RESUMO
Abstract This split-mouth randomized controlled trial aimed to evaluate the primary and secondary stability of hybrid implants with different thread configurations and hydrophilic surfaces. Twenty patients with a partially edentulous maxilla were selected. These patients received two types of implants with the same hydrophilic surface: CTP group: Cylindrical-Tapered implant with perforating threads; CTH: Cylindrical-Tapered implant with hybrid threads configuration (perforating and condensing threads). The primary and secondary stability parameters were measured by insertion torque and resonance frequency analysis at the time of implant placement and 7, 28, 56, and 90 days after the surgical procedure. The paired t-test was used to compare the data on the implant's stability between the groups. The statistical analysis was performed with a confidence level set at 95%. It was found that the implants in the CTH group presented higher primary stability values at the time of implant placement, due to the higher ISQ (63.61 ± 9.44 vs. 40.59 ±7.46) and insertion torque (36.92 ± 16.50 Ncm vs. 28.00 ± 14.40 Ncm), than the implants in the CTP group. The CTH group presented higher ISQ values in all follow-up periods: 7 days (68.67 ± 7.60 vs. 41.55 ± 9.07), 28 days (68.61 ± 5.98 vs. 47.90 ±13.10), 56 days (74.09 ± 3.96 vs. 55.85 ± 13.18), and 90 days (75.45 ± 4.02 vs. 63.47 ± 6.92) after implant placement. Hybrid implants with perforating and condensing threads demonstrated greater stability than hybrid implants with only perforating threads.
Resumo O objetivo deste estudo controlado randomizado de boca dividida foi avaliar a estabilidade primária e secundária de implantes híbridos com diferentes configurações de rosca e superfícies hidrofílicas. Vinte pacientes com maxila parcialmente edêntula foram selecionados. Esses pacientes receberam dois tipos de implantes com a mesma superfície hidrofílica: Grupo CTP: Implante cilíndrico-cônico com roscas perfurantes; Grupo CTH: Implante cilíndrico-cônico com roscas perfurantes e condensadoras. Os parâmetros de estabilidade primária e secundária foram medidos por análise de torque de inserção e frequência de ressonância no momento da colocação do implante e 7, 28, 56 e 90 dias após o procedimento cirúrgico. O teste t-pareado foi utilizado para comparação dos dados de estabilidade entre os grupos. A análise estatística foi executada levando-se em consideração um nível de confiança de 95%. Constatou-se que os implantes do grupo CTH apresentaram maiores valores de estabilidade primária no momento da colocação do implante, devido ao maior ISQ (63.61 ± 9.44 vs. 40.59 ±7.46) e torque de inserção (36.92 ± 16.50 Ncm vs. 28.00 ± 14.40 Ncm), do que os implantes do grupo CTP. Implantes do grupo CTH apresentaram valores de ISQ superiores em todos os períodos de acompanhamento: 7 dias (68.67 ± 7.60 vs. 41.55 ± 9.07), 28 dias (68.61 ± 5.98 vs. 47.90 ±13.10), 56 dias (74.09 ± 3.96 vs. 55.85 ± 13.18) e 90 dias (75.45 ± 4.02 vs. 63.47 ± 6.92). Os implantes híbridos com roscas perfurantes e condensantes demonstraram maior estabilidade do que os implantes híbridos com apenas roscas perfurantes.
RESUMO
Abstract This study evaluated osseointegration in areas grafted with deproteinized bovine bone (DBB) and biphasic ceramic based on hydroxyapatite and beta-tricalcium phosphate (HA/TCP) in rat tibias. Noncritical bone defects were made in the tibias of 28 rats that were randomly assigned to 2 groups: DBB: DBB-filled defects and HA/TCP: HA/TCP-filled defects. Bone defects were made in the tibias bilaterally and filled with biomaterials. After 60 days, the implants were inserted, and the animals were euthanized 15 and 45 days after the implants were installed. Osseointegration was evaluated by biomechanical, microtomographic and histometric analysis. Implants installed in the defects filled with DBB presented higher removal torque forces (2.33 ± 0.51 Ncm vs. 1.50 ± 0.54 Ncm) and mineralized tissue volume around implants at 15 days (34.96 ± 3.68 % vs. 25.61 ± 2.95 %) and greater bone-implant contact (20.87 ± 8.28 % vs. 11.52 ± 7.42 %) and bone area within implant threads (26.83 ± 12.35 % vs. 11.98 ± 7.56 %) at 45 days compared to the measurements of implants in areas grafted with HA/TCP. Implants installed in defects in areas grafted with DBB had a better osseointegration pattern than implants placed in defects in areas grafted with HA/TCP.
Resumo Este estudo avaliou a osseointegração em áreas enxertadas com osso bovino desproteinizado (DBB) e cerâmica bifásica à base de hidroxiapatita e beta-fosfato tricálcico (HA / TCP) em tíbias de ratos. Defeitos ósseos não críticos foram feitos nas tíbias de 28 ratos que foram divididos aleatoriamente em 2 grupos: DBB: defeitos preenchidos com DBB e HA / TCP: defeitos preenchidos com HA / TCP. Defeitos ósseos foram confeccionados nas tíbias bilateralmente e preenchidos com biomateriais. Após 60 dias, os implantes foram instalados e os animais sacrificados 15 e 45 dias após a instalação dos implantes. A osseointegração foi avaliada por análises biomecânica, microtomográfica e histométrica. Os implantes instalados nos defeitos preenchidos com DBB apresentaram maiores forças de torque de remoção (2,33 ± 0,51 Ncm vs. 1,50 ± 0,54 Ncm) e volume de tecido mineralizado ao redor dos implantes aos 15 dias (34,96 ± 3,68% vs. 25,61 ± 2,95%) e maior contato osso-implante (20,87 ± 8,28% vs. 11,52 ± 7,42%) e área de osso dentro das roscas do implante (26,83 ± 12,35% vs. 11,98 ± 7,56%) no período de 45 dias em comparação com os implantes em áreas enxertadas com HA / TCP. Implantes instalados em áreas enxertadas com DBB apresentaram melhor padrão de osseointegração do que implantes colocados em áreas enxertadas com HA / TCP.