RESUMO
Abstract To evaluate the effect of incorporating niobium phosphate bioactive glass (NbG) into commercial etch-and-rinse adhesive systems, with and without silane, on their degree of conversion (DC) (%) and microtensile bond strength (μTBS). The NbG micro-filler was added to two etch-and-rinse adhesive systems: One Step (OS) and Prime & Bond (PB) at 40% concentration. The following groups were formed: control without glass addition OS; addition of unsilanized NbG (OSNbG); addition of silanized NbG (OSNbGS); control without glass PB; addition of unsilanized NbG (PBNbG); addition of silanized NbG (PBNbGS). The DC was determined using total Fourier spectroscopy reflection (FTIR/ATR). For μTBS testing, 48 human third molars (n=8) were restored and sliced to obtain specimens (0.8 mm2) and they were tested at two different time intervals: immediately and after 6 months. The fracture mode was evaluated with a stereoscopic loupe (40×) and by scanning electron microscopy (SEM). The data were subjected to ANOVA and Tukey tests (a=0.05). NbG addition did not compromise the adhesive system DC values (p>0.05). Furthermore, the NbG added to the adhesive systems did not affect μTBS values (p>0.05). Fracture occurred predominantly at the dentin-adhesive interface. NbG bioactive glass did not affect the DC or microtensile bond strength results.
Resumo Avaliar o efeito da incorporação de vidro niobofosfato bioativo (NbG, 40% em peso) em dois sistemas adesivos simplificados convencionais (One Step [OS] e Prime & Bond {PB}) com e sem silano, no grau de conversão (%) e resistência de união (RU) após 6 meses. Os seguintes grupos foram testados: Controle OS: sem adição de partículas; OS e adição de NbG sem silano (OSNbG); OS e adição de partículas silanizadas NbG (OSNbGS); Controle PB: sem adição de partículas; PB e adição de partículas de NbG sem silano (PBNbG); PB e adição de partículas silanizadas NbG (PBNbGS). O grau de conversão (GC) foi determinado utilizando espectroscopia de Fourier (FTIR/ATR). Para RU, 48 terceiros molares humanos (n=8) foram restaurados e cortados para obter corpos-de-prova (0,8 mm2) e, em seguida, testados em dois momentos: imediato e após seis meses. O padrão de fratura foi avaliado com lupa estereoscópica (40×) e microscópio eletrônico de varredura (MEV). Os dados foram submetidos à análise de variância e Tukey (a=0,05). NbG não comprometeu valores de GC dos sistemas adesivos (p>0,05). Além disso, a adição de NbG aos sistemas adesivos não afetou os valores de RU (p>0,05). O padrão de fratura ocorreu predominantemente na interface dentina-adesivo. NbG não afetou os resultados de GC e RU.
Assuntos
Colagem Dentária , Nióbio/química , Fosfatos/química , Resistência à Tração , Cimentos Dentários , Análise do Estresse Dentário , Microscopia Eletrônica de Varredura , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
O propósito de presente estudo foi avaliar a sensibilidade pós-operatória (SPO) após 2 dias, 7 dias, 180 dias e 360 dias, em restaurações de dentes posteriores feitas com resina composta (Z-350, 3M-ESPE) associada a adesivos autocondicionantes. Foram realizadas 60 restaurações em 35 pacientes e os grupos experimentais foram assim delineados: GI= 20 cavidades tratadas com o sistema adesivo de três passos SBMU (3M-ESPE); GII= 20 cavidades tratadas com o sistema autocondicionante de dois passos Adper SE Plus (3M_ESPE); GIII= 20 cavidades tratadas com o sistema autocondicionante de um passo All Bond SE (BISCO). Após 48 horas, 7 dias, 180 dias e 360 dias, os pacientes foram chamados para avaliação da SPO. Inicialmente, o relato do paciente era considerado e classificado de zero a três, de acordo com critérios previamente estabelecidos. Posteriormente, teste clínico com frio era realizado e classificado de zero a dez, de acordo com a escala visual analógica modificada. Os resultados foram analisados pelos testes não paramétricos de Kruskall-Wallis, para comparar os diferentes tratamentos ao longo do tempo; e teste de Friedman, para analisar o comportamento de cada sistema ao longo dos períodos. Os testes estatísticos não mostraram diferenças significativas de SPO para os grupos testados em todos os períodos avaliados. Os resultados mostraram que, nesse caso, a SPO não foi influenciada pelos sistemas autocondicionantes.
Assuntos
Humanos , Adulto Jovem , Dente Pré-Molar , Resinas Compostas , Dentina , Dente Molar , Concentração de Íons de Hidrogênio , Dor , Interpretação Estatística de DadosRESUMO
The present investigation observed the sealing ability of low shrinkage composite resins in large and deep cavities, placed and photocured in one increment. Large, deep cavities (5.0 mm diameter and 2.5 mm deep) surrounded by enamel were prepared in bovine teeth, which were then divided into five groups. Groups 1, 2, 3 and 4: acid conditioning + Adper Single Bond (3M/ESPE, St Paul, MN, USA) and restoration with Aelite LS Posterior (BISCO Inc. Schaumburg, IL, USA) (G1); Filtek Z-350 (3M/ESPE,St Paul, MN, USA) (G2); Filtek Z-350 Flow (3M/ESPE, St Paul, MN, USA) (G3); Premisa (KERR Corporation, Orange, CA, USA) (G4). Group 5: Silorane Adhesive system (3M/ESPE, St Paul, MN, USA) + restoration with Filtek Low Shrinkage Posterior P90 (3M/ESPE, St Paul, MN, USA). After polymerization, the teeth were immersed in 0.5 percent basic fuchsine solution and immediately washed. Using the Imagetool Software, the extent of dye along the margins was calculated as a percentage of total perimeter. The restorations were then transversally sectioned and the depth of dye penetration was calculated in mm, using the same software. Kruskal-Wallis analysis for all groups showed no statistical differences for extent (p = 0.54) or depth (p = 0.8364) of dye penetration. According to this methodology, the so-called low shrinkage composite resins had the same sealing ability compared to regular and flowable nanocomposite materials.
Assuntos
Animais , Bovinos , Resinas Compostas/química , Adaptação Marginal Dentária , Colagem Dentária/métodos , Adesivos Dentinários/química , Preparo da Cavidade Dentária/métodos , Restauração Dentária Permanente/métodos , Teste de Materiais , Polímeros/química , Estatísticas não Paramétricas , Propriedades de Superfície , Fatores de TempoRESUMO
O objetivo deste trabalho clínico foi avaliar a sensibilidade pós-operatória após 2, 7, 180 e 365 dias em restaurações de resina composta realizadas em cavidades amplas e profundas em dentes posteriores empregando-se três sistemas adesivos convencionais atuais (condicionamento ácido total+adesivo). Foram realizados 60 procedimentos restauradores pelo mesmo operador, divididos em três grupos com 20 amostras em cada: SB - ADPER SingleBond 2 (3M ESPE®); AB - All Bond 3 (Bisco®); e XP - XP Bond (Dentsply®). Todas as restaurações foram preenchidas com a resina Z350 (3M ESPE®) e os resultados foram submetidos aos testes de Kruskall Wallis e Friedman. Todos os resultados para sensibilidade pós-operatória foram semelhantes ao longo dos tempos testados.
Assuntos
Humanos , Adulto Jovem , Pessoa de Meia-Idade , Pesquisa Biomédica , Resinas Compostas , Permeabilidade Dentária , Esmalte Dentário , Profilaxia Dentária , Dentina , Mastigação , Nanotecnologia , Período Pós-Operatório , SolventesRESUMO
The present clinical study aimed to assess the postoperative sensitivity (POS) after 48 hours and seven days in occlusal restorations bonded with three different adhesive systems, two of them containing glutaraldehyde. The restorative procedures were performed using the three-step etch-and-rinse Adper SBMP-Plus adhesive (SBMP), the two-step etch-and-rinse Gluma Comfort One Bond + Desensitizer adhesive (GC+D) and the all-in-one self-etching/priming I Bond (IB) adhesive, which also has glutaraldehyde in its formula. All cavities were restored with Filtek Supreme nanoparticle composite resin. After 48 hours and seven days the patients were recalled and the postoperative sensitivity evaluated. The data analyzed by non-parametric Friedman test showed no significant differences in POS among the three tested groups after 48 hours and seven days.
Assuntos
Adolescente , Adulto , Feminino , Humanos , Pessoa de Meia-Idade , Adulto Jovem , Sensibilidade da Dentina/etiologia , Glutaral/uso terapêutico , Complicações Pós-Operatórias , Cimentos de Resina/farmacologia , Resinas Compostas/farmacologia , Restauração Dentária Permanente , Sensibilidade da Dentina/diagnóstico , Medição da Dor , Complicações Pós-Operatórias/diagnóstico , Estatísticas não Paramétricas , Fatores de Tempo , Adulto JovemRESUMO
Os pinos pré-fabricados, cimentados nos condutos radiculares, são utilizados para aumentar a retenção do material de reconstrução e, em associação com a restauração indireta, aumentam a resistência do conjunto. O interior do conduto radicular é particularmente de difícil acesso e visualização. Assim, simplifica o protocolo de cimentação reduz a possibilidade de erros. Os cimentos autoadesivos, em virtude de sua fácil manipulação e aplicação, têm sido propostos para essa finalidade. No entanto, é necessário que a inter-relação desses materiais com a dentina e com o pino seja mais bem estudada e compreendida, bem como os aspectos relacionados à reação de polimerização. Sendo assim, este artigo tem como propósito apresentar informações das caracteristicas desse tipo de cimento, sua relação com a dentina e pino, com base em informações da literatura específica, bem como por meio de imagens obtidas com microscopia eletrônica de varredura (MEV).