RESUMO
Abstract Objectives: This study investigated the physical and mechanical properties, antibacterial effect and biocompatibility of novel elastomeric temporary resin-based filling materials (TFMs) containing zinc methacrylate (ZM). Material and Methods: Experimental TFMs were prepared by mixing the zinc methacrylate with monomer, co-monomer, photoinitiator and fillers. A ZM concentration of 0 (control), 0.5% (Z0.5); 1% (Z1), 2% (Z2), or 5% (ZM5) wt% was added to the TFMs. Fermit-N (F) was used for comparison with the experimental material. Microleakage, water sorption/solubility, degree of conversion, depth of cure, ultimate tensile strength, and hardness were determined and compared. A modified direct contact test (DCT) with Enterococcus faecalis and a Streptococcus mutans' biofilm accumulation assay was carried out to evaluate the antimicrobial effect and cytotoxicity of the assay. Statistical comparisons were performed (α=5%). Results: The results showed that the physical and mechanical properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference and some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values. TFMs with ZM killed E. faecalis only after 1 h. Biofilm development of S. mutans was not affected by the inclusion of ZM in the experimental TFMs. Conclusions: The present findings suggest that the physical, mechanical and biological properties of the experimental TFMs with ZM are comparable with the properties of the commercial reference. However, some properties were improved, such as lower microleakage and water sorption, and higher ultimate tensile strength values.
Assuntos
Animais , Bovinos , Zinco/química , Resinas Compostas/química , Elastômeros/química , Restauração Dentária Temporária/métodos , Metacrilatos/química , Valores de Referência , Solubilidade , Streptococcus mutans/efeitos dos fármacos , Resistência à Tração , Fatores de Tempo , Zinco/farmacologia , Teste de Materiais , Contagem de Colônia Microbiana , Distribuição Aleatória , Reprodutibilidade dos Testes , Enterococcus faecalis/efeitos dos fármacos , Resinas Compostas/farmacologia , Elastômeros/farmacologia , Infiltração Dentária , Testes de Dureza , Metacrilatos/farmacologia , Antibacterianos/farmacologiaRESUMO
ABSTRACT OBJECTIVE: The aim of the present study was to evaluate color changes and force degradation of orthodontic elastomeric ligatures in different stretching patterns during a 8-weeks period. METHODS: Two elastomers with the minimum and two with the maximum color changing, and gray elastomers of two brands (American Orthodontics and Ortho Technology) were selected according to an opinion poll with clinicians and color changes after 4 weeks of intraoral use were evaluated. These elastomers were mounted on special jigs fabricated using a CAD-CAM technique, underwent different stretching patterns and the force was measured in 0, 24 hours, 2, 4 and 8 weeks. During in vivo part of the study, force levels of elastomers were measured after 4 weeks on a material testing machine. Data were analyzed with four-way ANOVA and Tukey post hoc tests. RESULTS: All the elastomers showed color changing but the degree of color stability was significantly different. The mean force degradation was higher in 1-mm stretch groups. After 8 weeks, the average residual force of elastomers was 1.45 ± 0.18 N and the maximum force decay was seen in the elastomers that exhibited the maximum initial force. CONCLUSION: There is significant relationship between the stretching pattern and the amount of residual force of elastomers. Elastomers with higher initial forces exhibited higher percentages of force loss after 8 weeks. It seems that there is a relationship between initial color and color changing of elastomers.
RESUMO OBJETIVO: o objetivo do presente estudo foi avaliar as alterações de cor e a degradação da força de ligaduras elásticas em diferentes padrões de estiramento, durante um período de 8 semanas. MÉTODOS: duas ligaduras elásticas com alteração mínima de cor, duas com alteração máxima de cor e ligaduras elásticas na cor cinza de duas marcas comerciais (American Orthodontics e Ortho Technology) foram selecionadas de acordo com uma pesquisa de opinião com clínicos, e mediante a avaliação das alterações de cor após quatro semanas em uso intrabucal. Essas ligaduras elásticas foram montadas em jigs fabricados por meio da técnica CAD-CAM e foram expostas a diferentes padrões de estiramento, e a força foi medida nos tempos de 0h, 24h; 2, 4 e 8 semanas. Durante a parte in vivo do estudo, os níveis de força das ligaduras elásticas foram medidos após 4 semanas, em uma máquina de teste de materiais. Os dados foram analisados com os testes ANOVA de quatro vias e post-hoc de Turkey. RESULTADOS: todas as ligaduras elásticas mostraram alterações de cor, mas houve diferenças significativas quanto ao grau de estabilidade da cor. A média de degradação da força foi mais alta nos grupos com estiramento a 1 mm. Após 8 semanas, a média da força residual nas ligaduras elásticas foi de 1,45 ± 0,18 N e a maior degradação na força foi observada nas ligaduras elásticas que apresentaram a maior força inicial. CONCLUSÃO: há uma relação significativa entre o padrão de estiramento e a quantidade de força residual nas ligaduras elásticas. As ligaduras elásticas com as maiores forças iniciais exibiram as mais altas porcentagens de degradação da força após 8 semanas. É, também, possível que haja uma relação entre a cor inicial da ligadura elástica e sua alteração de cor.
Assuntos
Humanos , Aparelhos Ortodônticos , Estresse Mecânico , Cor , Elastômeros/química , Polímeros , Resistência à Tração , Fatores de Tempo , Teste de Materiais , Desenho de Aparelho Ortodôntico , Desenho Assistido por Computador , Análise do Estresse Dentário , Elasticidade , Fenômenos MecânicosRESUMO
Abstract The aim of this study was to evaluate deflection forces of orthodontic wires of different alloys engaged into conventional brackets using several ligation types. Stainless steel, conventional superelastic nickel-titanium and thermally activated nickel-titanium archwires tied into conventional brackets by a ring-shaped elastomeric ligature (RSEL), a 8-shaped elastomeric ligature (8SEL) and a metal ligature (ML) were tested. A clinical simulation device was created especially for this study and forces were measured with an Instron Universal Testing Machine. For the testing procedure, the block representing the maxillary right central incisor was moved 0.5 and 1 mm bucco-lingually at a constant speed of 2 mm/min, and the forces released by the wires were recorded, in accordance with the ISO 15841 guidelines. In general, the RSEL showed lighter forces, while 8SEL and ML showed higher values. At the 0.5 mm deflection, the 8SEL presented the greatest force, but at the 1.0 mm deflection the ML had a statistically similar force. Based on our evaluations, to obtain lighter forces, the thermally activated nickel-titanium wire with the RSEL are recommended, while the steel wire with the 8SEL or the ML are recommended when larger forces are desired. The ML exhibited the highest force increase with increased deflections, compared with the elastomeric ligatures.
Assuntos
Fios Ortodônticos , Braquetes Ortodônticos , Desenho de Aparelho Ortodôntico/métodos , Valores de Referência , Aço Inoxidável/química , Titânio/química , Teste de Materiais , Análise de Variância , Fricção , Elastômeros/química , Elasticidade , Níquel/químicaRESUMO
OBJECTIVE: To investigate the effects of different sterilization/disinfection methods on the mechanical properties of orthodontic elastomeric chains. METHODS: Segments of elastomeric chains with 5 links each were sent for sterilization by cobalt 60 (Co60) (20 KGy) gamma ray technology. After the procedure, the elastomeric chains were contaminated with clinical samples of Streptococcus mutans. Subsequently, the elastomeric chains were submitted to sterilization/disinfection tests carried out by means of different methods, forming six study groups, as follows: Group 1 (control - without contamination), Group 2 (70°GL alcohol), Group 3 (autoclave), Group 4 (ultraviolet), Group 5 (peracetic acid) and Group 6 (glutaraldehyde). After sterilization/disinfection, the effectiveness of these methods, by Colony forming units per mL (CFU/mL), and the mechanical properties of the material were assessed. Student's t-test was used to assess the number of CFUs while ANOVA and Tukey's test were used to assess elastic strength. RESULTS: Ultraviolet treatment was not completely effective for sterilization. No loss of mechanical properties occurred with the use of the different sterilization methods (p > 0.05). CONCLUSION: Biological control of elastomeric chains does not affect their mechanical properties. .
OBJETIVO: verificar os efeitos de diferentes métodos de esterilização/desinfecção nas propriedades mecânicas de elásticos ortodônticos em cadeia. MÉTODOS: segmentos de elástico em cadeia com 5 elos cada foram enviados para esterilização em radiação gama com cobalto 60 (20 KGy). Após esterilização, esses foram contaminados com amostras clínicas de Streptococcus mutans. Passado esse período, foram submetidos aos testes de esterilização/desinfecção por diferentes métodos, formando seis grupos de estudo, assim denominados: Grupo 1 (controle - sem ter sido contaminado), Grupo 2 (álcool 70°GL), Grupo 3 (autoclave), Grupo 4 (ultravioleta), Grupo 5 (ácido peracético) e Grupo 6 (glutaraldeído). Após esterilização/desinfecção, avaliou-se a efetividade desses métodos, por meio de contagem de unidades formadoras de colônias por mL (UFC/mL), e as propriedades mecânicas desses materiais. Utilizou-se o teste t de Student para avaliar o número de UFC, além do ANOVA e, posteriormente, do teste de Tukey para avaliação da força. RESULTADOS: verificou-se que o ultravioleta não obteve eficácia total quanto à esterilização. E não ocorreu perda das propriedades mecânicas dos elásticos, com os diferentes métodos de esterilização utilizados (p > 0,05). CONCLUSÃO: o controle biológico de elásticos em cadeia não interfere nas suas propriedades mecânicas. .
Assuntos
Humanos , Aparelhos Ortodônticos/microbiologia , Esterilização/métodos , Elastômeros/química , Materiais Dentários/química , Ácido Peracético/uso terapêutico , Streptococcus mutans/efeitos dos fármacos , Streptococcus mutans/efeitos da radiação , Estresse Mecânico , Fatores de Tempo , Raios Ultravioleta , Teste de Materiais , Desinfecção/métodos , Glutaral/uso terapêutico , Radioisótopos de Cobalto/uso terapêutico , Desinfetantes de Equipamento Odontológico/uso terapêutico , Compostos Radiofarmacêuticos/uso terapêutico , Elastômeros/efeitos da radiação , Materiais Dentários/efeitos da radiação , Etanol/uso terapêutico , Elasticidade , Carga Bacteriana/efeitos dos fármacos , Carga Bacteriana/efeitos da radiação , Raios gama/uso terapêutico , Temperatura AltaRESUMO
INTRODUCTION: Some patients refer to pre-banding orthodontic separation as a painful orthodontic procedure. Low-level laser therapy (LLLT) has been reported to have local analgesic effect. OBJECTIVE: The aim of this single-blind study was to investigate the perception of pain caused by orthodontic elastomeric separators with and without a single LLLT application (6J). METHODS: The sample comprised 79 individuals aged between 13 and 34 years old at orthodontic treatment onset. Elastomeric separators were placed in first maxillary molars at mesial and distal surfaces and kept in place for three days. The volunteers scored pain intensity on a visual analogue scale (VAS) after 6 and 12 hours, and after the first, second and third days. One third of patients received laser applications, whereas another third received placebo applications and the remaining ones were controls. Applications were performed in a split-mouth design. Thus, three groups (laser, placebo and control) were assessed. RESULTS: No differences were found among groups considering pain perception in all periods observed. CONCLUSION: The use of a single-dose of LLLT did not cause significant reduction in orthodontic pain perception. Overall pain perception due to orthodontic separator placement varied widely and was usually mild. .
INTRODUÇÃO: alguns pacientes referem-se à separação ortodôntica pré-bandagem como um procedimento doloroso. Tem sido relatado que a terapia com laser de baixa intensidade (LLLT) produz um efeito analgésico local. OBJETIVO: o objetivo deste estudo simples-cego foi investigar a percepção da dor causada por elásticos ortodônticos separadores, com ou sem uma única aplicação de LLLT (6J). MÉTODOS: a amostra foi composta por 79 indivíduos com 13-34 anos de idade no início do tratamento ortodôntico. Elásticos separadores foram colocados nos molares superiores, nas proximais mesial e distal, e mantidos por três dias. Os voluntários marcaram a intensidade da dor em uma escala visual analógica (EVA) após 6 horas, 12 horas, 1 dia, 2 dias e 3 dias. Um terço dos dentes separados recebeu aplicações de laser; outro terço, aplicações placebo; e os demais foram usados como controle. As aplicações foram realizadas segundo um desenho metodológico de boca dividida. Portanto, foram comparados três grupos: laser, placebo e controle. RESULTADOS: não foram encontradas diferenças entre os grupos, em relação à percepção de dor, em nenhum dos períodos observados. CONCLUSÕES: a utilização da LLLT em dose única não causou redução significativa na dor ortodôntica. Além disso, a percepção geral da dor devida à colocação de separadores ortodônticos variou muito e foi, geralmente, leve. .
Assuntos
Humanos , Adolescente , Adulto , Adulto Jovem , Aparelhos Ortodônticos , Desenho de Aparelho Ortodôntico , Elastômeros/química , Terapia com Luz de Baixa Intensidade/métodos , Percepção da Dor/efeitos da radiação , Placebos , Técnicas de Movimentação Dentária/instrumentação , Medição da Dor/métodos , Método Simples-Cego , Seguimentos , Lasers Semicondutores/uso terapêuticoRESUMO
Objective This paper focused on optimal stress distribution in the mandibular bone surrounding a dental implant and is devoted to the development of a modified Osteoplant® implant type in order to minimize stress concentration in the bone-implant interface. Material and Methods This study investigated 0.4 mm thick layers of two elastomeric stress barriers incorporated into the dental implant using 3-D finite element analysis. Results Overall, this proposed implant provoked lower load transfer in bone-implant interface due to the effect of the elastomers as stress absorbers. The stress level in the bone was reduced between 28% and 42% for three load cases: 75 N, 60 N and 27 N in corono-apical, linguo-buccal and disto-mesial direction, respectively. Conclusion The proposed model provided an acceptable solution for load transfer reduction to the mandible. This investigation also permitted to choose how to incorporate two elastomers into the Osteoplant® implant system. .
Assuntos
Humanos , Implantação Dentária Endóssea , Implantes Dentários , Análise do Estresse Dentário , Elastômeros/química , Modelos Biológicos , Fenômenos Biomecânicos , Força de Mordida , Força Compressiva , Desenho de Equipamento , Análise de Elementos Finitos , Imageamento Tridimensional , Modelos Anatômicos , Valores de Referência , Estresse Mecânico , Resistência à Tração , Suporte de CargaAssuntos
Humanos , Ortodontia/tendências , Fios Ortodônticos , Ortodontia Corretiva/tendências , Aço Inoxidável/química , Estresse Mecânico , Fatores de Tempo , Titânio/química , Extração Dentária , Fenômenos Biomecânicos , Marketing de Serviços de Saúde , Protocolos Clínicos , Braquetes Ortodônticos/classificação , Desenho de Aparelho Ortodôntico , Fricção , Torque , Elastômeros/química , Materiais Dentários/química , Procedimentos de Ancoragem Ortodôntica/instrumentação , Reino Unido , Má Oclusão/terapiaRESUMO
OBJECTIVE: To compare the frictional resistance between self-ligating and conventional brackets tied to different types of wire. MATERIAL AND METHODS : Abzil Kirium Capelozza (Pattern I) and Easy Clip (Roth prescription) incisor brackets were used. An elastomeric ligature or a ligating wire 0.10-in was used to ligate the wire to the Abzil bracket. Three types of orthodontic archwire alloys were assessed: 0.016-in NiTi wire, 0.016 x 0.021-in NiTi wire and 0.019 x 0.025-in steel wire. Ten observations were carried out for each bracket-archwire angulation combination. Brackets were mounted in a special appliance, positioned at 90 degrees in relation to the wire and tested in two angulations. Frictional test was performed in a Universal Testing Machine at 5 mm/min and 10 mm of displacement. The means (MPa) were submitted to ANOVA and Tukey's test set at 5% of significance. The surfaces of wires and brackets were observed at SEM. RESULTS: Steel-tied brackets (16.48 ± 8.31) showed higher means of frictional resistance than elastomeric-tied brackets (4.29 ± 2.16 ) and self-ligating brackets (1.66 ± 1.57) (P < 0.05), which also differed from each other (P < 0.05). As for the type of wire, 0.019 x 0.025-in steel wire (5.67 ± 3.97) showed lower means (P < 0.05) than 0.16-in NiTi wire (8.26 ± 10.92) and 0.016 x 0.021-in NiTi wire (8.51 ± 7.95), which did not differ from each other (P > 0.05). No statistical differences (P > 0.05) were found between zero (7.76 ± 8.46) and five-degree (7.19 ± 7.93) angulations. CONCLUSIONS: Friction was influenced not only by the type of bracket, but also by the ligating systems. Different morphological aspects were observed for the brackets and wires studied .
OBJETIVO: comparar a resistência ao atrito entre braquetes autoligáveis e braquetes convencionais, variando o tipo de fio. MÉTODOS: foram usados braquetes incisivos Abzil Kirium Capelozza e Easy Clip. Uma ligadura elastomérica ou um fio ligável de 0,010" foi usado para ligação do fio no braquete Abzil. Três tipos de ligas de fio ortodôntico foram avaliadas: fio de NiTi de 0,016"; fio de NiTi de 0,016" x 0,022"; e fio de aço de 0,019" x 0,025". Dez observações foram feitas para cada combinação "braquete-fio-inclinação". Os braquetes foram montados em um aparelho especial, posicionados a 90° em relação ao fio, e testados em duas inclinações. O teste de atrito foi realizado na máquina universal de ensaios, a 5mm/min e com 10mm de deslocamento. As médias (em MPa) foram submetidas aos testes ANOVA e de Tukey, a 5% de significância. As superfícies dos fios e dos braquetes foram observadas no MEV. RESULTADOS: o braquete com amarrilhos metálicos (16,48 ± 8,31MPa) apresentou médias mais altas que o braquete com ligaduras elastoméricas (4,29 ± 2,16MPa) e o braquete autoligável (1,66 ± 1,57) (p < 0,05), os quais também diferiram entre si (p < 0,05). Quanto ao tipo do fio, o fio de aço de 0,019" x 0,025" (5,67 ± 3,97MPa) apresentou médias mais baixas (p < 0,05) que os fios de NiTi de 0,016" (8,26 ± 10,92MPa) e de 0,016" x 0,022" (8,51 ± 7,95), os quais não diferiram entre si (p > 0,05). Nenhuma diferença estatística (p > 0,05) foi encontrada entre inclinações de zero (7,76 ± 8,46) e cinco (7,19 ± 7,93) graus. Concluão: o atrito foi influenciado pelo tipo de braquete e sistemas de ligaduras. Diferentes aspectos morfológicos foram observados para os braquetes e fios estudados. .
Assuntos
Humanos , Ligas Dentárias/química , Materiais Dentários/química , Elastômeros/química , Desenho de Aparelho Ortodôntico , Braquetes Ortodônticos , Fios Ortodônticos , Ligas/química , Análise do Estresse Dentário/instrumentação , Fricção , Teste de Materiais , Microscopia Eletrônica de Varredura , Níquel/química , Estresse Mecânico , Propriedades de Superfície , Aço Inoxidável/química , Titânio/químicaRESUMO
Objective: The aim of this article was to assess how intraoral biodegradation influenced the surface characteristics and friction levels of metallic brackets used during 12 and 24 months of orthodontic treatment and also to compare the static friction generated in these brackets with four different methods of the ligation of orthodontic wires. Material and Methods: Seventy premolar brackets as received from the manufacturer and 224 brackets that were used in previous orthodontic treatments were evaluated in this experiment. The surface morphology and the composition of the deposits found in the brackets were evaluated with rugosimetry, scanning electron microscopy, and energy dispersive X-ray spectroscopy. Friction was analyzed by applying tensile tests simulating sliding mechanics with a 0.019x0.025" steel wire. The static friction levels produced by the following ligation methods were evaluated: loosely attached steel ligature around all four bracket wings, steel ligature attached to only two wings, conventional elastomeric ligation around all 4 bracket wings, and non-conventional Slide® elastomeric ligature. Results: The results demonstrated the presence of biodegradation effects such as corrosion pits, plastic deformation, cracks, and material deposits. The main chemical elements found on these deposits were Carbon and Oxygen. The maximum friction produced by each ligation method changed according to the time of intraoral use. The steel ligature loosely attached to all four bracket wings produced the lowest friction levels in the new brackets. The conventional elastic ligatures generated the highest friction levels. The metallic brackets underwent significant degradation during orthodontic treatment, showing an increase in surface roughness and the deposit of chemical elements on the surface. Conclusion: The levels of static friction decreased with use. The non-conventional elastic ligatures were the best alternative to ...
Assuntos
Humanos , Adulto , Análise de Falha de Equipamento/métodos , Fricção , Desenho de Aparelho Ortodôntico , Braquetes Ortodônticos , Fios Ortodônticos , Análise de Variância , Elastômeros/química , Teste de Materiais , Microscopia Eletrônica de Varredura , Espectrometria por Raios X , Aço Inoxidável/química , Estatísticas não Paramétricas , Propriedades de Superfície , Fatores de TempoRESUMO
OBJECTIVE: The aim of this study was to assess pain, masticatory performance and swallowing threshold of patients undergoing orthodontic treatment. METHODS: Ten patients of both genders (mean age of 17.25 ± 5.21 years), with complete permanent dentition, who underwent orthodontic treatment with fixed appliances were evaluated. The masticatory performance and the swallowing threshold were assessed by patient's individual capacity of fragmenting an artificial test food (Optocal) which was chewed and had the resulting particles processed by a standardized sieving method, presenting the median particle size (MPS) of crushed units. The intensity of pain / discomfort during chewing was evaluated by means of a visual analog scale. All tests were performed at the following times: T0 - before activating the orthodontic appliance; T1 - 24 hours after activation, and T2 - 30 days after activation. RESULTS: The results showed a significant increase in pain at T1 (T0 - 0.60 ± 0.70 mm; T1 - 66.2 ± 34.5 mm), returning to baseline values at T2 (3.20 ± 3.82 mm). Masticatory performance was also reduced in T1 (MPS 10.15 ± 1.1 mm²) in comparison to T0 (MPS 7.01 ± 2.9 mm²) and T2 (MPS 6.76 ± 1.3 mm²). However, particle size was not affected in the swallowing threshold test (T0 - 5.47 ± 2.37 mm²; T1 - 6.19 ± 2.05 mm²; T2 - 5.94 ± 2.36 mm²). CONCLUSION: The orthodontic appliances did not interfere in the size of the particles that would be swallowed, even in the presence of pain.
OBJETIVO: o objetivo desse estudo foi avaliar a dor, a performance mastigatória e o limiar de deglutição em pacientes submetidos ao tratamento ortodôntico. MÉTODOS: foram avaliados dez pacientes de ambos os sexos (idade média 17,25 ± 5,21 anos), com dentição permanente completa, submetidos ao tratamento ortodôntico com aparelhos fixos. A performance mastigatória e o limiar de deglutição foram avaliados pela capacidade individual de fragmentação de um alimento teste artificial (Optocal), o qual foi mastigado e as partículas resultantes processadas por um método padronizado com peneiras, apresentando o tamanho mediano das partículas (TMP) das unidades trituradas. A intensidade da dor/desconforto foi avaliada com o uso de uma escala analógica visual. Todos os testes foram realizados nos seguintes momentos: T0: antes da ativação do aparelho ortodôntico; T1: 24 após a ativação, e T2: 30 dias após a ativação. RESULTADOS: os resultados demonstraram um aumento significativo na dor em T1 (T0: 0,60 ± 0,70mm; T1: 66,2 ± 34,5mm), retornando aos valores basais em T2 (3,20 ± 3,82mm). A performance mastigatória também foi reduzida em T1 (TMP: 10,15 ± 1,1mm²) comparada a T0 (TMP: 7,01 ± 2,9mm²) e T2 (TMP = 6,76 ± 1,3 mm²). Entretanto, o tamanho das partículas não foi afetado no teste do limiar de deglutição (T0: 5,47 ± 2,37mm²; T1: 6,19 ± 2,05mm²; T2: 5,94 ± 2,36mm²). CONCLUSÃO: os aparelhos ortodônticos não interferiram no tamanho das partículas que seriam deglutidas, mesmo na presença da dor.
Assuntos
Adolescente , Feminino , Humanos , Masculino , Deglutição/fisiologia , Mastigação/fisiologia , Aparelhos Ortodônticos , Medição da Dor , Ligas Dentárias/química , Elastômeros/química , Seguimentos , Níquel/química , Fios Ortodônticos , Tamanho da Partícula , Dor/fisiopatologia , Limiar Sensorial/fisiologia , Aço Inoxidável/química , Fatores de Tempo , Titânio/químicaRESUMO
Objective Disinfection procedures often cause deterioration in a maxillofacial prosthesis. Color and hardness alterations could lead to a replacement of the prosthesis. Material and Methods An experimental chlorinated polyethylene (CPE) and a commercial polydimethyl siloxane (PDMS) sample were treated with four different disinfection procedures for a period which simulates 1 year of clinical service. The applied disinfection procedures included microwave exposure and immersion in three solutions, sodium hypochlorite, neutral soap and a commercial disinfecting soap. Shore A hardness (∆H) and color differences (∆E) were determined before and after each procedure. All data were analyzed by Two Way Analysis of Variance (ANOVA) and Tukey's post hoc tests at a level of α=0.05. Results The samples presented significant alterations in color and hardness after the different disinfection treatments. The color differences (∆E) were at least eye detectable in all cases and clinically unacceptable in most of the cases, with values ranging from 1.51 to 4.15 and from 1.54 to 5.92 for the PDMS and CPE material, respectively. Hardness was decreased after all the disinfection procedures in the PDMS, while for the CPE, a decrement was observed after disinfection with sodium hypochlorite and neutral soap and an increment after microwave exposure and the disinfection with a commercial antimicrobial agent. The PDMS samples presented greater alterations in color and hardness after disinfection with sodium hypochlorite solution, while the microwave exposure caused negligible effects. The CPE samples were affected most after disinfection when treated with neutral soap, and more slightly when disinfected with sodium hypochlorite solution. Conclusions The disinfection procedures caused alterations in color and hardness of the examined materials. The most suitable disinfection procedure for ...
Assuntos
Humanos , Desinfetantes/química , Desinfecção/métodos , Elastômeros/química , Pigmentação em Prótese , Análise de Variância , Cor , Dimetilpolisiloxanos/química , Testes de Dureza , Teste de Materiais , Micro-Ondas , Polietileno/química , Estatísticas não Paramétricas , Sabões/química , Hipoclorito de Sódio/química , Fatores de TempoRESUMO
OBJECTIVE: The purpose of this laboratory study was to evaluate changes in the pigmentation of esthetic elastomeric ligatures after immersion in a staining solution. METHODS: Sixty ligatures were selected and divided into 12 groups according to their brand and also considering their condition, i.e., unstretched or stretched. The groups were divided into: Morelli (clear), TP Orthodontics (clear), American Orthodontics (clear), 3M/Unitek (clear), American Orthodontics (pearl color) and 3M/Unitek (pearl color), separated into groups of 5 unstretched and five stretched ligatures. Assessment of their color changes was performed by means of digital photograph and computer analysis using Adobe Photoshop. Standardized digital photographs were taken at T0 (before the staining process, with unstretched ligatures) and at T1 (following the 5-days staining process). The staining solution was composed of artificial saliva and foods with staining potential. At T1 the ligatures were either stretched or unstretched. RESULTS: The results of this study showed that esthetic elastomeric ligatures are prone to staining. Among the evaluated brands, TP Orthodontics and American Orthodontics clear ligatures were the most stable. Moreover, 3M/Unitek pearl ligatures demonstrated statistically significant changes in all variables. CONCLUSIONS: Esthetic elastomeric ligatures are susceptible to staining and no statistically significant difference was found between unstretched or stretched ligatures, with the sole exception of the TP Orthodontics brand. The 3M/Unitek's pearl color ligatures displayed the greatest staining potential.
OBJETIVO: avaliar alterações da pigmentação de ligaduras elásticas estéticas após imersão em solução de pigmentação. MÉTODOS: Sessenta ligaduras foram selecionadas e divididas em doze grupos de acordo com a marca comercial utilizada e nas condições normal e distendida. Os grupos foram divididos em: Morelli transparente, TP Orthodontics transparente, American Orthodontics transparente, Unitek/3M transparente, American Orthodontics pérola e Unitek/3M pérola, separados quanto à condição normal e distendida, totalizando 5 ligaduras em cada condição. A avaliação das mudanças de coloração foi realizada por meio de fotografia digital e análise computadorizada usando o programa Adobe Photoshop. Foram realizadas fotografias digitais padronizadas nos tempos T0 - antes do processo de pigmentação, com as ligaduras em estado normal; e T1 - após o processo de pigmentação, que durou cinco dias. A solução de pigmentação utilizada foi composta por saliva artificial e por alimentos que possuem potencial de coloração. No tempo T1, as ligaduras se encontravam em estado distendido e em estado normal (sem distensão). RESULTADO: os resultados do presente estudo demonstraram que ligaduras elásticas estéticas são suscetíveis à pigmentação. Dentre as marcas comerciais avaliadas a TP Orthodontics e American Orthodontics transparente foram as mais estáveis. Já a Unitek/3M pérola demonstrou alterações estatisticamente significativas em todas as variáveis avaliadas. CONCLUSÃO: ligaduras elásticas estéticas são suscetíveis à pigmentação, não havendo diferença estatisticamente significativa entre o estado normal e o estado distendido, com exceção na marca TP Orthodontics. A marca Unitek/3M pérola demonstrou ser a que apresenta maior potencial para pigmentação.
Assuntos
Cor/normas , Elastômeros/química , Aparelhos Ortodônticos , Pigmentos Biológicos , Análise de Variância , Teste de Materiais , Fotografação/instrumentação , Fotografação/métodos , Saliva Artificial , SoftwareRESUMO
OBJECTIVE: To analyze the in vitro force degradation of four different brands of elastomeric chains: American Orthodontics, Morelli, Ormco and TP Orthodontics. METHODS: The sample consisted of 80 gray elastomeric chains that were divided into four groups according to their respective manufacturers. Chain stretching was standardized at 21 mm with initial force release ranging from 300 g to 370 g. The samples were kept in artificial saliva at a constant temperature of 37°C and the degradation force was recorded at the following time intervals: initial, 1, 3, 5, 7 and 9 hours, and 1, 7, 14, 21, 28, and 35 days. RESULTS: There was a statistically significant difference between the groups regarding the force degradation, mainly within the first day, as a force loss of 50-55% was observed during that time in relation to the initial force. The force delivered at 35 days ranged from 122 g to 148 g. CONCLUSION: All groups showed force degradation over time, regardless of their trademarks, a force loss of 59-69% was observed in the first hour compared to baseline. However, because the variation in force degradation depends on the trademark, studies such as the present one are important for guiding the clinical use of these materials.
OBJETIVO: analisar, in vitro, a degradação de força, ao longo do tempo, de elastômeros das marcas comerciais American Orthodontics, Morelli, Ormco e TP Orthodontics. MÉTODOS: a amostra constituiu-se de 80 segmentos de elastômeros em cadeia fechada na cor cinza, divididos em quatro grupos, conforme o fabricante. A distensão foi padronizada em 21mm, com liberação de força inicial variando de 300 a 370g de força. As amostras foram mantidas em saliva artificial em temperatura constante de 37ºC, e a força avaliada nos seguintes intervalos: inicial, 1h, 3h, 5h, 7h, 9h, 1 dia, 7 dias, 14 dias, 21 dias, 28 dias e 35 dias. RESULTADOS: houve diferença estatisticamente significativa na degradação de força entre os grupos avaliados, sendo que no primeiro dia houve perda de 50 a 55% em relação à força inicial. Os valores médios de força em 35 dias variaram de 122 a 148g. CONCLUSÃO: todas as marcas comerciais apresentaram degradação de força ao longo do tempo, sendo que na primeira hora a perda de força esteve entre 59 e 69% da força inicial. Porém, como existe variação dessa degradação dependendo da marca comercial, estudos como esses são importantes para orientação do uso desses elastômeros.
Assuntos
Elastômeros/química , Teste de Materiais/métodos , Ortodontia Corretiva/instrumentação , Poliuretanos/química , Análise de Variância , Saliva Artificial , Estresse Mecânico , Resistência à TraçãoRESUMO
Aim of the study: The aim of this study was to consider friction in buccal segment attachments during overjet reduction by means of sliding mechanics. Friction was compared in Stainless Steel, Titanium and Cobalt Chromium brackets, using Stainless Steel and Beta Titanium wires. Materials and Methods: This in-vitro study comprised 18 samples (6 x 3 brackets of different materials-stainless steel, titanium and cobalt chromium). Each jig comprised of a buccal segment model of two premolar brackets and a molar tube simulating the upper posterior buccal segment. Each jig was coupled with the wire of 0.019 x 0.025 inch dimension and was tested with a Universal Testing Machine. Ligation was achieved using low friction elastomeric modules (Slide TM , Leone, Italy), a non-conventional elastomeric module. Results: All three bracket systems showed significantly higher frictional forces for the beta titanium wire than for the stainless steel wire. When coupled with the stainless steel wire, the titanium bracket showed the least friction, followed by stainless steel and cobalt chromium brackets. When coupled with the beta titanium wire, the titanium brackets again showed the least friction; while the difference in frictional levels between the stainless steel and cobalt chromium brackets was not statistically significant. The titanium brackets showed the least friction among all the groups tested for both wires. Conclusion: Titanium bracket with Beta Titanium wires could and probably should be the alternative metal bracket used in the nickel sensitive patient.
Assuntos
Dente Pré-Molar , Ligas de Cromo/química , Ligas Dentárias/química , Materiais Dentários/química , Análise do Estresse Dentário/instrumentação , Elastômeros/química , Fricção , Humanos , Teste de Materiais , Dente Molar , Braquetes Ortodônticos , Fios Ortodônticos , Aço Inoxidável/química , Estresse Mecânico , Titânio/química , Técnicas de Movimentação Dentária/instrumentação , TorqueRESUMO
The hypothesis tested in this study was that intraoral exposure of elastomeric chains alters their tensile strength. For such purpose, it was evaluated the in situ behavior of different elastomeric chains stretched for 3 weeks. Three kinds of elastomeric chains, Plastic chain (PC), Memory chain (MC) and Super slick chain (SSC), were randomly placed in 3 quadrants of 13 patient in a fixed distance of 16 mm and mean initial force of 180 g. Tensile testing was performed in an universal testing machine at different intervals: initial, 1 h, 24 h, 1 week, 2 weeks and 3 weeks. A two-way ANOVA test was performed to identify the influence of both material and time on the force decrease. A subsequent one-way ANOVAtest with the Tukey's post hoc test was used to identify statistically significant intragroup and intergroup remaining force (g and %) differences at 5% significance level. The effect of both the material and the time factors were significant. All groups showed significant force decrease after the 1-h period (23% for PC and 14% for MC and SSC). At the end of the 3-week period, the remaining force was 57% (96 g), 67% (129 g) and 71% (125 g) for PC, MC and SSC, respectively. In conclusion, intraoral exposure of elastomeric chains altered their tensile strength. In general, the greater force decrease occurred within the first hour. The remaining force of the enhanced chains measured at each time interval was greater than the conventional one (PC). After 3 weeks, only the enhanced chains maintained the force applied over 100 g.
A hipótese testada foi que a exposição dos elásticos em cadeia ao meio bucal altera sua força de tensão. Portanto, o objetivo deste estudo foi avaliar o comportamento, in situ, de diferentes cadeias elastoméricas quando tensionadas durante 3 semanas. Três tipos de elásticos em cadeia Plastic Chain (PC), Memory Chain (MC) e Super Slick Chain (SSC) foram inseridos aleatoriamente em 3 dos quadrantes de 13 pacientes com distância fixa de 16 mm e força inicial de 180 g. Foi realizado ensaio de tração em uma máquina de ensaio universal EMIC nos seguintes intervalos: inicial, 1 h, 24 h, 1 semana, 2 semanas e 3 semanas. O teste ANOVA a dois critérios foi aplicado para verificar a influência do material e do tempo na degradação da força. Subsequentemente, foi utilizado o teste ANOVA a um critério e pós-teste de Tukey para identificar diferenças estatísticas (p<0,05), intra-grupo e inter-grupo, na força remanescente (g e %). Tanto o material quanto o tempo tiveram efeito significativo na degradação da força. Todos os grupos mostraram diminuição significativa da força depois de 1 h sob tensão (23% para o PC e 14% para o MC e SSC). Ao final do período de 3 semanas, a força remanescente foi de 57% (96 g), 67% (129 g) e 71% (125 g) para o PC, MC e SSC, respectivamente. A exposição dos elásticos em cadeia ao meio bucal alterou a força de tensão. No geral, a maior diminuição da força ocorreu na primeira hora. A força remanescente testada em cada intervalo foi maior para os elásticos reforçados (MC e SSC) do que para o elástico convencional (PC). Após 3 semanas, apenas os elásticos reforçados mantiveram a força acima de 100 g.
Assuntos
Humanos , Materiais Dentários/química , Elastômeros/química , Aparelhos Ortodônticos , Análise do Estresse Dentário/instrumentação , Elasticidade , Teste de Materiais , Desenho de Aparelho Ortodôntico , Fechamento de Espaço Ortodôntico/instrumentação , Plásticos/química , Estresse Mecânico , Resistência à Tração , Fatores de Tempo , Técnicas de Movimentação Dentária/instrumentaçãoRESUMO
El objetivo del trabajo fue evaluar la estabilidad dimensional lineal de diferentes elastómeros para impresión. Se confeccionó una matriz metálica con sus correspondientes cubetas individuales realizadas con láminas termoplásticas (Marca Sabilex, de 0.125 mm de espesor). Se tomaron tres impresiones con cada material a estamatriz. Se utilizaron tres siliconas por adición: Examix-GC- (AdEx), Aquasil-Dentsply-(AdAq), y Panasil Kettenbach-(AdPa); y tres siliconas por condensación: Densell-Dental Medrano-(CoDe), Speedex-Coltene-(CoSp), y Lastic-Kettenbach-(CoLa). Se realizaron todas las impresiones utilizando dos consistencias: pesada y liviana, con la técnica de un solo tiempo. Luego se tomaron fotografías estandarizadas a diferentes intervalos de tiempo (0, 15,30, 60, 120 minutos; 24 horas; 7 días y 14 días), con una cámara fotográfica digital, utilizando un dispositivo ad-hoc. Las imágenes se analizaron con software de procesamiento de imágenes (Image Tool) realizando la medición de la distancia entre las interseccionesde surcos previamente realizados en la porción superior de la matriz. Los resultados obtenidos fueron analizados mediante Análisis de varianza para mediciones repetidas. La media y el DSinicial y final para todos los materiales fue: AdEx: 1,32 (0,01) y 1,31 (0,00); AdAq: 1,32 (0,00) y 1,32 (0,00); AdPa: 1,327 (0,006) y 1,31 (0,00); CoDe: 1,32 (0,00) y 1,32 (0,01); CoSp: 1,327 (0,006) y 1,31 (0,00); CoLa: 1,327 (0,006) y 1,303 (0,006). La evaluaciónestadística mostró el efecto significativo de las variables material y tiempo. Conclusión: Bajo las condiciones de este estudio podemos concluir que el tiempo afectaría significativamente la estabilidad dimensional lineal de elastómeros para impresiones.
Assuntos
Elastômeros/química , Materiais para Moldagem Odontológica/classificação , Fenômenos Químicos , Técnica de Moldagem Odontológica , Interpretação Estatística de Dados , Fatores de TempoRESUMO
The aim of this study was to determine quantitatively and qualitatively the inorganic particle fraction of commercially available dental elastomers. The inorganic volumetric fraction of two addition silicones (Reprosil Putty/Fluid and Flexitime Easy Putty/Fluid), three condensation silicones (Clonage Putty/Fluid, Optosil Confort/Xantopren VL and Silon APS Putty/Fluid), one polyether (Impregum Soft Light Body) and one polysulfide (Permlastic Light Body) was accessed by weighing a previously determined mass of each material in water before and after burning samples at 600ºC, during 3 h. Unsettled material samples were soaked in acetone and chloroform for removal of tthe organic portion. The remaining filler particles were sputter-coated with gold evaluation of their morphology and size, under scanning electron microscopy (SEM). Flexitime Easy Putty was the material with the highest results for volumetric particle fraction, while Impregum Soft had the lowest values. Silon 2 APS Fluid presented the lowest mean filler size values, while Clonage Putty had the highest values. SEM micrographs of the inorganic particles showed several morphologies - lathe-cut, spherical, spherical-like, sticks, and sticks mixed to lathe-cut powder. The results of this study revealed differences in particle characteristics among the elastometic materials that could lead to different results when testing mechanical properties.
O objetivo desse estudo foi determinar quantitativamente e qualitativamente a fração de partículas inorgânicas de elastômeros dentais disponíveis comercialmente. A fração volumétrica de dois silicones por adição (Reprosil Denso/Fluído e Flexitime Denso/Fluído), três silicones por condensação (Clonage Denso/Fluído, Optosil/Xantopren, e Silon 2 APS Denso/Fluído), um poliéter (Impregum Soft Light) e um polissulfeto (Permlastic Light Body) foi determinada pela pesagem prévia de uma determinada massa de cada material em água antes e após a queima das amostras a 600ºC, por 3 h. Amostras de material não polimerizado foram imersas em acetona e clorofórmio para a remoção da parte orgânica. As partículas de carga remanescentes foram cobertas com uma camada de ouro para avaliação da sua morfologia e tamanho, em microscopia eletrônica de varredura. O material Flexitime Denso foi o material com maior fração volumétrica de partículas de carga, enquanto que o Impregum teve menor fração volumétrica. Silon 2 APS Fluído apresentou partículas de carga de menor tamanho, enquanto que o Clonage Denso apresentou as maiores partículas. A observação em MEV. mostrou partículas de carga com vários tipos de morfologia (esféricas, irregulares, semi-esféricas, retangulares e mistura de retangulares/irregulares). Os resultados desse estudo mostraram diferenças nas partículas de carga dos materiais, as quais podem levar a diferentes resultados em suas propriedades mecânicas.
Assuntos
Análise do Estresse Dentário , Materiais para Moldagem Odontológica/química , Elastômeros/química , Compostos Inorgânicos/análise , Teste de Materiais , Microscopia Eletrônica de Varredura , Tamanho da Partícula , Polivinil , Resinas Sintéticas/química , Espectrometria por Raios X , Siloxanas/química , Sulfetos/química , ViscosidadeRESUMO
The purpose of this study was to evaluate the accuracy of the respective dies after polyether elastomeric procedure in the presence or absence of cervical contact of the acrylic resin shell with the cervical region, establishing a comparison to dies obtained with stock trays. This study consisted of three groups with 10 specimens each: 1) acrylic copings without cervical contact, (cn); 2) acrylic copings with cervical contact (cc); 3) perforated stock tray, (st). The accuracy of the resulting dies was verified with the aid of a master crown, precisely fit to the master steel die. ANOVA test found statistically significant differences among groups (p<0.001). Tukey's test found that the smallest discrepancy occurred in group cn, followed by cc, while the st group presented the highest difference (cc x cn: p=0.007; st x cn: p<0.001; st x cc: p<0.001).
Assuntos
Humanos , Resinas Acrílicas/química , Coroas , Sulfato de Cálcio/química , Dente Suporte , Modelos Dentários , Planejamento de Prótese Dentária , Reembasamento de Dentadura , Materiais para Moldagem Odontológica/química , Materiais Dentários/química , Elastômeros/química , Ligas de Cromo/química , Técnica de Moldagem Odontológica/instrumentação , Teste de Materiais , Metilmetacrilatos/química , Resinas Sintéticas/química , Propriedades de Superfície , Aço Inoxidável/química , Preparo Prostodôntico do Dente/classificaçãoRESUMO
This in vivo experimental study evaluated the efficacy of fluoride-releasing elastomers in the control of Streptococcus mutans levels in the oral cavity. Forty orthodontic patients were recruited and divided into two groups of 20. Fluoride-releasing elastomeric ligature ties (Fluor-I-Ties, Ortho Arch Co. Inc., USA) were used in the experimental group, and conventional elastomeric ligature ties (D. Morelli, Brazil), in the control group. Two initial samples of saliva were collected at a 14-day interval to determine the number of colony forming units (CFU) of Streptococcus mutans. Immediately after collecting the second sample, fluoride-releasing elastomeric ligature ties were placed in the patients of the experimental group, and conventional ligature ties, in the patients of the control group. Seven, 14 and 28 days after placement of the elastomeric ligature ties, saliva and plaque surrounding the orthodontic appliance were collected for microbiologic analysis. There were no significant differences in the number of Streptococcus mutans CFUs in saliva or plaque in the area surrounding the fluoride-releasing or conventional elastomeric ligature ties. Thus, fluoride-releasing elastomeric ligature ties should not be indicated to reduce the incidence of enamel decalcification in orthodontic patients. Since there was no significant reduction in S. mutans in saliva or plaque, other means of prevention against enamel decalcification should be indicated for these patients.
Esta pesquisa in vivo teve como objetivo avaliar a eficácia dos elastômeros liberadores de fluoreto estanoso no controle dos níveis de Streptococcus do grupo mutans na cavidade oral. Utilizou-se uma amostra de 40 pacientes ortodônticos, dividida em dois grupos de vinte indivíduos cada. No grupo experimental, foi utilizada ligadura elástica com liberação de fluoretos (Fluor-I-Ties, Ortho Arch Co. Inc., EUA) e, no grupo controle, foi utilizada ligadura elástica convencional (D. Morelli, Brasil). Para determinação do número de unidades formadoras de colônia (UFC) de Streptococcus do grupo mutans, foram realizadas duas coletas iniciais de saliva com intervalo de catorze dias. Logo após a segunda coleta de saliva, foram colocados os elastômeros liberadores de fluoretos nos pacientes do grupo experimental e, nos pacientes do grupo controle, foram inseridos os elastômeros convencionais. Nos 7°, 14° e 28° dias, saliva e biofilme ao redor do acessório ortodôntico foram coletados para análise microbiológica. Constatou-se que não houve diferenças estatisticamente significantes no número de UFC de Streptococcus do grupo mutans encontradas na saliva e no biofilme ao redor dos elastômeros com ou sem fluoretos. Dessa forma, os elastômeros liberadores de fluoreto não podem ser utilizados para reduzir a incidência de descalcificação do esmalte em pacientes ortodônticos. Como não houve redução significativa na quantidade de S. mutans na saliva e no biofilme, torna-se necessário indicar outros meios de prevenção da descalcificação do esmalte para esses pacientes.
Assuntos
Adolescente , Adulto , Criança , Feminino , Humanos , Masculino , Cariostáticos/farmacologia , Elastômeros/química , Fluoretos Tópicos/farmacologia , Aparelhos Ortodônticos/microbiologia , Streptococcus mutans/efeitos dos fármacos , Desmineralização do Dente/prevenção & controle , Contagem de Colônia Microbiana , Suscetibilidade à Cárie Dentária , Cárie Dentária/etiologia , Cárie Dentária/microbiologia , Cárie Dentária/prevenção & controle , Esmalte Dentário/efeitos dos fármacos , Aparelhos Ortodônticos/efeitos adversos , Saliva/microbiologia , Streptococcus mutans/isolamento & purificaçãoRESUMO
Avaliou-se o reembasamento de moldes obtidos pela técnica de moldagem com resina acrílica gelada comparativamente à uma técnica convencional de moldagem com casquete preenchido com mercaptana. Foi utilizado um dispositivo metálico contendo um troquel para casquetes e um para moldagem. Os troquéis foram metalizados pela eletrodeposiçäo de íons prata no molde. A alteraçäo dimensional dos moldes foi mensurada em microscópio de profundidade, pela discrepância de alinhamento horizontal entre a borda oclusal de um anel de aço que simula uma coroa total e se adapta perfeitamente ao troquel padräo, e a face oclusal de cada troquel reproduzido. As médias das alteraçöes dimensionais e respectivos desvios-padräo, em micrômetros foram: A-) 678,8 (ñ59,2) para Duralay sem reembasamento, 379,9 (ñ72,9) para Duralay com reembasamento e 18,8 (ñ6,2) para o Permlastic. A resina acrílica sem reembasamento apresentou maior alteraçäo dimensional. Troquéis reproduzidos a partir dos moldes de mercaptana apresentaram-se dimensionalmente mais próximos do padräo. O reembasamento demonstrou proporcionar melhora significante na moldagem com a resina acrílica gelada