANDTEC fiber exhibited the greatest values of resistance to fracture and for the resins studied the viscosity did not influence on the resistance to fracture of AFPP.
Objetivo: O objetivo deste estudo foi avaliar a influência do reforço com fibra de vidro e viscosidade da resina na resistência à fratura de prótese parcial fixa adesiva (PPFA). Material e Método: Um molde de aço inoxidável foi confeccionado simulando preparos oclusais para PPFA em primeiro pré-molar superior (4 x 4 x 2 mm) e molar (6 x 4 x 2 mm), com uma caixa proximal (2 x 1 x 4 mm) e 7 mm de distância entre eles. Esses moldes foram duplicados em poliuretano (n = 60) e divididos em dois grupos de acordo com a viscosidade da resina: G Grandio SO (VOCO) (n = 30) e GHF - Grandio SO Heavy flow (VOCO) (n = 30). Estes grupos foram subdivididos em três subgrupos de acordo com o reforço de fibra de vidro utilizado (n = 10): Subgrupo N - sem reforço de fibra de vidro; Subgrupo V - GRANDTEC (VOCO); subgrupo S everStick C & B (Stick Tech). Quatro incrementos divididos em 2 camadas, 2 na parte inferior e 2 na parte superior dos preparos foram fotopolimerizados de acordo com as instruções dos fabricantes. Uma força vertical foi aplicada no centro das peças a uma velocidade de 1 mm/min. Os dados foram obtidos em Kgf e submetidos a ANOVA a 2 fatores e teste de Tukey (α = 0,05). Resultado: A ANOVA mostrou diferenças significativas para reforço de fibra de vidro. Subgrupo N (24,45 ± 3,60) a foi significativamente diferente do subgrupo S (32,54 ± 6,94)b e subgrupo V (37,18 ± 5,33)c. As fibras de vidro testadas foram capazes de melhorar a resistência à fratura de PPFA. Conclusão: A Fibra GRANDTEC apresentou os maiores valores de resistência à fratura e, para as resinas estudadas, a viscosidade não teve influência na resistência à fratura de PPFA.
Assuntos
Resinas Compostas , Prótese Parcial FixaRESUMO
Objective: This study determined whether chewing side preference (CSP) is correlated to chewing side preference during the first chewing cycle (CSP1ºC) in the deciduous, mixed and permanent dentitions. Methods: Three-hundred subjects were divided in 3 groups: Group 1 100 children 3-5 years old, primary dentition; Group 2 100 children 6-12 years old, mixed dentition; Group 3 100 subjects 18-47 years old, permanent dentition. CSP was determined using a method developed by McDonnell et al. Subjects were given a piece of gum and the position of the chewing gum was recorded 7 times as right or left. Subjects were classified as observed preferred chewing side (OPCS) when they performed 5/7, 6/7 or 7/7 strokes on the same side. OPCS corresponded to the CSP. CSP1ºC was determined using a method developed by Hoogmartens and Caubergh (1987). Subjects were given five pieces of gum and five pieces of bread and the position of the chewing gum at first chewing cycle was recorded as right or left. For each subject, an index (I) was performed. Chi-square (X2) and phi correlation (r) tests were used to investigate significant correlations between CSP and CSP1ºC. Results: There was a strong positive and significant correlation between CSP and CSP1ºC for primary dentition (p= 0.000; r = 0.82), for mixed dentition (p = 0.000; r = 0.81) and a very strong positive and significant correlation for permanent dentition (p = 0.000; r = 0.90). Conclusion: CSP can be significantly correlated to CSP1ºC for primary dentition, mixed dentition and permanent dentition, and these are strong positive relationships for primary and mixed dentitions and very strong positive relationship for permanent dentition.
Objetivo: Este estudo determinou se o lado preferencial mastigatório (LPM) é correlacionado com o lado preferencial no primeiro ciclo mastigatório (LP1ºCM) nas dentições decídua, mista e permanente. Métodos: Trezentos indivíduos foram divididos em 3 grupos: Grupo 1 100 crianças de 3-5 anos, dentição primária; Grupo 2 100 crianças de 6-12 anos, dentição mista; Grupo 3 100 indivíduos de 18-47 anos, dentição permanente. O LPM foi determinado usando o método desenvolvido por McDonnell et al. Indivíduos recebiam um pedaço de goma de mascar e, durante a mastigação, foi anotado o lado (esquerdo ou direito) por 7 vezes. Os indivíduos foram classificados como lado preferencial mastigatório observacional (LPMO) quando realizavam 5/7, 6/7 ou 7/7 mordidas do mesmo lado, correspondendo, portando, ao LPM. O LP1ºCM foi determinado usando o método desenvolvido por Hoogmartens e Caubergh. Os indivíduos recebiam 5 pedaços de goma de mascar e 5 pedaços de torrada, e a posição da primeira mordida foi anotada (esquerdo ou direito). Cada indivíduo recebeu um index (I). Os testes Qui-quadrado (X2) e Correlação de Phi (r) foram utilizados para avaliar as correlações significantes entre LPM e LP1ºCM. Resultados: Houve forte e positiva correlação significante entre LPM e LP1ºCM para as dentições decíduas (p = 0,000; r = 0,82), para dentição mista (p = 0,000; r = 0,81) e muito forte e positiva para dentição permanente (p = 0,000; r = 0,90). Conclusão: LPM pode ser significantemente correlacionado com LP1ºCM para todas as dentições, e essas correlações são fortes e positivas para as dentições decídua e mista e muito forte e positiva para a dentição permanente.
Assuntos
Humanos , Pré-Escolar , Criança , Adolescente , Adulto Jovem , Pessoa de Meia-Idade , Dentição Mista , Dentição Permanente , Mastigação , Dente DecíduoRESUMO
Objective: The aim of this study was to compare the bond strength of two self-etching adhesive systems with different types of dentin abrasion. Methods: Thirty two sound human molars were selected and had the dentin surface exposed and flattened. Tooth were randomly divided into four experimental conditions, according with the adhesive system [Clearfil SE Bond (SE) and One-Up Bond F(ONE)] and the type of dentin abrasion [conventional diamond bur (D) and ultrasound diamond bur (CVD)]. The adhesives were applied following manufactures instructions and light cured composite blocks of 4mm height were placed over dentin. After storage in distilled water for 24 h in 37 ºC, serial cuts were made on mesio-distal and buccal-lingual direction, obtaining specimens with stick format, with cross section of 8mm². The microtensile test was performed at a crosshead speed of 0.5 mm/min and load cell of 10kg, until failure. Data were submitted to ANOVA-2-Way followed by Tukey test (5%). Results: The results (MPa) were: D/ SE: 24.06 ± 8.84, D/ONE:15.03 ± 8.61, CVD/SE: 39.90 ± 8.24 and CVD/ONE:15.03 ±8.61. It can be concluded that the adhesive system Clearfil SE Bond showed higher bond strength related with the abrasion with CVD; the type of dentin abrasion interfered on the performance of Clearfil SE Bond but did not influence the One-Up Bond F results
Objetivo: O objetivo desta pesquisa foi comparar a resistência de união de dois sistemas adesivos autocondicionantes com diferentes métodos de preparo da dentina. Métodos: Foram utilizados 32 molares humanos hígidos extraídos, sendo que a superfície dentinária oclusal foi exposta e planificada. Os dentes foram aleatoriamente divididos em quatro diferentes condições experimentais de acordo com o sistema adesivo: Clearfil SE Bond (SE) ou One- Up Bond F (ONE) e com o método de preparo da dentina: ponta diamantada em alta rotação (D) ou ponta diamantada em ultra-som (CVD). Os adesivos foram aplicados de acordo com as recomendações do fabricante e foram confeccionados blocos de 5mm de altura de resina composta fotopolimerizável, pela técnica incremental. Após estocagem em água destilada por 24 h a 37 ºC, foram realizadas secções seriadas no sentido mésio-distal e vestíbulo-lingual, obtendo-se espécimes em forma de palitos, com secção transversal de aproximadamente 0.8 mm2. Os corpos-de-prova foram submetidos ao ensaio de microtração com velocidade de 0.5mm/min e célula de carga de 10kg. Os dados foram submetidos à análise estatística ANOVA e teste de Tukey (5%). Resultados: Os resultados (MPa) foram: D/SE: 24,06 ± 8,84, D/ONE: 15,03 ± 8,61, CVD/SE: 39,90 ± 8,24 e CVD/ONE:15,03 ± 8,61. Concluiu-se que o sistema adesivo Clearfil SE Bond apresentou superioridade significativa de resistência de união em relação ao preparo com ponta CVD; o método de preparo da dentina interferiu no desempenho do Clearfil SE Bond e não influenciou o desempenho do One-Up Bond F
Assuntos
Humanos , Dentina , Adesivos Dentinários , Resistência à TraçãoRESUMO
Objective: The aim of this study was to evaluate the surface roughness of indirect composites after polishing with aluminum oxide (Al2O3) discs. Material and Methods: One-hundred and eighty specimens were confectioned with 6 indirect composites using a prefabricated matrix, resulting in six groups (n-30): Group SO - Solidex, Group SI - Signum, Group SF - Sinfony, Group OP - Opallis; Group RE - Resilab, Group EP - Epricord, Group AD - Adoro. Each group was divided into three subgroups according to the polishing (n-10): Subgroup C (Control) without polishing (polyester strip); Subgroup S polishing with Sof-Lex discs; Subgroup T - polishing with TDV discs. The surface roughness was measured with a profilometer. Results: The results were analyzed by ANOVA and Tukey tests (5%), resulting in p = 0.00. The mean values (±standard-deviation) measured in Ra (µm) for each Group/Subgroup were: RE/C - 0.14 (± 0.14) a; EP/C - 0.18 (± 0.46) ab; SO/C - 0.24 (± 0.22) abc; SF/S - 0.24 (± 0.17) abc; SF/C - 0.26 (± 2.54)abc; SI/C - 0.30 (± 0.34)abcd; SO/T - 0.33(± 0.42) abcd; AD/S - 0.34(± 0.88)abcd; AD/C - 0.37(± 0.60)ab; SI/S - 0.37(± 1.39)bcd; SO/S - 0.43(± 0.26) cd; EP/S 0.44 (± 1.02) cd; RE/S - 0.54(±2.02) de; SI/T - 0.65(± 0.88)ef; RE/T - 0.83 (± 0.54) fg; SF/T - 0.85 (± 0.21) fg; AD/T - 0.88 (± 1.74) fg; EP/T - 0.91(± 0.89) g. Conclusion: It is concluded that polyester strip resulted in significantly lowest surface roughness; polishing with TDV discs resulted in significantly higher surface roughness compared to Sof-Lex discs and that the surface roughness results depend on the composite tested
Objetivo: O objetivo este estudo foi avaliar a rugosidade superficial de resinas compostas indiretas após polimento com discos de óxido de alumínio (Al2O3). Material e Métodos: Foram confeccionados 180 espécimes de 6 resinas compostas indiretas utilizando uma matriz pré-fabricada, resultando em 6 grupos (n - 30): Grupo SO - Solidex, Grupo SI - Signum, Grupo SF - Sinfony, Grupo OP - Opallis; Grupo RE - Resilab, Grupo EP - Epricord, Grupo AD - Adoro. Cada grupo foi dividido em três subgrupos, de acordo com a técnica de polimento: Subgrupo C - não foi realizado polimento (tira de poliéster); Subgrupo S: polimento com discos Sof-Lex; Subgrupo T: polimento com discos TDV. A rugosidade superficial foi mensurada com um rugosímetro. Resultados: Os resultados foram analisados pelos testes estatísticos de ANOVA e Tukey (5%), obtendo-se p = 0,00. Os valores de média (± desvio-padrão) medidos em Ra (μm) para cada Grupo/ Subgrupo foram: RE/C 0,14 (± 0,14) a; EP/C 0,18(± 0,46) ab; SO/C 0,24 (± 0,22)abc; SF/S 0,24 (± 0,17) abc; SF/C 0,26 (± 2,54) abc; SI/C 0,30 (± 0,34) abcd; SO/T 0,33 (± 0,42) abcd; AD/S 0,34 (± 0,88) abcd; AD/C 0,37 (± 0,60) ab; SI/S 0,37(± 1,39) bcd; SO/S 0,43 (± 0,26) cd; EP/S 0,44 (± 1,02) cd; RE/S 0,54 (±2,02)de; SI/T 0,65 (± 0,88) ef; RE/T 0,83 (± 0,54) fg; SF/T 0,85 (± 0,21) fg; AD/T - 0,88 (± 1,74 ) fg; EP/T - 0,91(± 0,89) g. Conclusão: Pode-se concluir que a tira de poliéster resultou na menor rugosidade superficial; o polimento com discos TDV apresentou média significantemente maior de rugosidade em relação ao polimento com discos Sof-Lex e que o resultado de lisura superficial depende da resina composta testada.