Ability of two reciprocating Nickel-Titanium instruments for guttapercha/ sealer removal in simulated curved root canals / Análisis de la capacidad de dos instrumentos reciprocantes de Niquel-Titanio para la remoción de gutapercha/sellador en conductos curvos simulados

ABSTRACT The aim of this study was to compare the capacity of two reciprocating NiTi instruments in removing gutta-percha/sealer material from simulated curved root canals (SCRC). The time required for filling material removal was also recorded. Twenty SCRCs were divided into two groups of 10 (n=10) samples each. In Group 1, the SCRC were prepared to a R25 Reciproc Blue instrument (RCPB; VDW, Munich, Germany). In Group 2 the SCRC were prepared to a Primary WaveOne Gold instrument (PWOG; Dentsply, Ballaigues, Switzerland). In both groups, the canals were filled with matched-taper single gutta-percha cones and AH Plus sealer. Filling materials were removed with R25 RCPB (Group 1) and PWOG (Group 2). The amount of remaining gutta-percha/sealer was calculated at three predetermined levels of evaluation located at 2, 6 and 10 mm from the WL and expressed in percentages. Canals re-treated with RCPB contained significantly less remaining gutta-percha/sealer compared to canals prepared with PWOG (P=0.02). The RCPB instruments required significantly less time to complete the retreatment procedures (P<0.01). No unwinding or instrument separation was noted. RCPB instruments removed significantly more gutta-percha/sealer from simulated curved root canals than PWOG. However, neither of the tested instruments completely removed all filling materials.

RESUMEN El propósito del presente estudio fue comparar la capacidad de dos instrumentos de NiTi de movimiento reciproco para remover la obturación de gutapercha/sellador durante el retratamiento de conductos curvos simulados (SCRC). El tiempo requerido para la remoción del material fue también registrado. Se utilizaron veinte (n=20) SCRC divididos en dos grupos de diez especimenes (n=10) cada uno. En el Grupo 1 los SCRC se prepararon hasta un instrumento Reciproc Blue R25 (RCPB; VDW, Munich, Germany). En el Grupo 2, los SCRC se prepararon hasta un instrumento WaveOne Gold Primary (PWOG; Dentsply, Ballaigues, Switzerland). En ambos grupos los conductos se obturaron con cono único de gutapercha de conicidad creciente y el sellador AH Plus. La remoción de los materiales de obturación se realizó mediante los instrumentos RCPB R25 (Grupo 1) o PWOG (Grupo 2). La cantidad de gutapercha/sellador remanente se calculó en tres niveles de evaluación predeterminados ubicados a 2, 6 y 10 mm de la LT, y finalmente fue expresada en porcentajes. La cantidad de gutapercha/ sellador remanente en los SCRC retratados con RCPB fue significativamente menor en comparación con los que fueron retratados con PWOG (P=0.02). Los instrumentos RCPB requirieron un tiempo significativamente menor para completar el retratamiento (P<0.01). No se observaron deformaciones o separación de los instrumentos. Los instrumentos RCPB removieron una cantidad significativamente mayor de gutapercha/sellador que los instrumentos PWOG en conductos curvos simulados. Sin embargo, ninguno de los instrumentos ensayados removió completamente los materiales de obturación.

Pit and fissure depth in the enamel of mandibular third molars / Profundidad de fosas y fisuras en el esmalte de terceros molares inferiores

ABSTRACT The aim of this descriptive ex vivo study was to evaluate qualitatively the depth of pit and fissures (P&F) of the enamel in human mandibular third molars. Fifty (n=50) extracted human mandibular third molars were cleaned and disinfected. All tooth surfaces were coated with nail varnish except for a 1-mm margin around the periphery of the occlusal surface. The teeth were immersed for 48 hours at 37 °C in 1% methylene blue dye solution prepared in artificial saliva. After cleaning, the crowns were separated from the root at the cementoenamel junction and subsequently sectioned longitudinally in buccolingual direction at the location of the central fossa. All sections were examined using a stereoscopic microscope and photographed. The images were downloaded on a computer. The length of penetration of the P&F was recorded using the following scoring system: C1: P&F extended to half of the enamel thickness; C2: P&F extended beyond half of the enamel thickness without reaching the dentine-enamel junction; C3: P&F extended to the dentine-enamel junction. For pits, C1, C2 and C3 were observed in 35, 9 and 6 teeth, respectively, while for fissures, C1, C2 and C3 were observed in 15, 18 and 17 teeth, respectively. The P&F detected in the samples extended to the deepest portions of enamel, quite frequently reaching the enamel-dentine junction. Clinicians should recognize that even if pits and fissures are not clinically obvious, they penetrate deep into the enamel and frequently reach the dentine-enamel junction. Effective treatment is recommended to block access to P&F, thus preventing ingress of bacteria.

RESUMEN Objetivos: El objetivo del presente estudio descriptivo fue evaluar cualitativamente mediante un ensayo ex vivo la profundidad de las fosas y fisuras (F&F) del esmalte en terceros molares inferiores humanos. Materiales y métodos: Cincuenta (n=50) terceros molares inferiores sanos extraídos se lavaron, se descontaminaron y se recubrieron con esmalte para uñas hasta 1 mm menos del área de las F&F. Luego se sumergieron durante 48 horas a 37°C en una solución de azul de metileno al 1% (pH 7,4) preparada con saliva artificial. Posteriormente se lavaron y se separaron las coronas a nivel del límite amelocementario. En cada molar se realizó una sección longitudinal de 1 mm de espesor con orientación vestíbulo-lingual a nivel de la fosa central. Las secciones fueron analizadas con microscopio estereoscópico y fotografiadas. Las imágenes se transfirieron a una computadora. Se determinó cualitativamente la extensión de las F&F en el espesor del esmalte y se las clasificó de acuerdo a 3 categorías. C1: extensión hasta la mitad del espesor del esmalte; C2: extensión que supera la mitad del espesor del esmalte sin afectar el límite amelodentinario; C3: extensión que llega al límite amelodentinario. Resultados: Para las fosas, 35, 9 y 6 especimenes correspondieron a las categorías C1, C2 y C3 respectivamente. Para las fisuras, 15, 18 y 17 especimenes correspondieron a las categorías C1, C2 y C3 respectivamente. Conclusiones: Las fosas y fisuras de la muestra analizada se extienden hasta la zona más profunda del espesor del esmalte. Con cierta frecuencia llegan hasta el límite amelodentinario.