RESUMO
ABSTRACT The aim of this study was to evaluate the degree of conversion, cytotoxicity, solubility and pH of photopolymerizable calciumbased cements submitted to preheating. The degree of conversion was analyzed by Fourier transform infrared, cytotoxicity by the MTT test and solubility through loss of mass. The data were subjected to statistical tests (ANOVA / Tukey's, p<0.05). The photopolymerizable materials showed a low degree of conversion, regardless of preheating. All materials caused a reduction in cell viability at 24 hours and 7 days, with the Dycal (control) being more cytotoxic. Heat had a positive effect on Biocal at 7 days. Dycal is the most soluble material. Heat had no effect on the solubility or pH of the polymerizable materials. It is concluded that photopolymerizable calcium-based cements have a low degree of conversion and are soluble, which results in mild to moderate cytotoxicity.
RESUMO O objetivo do presente estudo foi avaliar o grau de conversão, citotoxicidade, solubilidade e pH de cimentos à base de cálcio fotopolimerizáveis submetidos a pré-aquecimento. O grau de conversão foi analisado por espectroscopia no infravermelho com transformada de Fourier, a citotoxicidade pelo teste de MTT e a solubilidade através da perda de massa. Os dados foram submetidos a testes estatísticos (ANOVA/Tukey, p<0,05). Os materiais fotopolimerizáveis apresentaram baixo grau de conversão, independente do pré-aquecimento. Todos os materiais causaram redução da viabilidade celular nas análises de 24 horas e 7 dias, sendo que o Dycal (controle) apresentouse mais citotóxico e o calor apresentou efeito positivo sobre o Biocal na análise de 7 dias. O Dycal é o material mais solúvel e o calor não causou efeito na solubilidade e pH dos materiais polimerizáveis. Assim, conclui-se que os cimentos à base de cálcio fotopolimerizáveis apresentam baixo grau de conversão e são solúveis, que resulta em citotoxicidade suave e moderada.
Assuntos
Humanos , Hidróxido de Cálcio/toxicidade , Sobrevivência Celular/efeitos dos fármacos , Cimentos Dentários/química , Agentes de Capeamento da Polpa Dentária e Pulpectomia/toxicidade , Hidróxido de Cálcio/química , Cálcio , Cimentos Dentários/toxicidade , Capeamento da Polpa Dentária , Cura Luminosa de Adesivos Dentários , Processos Fotoquímicos , Agentes de Capeamento da Polpa Dentária e Pulpectomia/química , Polimerização , Concentração de Íons de HidrogênioRESUMO
Abstract Objectives: To evaluate the effect of calcium hydroxide (CH) associated with two different vehicles as a capping material for pulp tissue in primary molars, compared with mineral trioxide aggregate (MTA). Methodology: Forty-five primary mandibular molars with dental caries were treated by conventional pulpotomy using one of the following materials: MTA only (MTA group), CH with saline (CH+saline group) and CH with polyethylene glycol (CH+PEG group) (15 teeth/group). Clinical and periapical radiographic examinations of the pulpotomized teeth were performed 3, 6, and 12 months after treatment. Data were tested by chi-squared analysis and a multiple comparison post-test. Results: The MTA group showed both clinical and radiographic treatment success in 14/14 teeth (100%), at all follow-up appointments. By clinical evaluation, no teeth in the CH+saline and CH+PEG groups had signs of mobility, fistula, swelling or inflammation of the surrounding gingival tissue. However, in the CH+saline group, radiographic analysis detected internal resorption in up to 9/15 teeth (67%), and inter-radicular bone resorption and furcation radiolucency in up to 5/15 teeth (36%), from 3 to 12 months of follow-up. In the CH+PEG group, 2/11 teeth (18%) had internal resorption and 1/11 teeth (9%) presented bone resorption and furcation radiolucency at all follow-up appointments. Conclusion: CH with PEG performed better than CH with saline as capping material for pulpotomy of primary teeth. However, both combinations yielded clinical and radiographic results inferior to those of MTA alone.
Assuntos
Humanos , Pré-Escolar , Criança , Óxidos/uso terapêutico , Pulpotomia/métodos , Dente Decíduo/cirurgia , Hidróxido de Cálcio/uso terapêutico , Silicatos/uso terapêutico , Compostos de Cálcio/uso terapêutico , Compostos de Alumínio/uso terapêutico , Agentes de Capeamento da Polpa Dentária e Pulpectomia/uso terapêutico , Fatores de Tempo , Dente Decíduo/diagnóstico por imagem , Hidróxido de Cálcio/química , Radiografia Dentária , Estudos Prospectivos , Seguimentos , Resultado do Tratamento , Combinação de Medicamentos , Agentes de Capeamento da Polpa Dentária e Pulpectomia/química , Solução Salina/uso terapêutico , Solução Salina/químicaRESUMO
O desenvolvimento de biomateriais com aplicações na área da saúde mostram-se cada vez mais importantes e a procura por novos polímeros com propriedades bioativas, biodegradabilidade, atoxicidade são o foco das principais pesquisas em diferentes aplicações médicas e odontológicas. Os materiais capeadores pulpares evoluíram rapidamente na ultima década, sendo que são disponibilizadas atualmente diversas alternativas para uso clínico odontológico. Este trabalho teve como objetivo o desenvolvimento de um novo produto bioestimulador e capeador dentino/pulpar que poderá ser base para o desenvolvimento e recobrimento de scaffolds para reparo das diferentes estruturas dentárias. O desenvolvimento das bandagens BBio e os resultados obtidos nos testes das propriedades físico-químicas (absorção de água, perda de massa e pH), bem como as análises biológicas da morfologia celular e viabilidade celular com MTT a BBio apresentaram dados favoráveis e desejáveis para sua aplicação clínica. A propriedade de liberação de cálcio foi bastante promissora, sendo esta uma condição que dará a diferenciação positiva da BBio como um produto bioestimulador pulpar. Com esses dados pode-se concluir que a mesma se encontra dentro dos parâmetros desejados para o produto final e com propriedades semelhantes aos produtos existentes no mercado, de qualidade e aprovados pelas agências reguladoras.(AU)
The development of biomaterials with applications in the health area are increasingly important and the search for new polymers with bioactive properties, biodegradability and toxicity are the focus of the main researches in different medical and dental applications. The pulp capping materials evolved rapidly in the last decade, and several alternatives are now available for clinical dental use. This project aimed to develop a new biostimulating and dentin / pulp capping product that could be the basis for the development and recoating of "scaffolds" for repair of different dental structures. The development of the BBio bandages and the results obtained in the physical-chemical properties tests (water absorption, loss of mass and pH), as well as the biological analyzes of the cellular morphology and cell viability with MTT to BBio presented favorable and desirable data for its clinical application. The calcium release property was quite promising, and this is a condition that will give BBio a positive differentiation as a pulp biostimulator product. With this data it can be concluded that it is within the parameters desired for the final product and with properties similar to the products on the market, of quality and approved by the regulatory agencies.(AU)
Assuntos
Humanos , Materiais Biocompatíveis/química , Polpa Dentária/efeitos dos fármacos , Dentina/efeitos dos fármacos , Agentes de Capeamento da Polpa Dentária e Pulpectomia/química , Análise de Variância , Materiais Biocompatíveis/farmacologia , Materiais Biocompatíveis/normas , Sobrevivência Celular , Quitina/química , Quitosana/química , Fibroblastos/efeitos dos fármacos , Teste de Materiais , Microscopia Eletroquímica de Varredura , Agentes de Capeamento da Polpa Dentária e Pulpectomia/farmacologia , Agentes de Capeamento da Polpa Dentária e Pulpectomia/normas , Reprodutibilidade dos Testes , Fatores de TempoRESUMO
This aim of this study was to evaluate the physicochemical and biological properties of novel experimental cements (Hybrid, Paste and Resin) based on synergistic combinations of existing materials, including pH, diametral tensile strength (DTS) and cytotoxicity comparing them with mineral trioxide aggregate (MTA - Angelus®) and a glass ionomer cement (GIC) developed at our laboratory. For the physicochemical and biological tests, specimens with standard dimensions were produced. pH measurements were performed with digital pH meter at the following time intervals: 3, 24, 48 and 72 h. For the DTS test, cylindrical specimens were subjected to compressive load until fracture. The MTT assay was performed for cytotoxicity evaluation. Data were analyzed by ANOVA and Tukey's test (α=0.05). Paste group showed pH values similar to MTA, and Hybrid group presented pH values similar to GIC (p>0.05). The tested materials showed pH values ranging from alkaline to near neutrality at the evaluated times. MTA and GIC showed similar DTS values. The lowest and highest DTS values were seen in the Paste and Resin groups, respectively (p<0.05). Cell viability for MTA and experimental Hybrid, Paste and Resin groups was 49%, 93%, 90% and 86%, respectively, when compared with the control group. The photo-cured experimental resin cement showed similar or superior performance compared with the current commercial or other tested experimental materials.
O objetivo deste estudo foi avaliar propriedades físico-químicas e biológicas de novos cimentos experimentais (Híbrido, Pasta e Resinoso) baseado na combinação sinérgica de materiais existentes, incluindo pH, resistência à tração diametral (RTD) e citotoxidade, comparando-os ao MTA (Angelus®) e a um cimento de ionômero de vidro (CIV) desenvolvido em nosso laboratório. Para a realização dos testes físico-mecânico e biológico, foram confeccionados espécimes com dimensões padrão. O teste de pH foi realizado por meio de pH-metro digital nos tempos: 3, 24, 48 e 72 h. Para o teste de RTD, espécimes cilíndricos foram submetidos a carga compressiva até sua fratura. Para avaliação da citotoxidade, utilizou-se o teste MTT. Os dados foram analisados utilizando ANOVA e teste de Tukey (α=0,05). O grupo Pasta apresentou valores de pH semelhantes ao MTA, assim como o grupo Híbrido seguiu os parâmetros do CIV (p>0,05). Todos os materiais apresentaram valores de pH alcalinos ou próximosà neutralidade nos tempos avaliados. MTA e CIV apresentaram valores de RTD similares. Os menores e maiores valores observados foram do grupo Pasta e Resinoso, respectivamente (p<0,05). A viabilidade celular para os grupos MTA, Híbrido, Pasta, Resinoso, quando comparados ao grupo controle foi de: 49, 93, 90 e 86%, respectivamente. O cimento experimental Resinoso apresentou desempenho similar ou superior aos materiais comerciais e experimentais avaliados.