摘要
Abstract The purpose of this study was to examine the effect of different decontamination agents on the bond strength of saliva-contaminated CAD/CAM blocks and repair composite materials. Two hunderd eighty 3-mm-thick specimens were prepared from four different CAD/CAM materials: Katana Zirconia UTML disc, IPS e.max CAD block, Shofu block, and Vita Enamic block. Each material was divided into seven different subgroups (N=70). Group 1 had a clean surface. The other groups were comprised of the samples, which were contaminated with human saliva: group 2: negative control (non-cleaned); group 3: cleaned with water spray; group 4: cleaned with 70% ethanol; group 5: cleaned with Ivoclean; group 6: cleaned with Katana Cleaner; and group 7: cleaned with phosphoric acid. After the decontamination protocols, the resin composite cylinders were bonded to the CAD/CAM surfaces with a thin layer of dual-cured resin cement. The samples were stored for 24 hours at 37°C in distilled water. Then, they were subjected to a shear bond strength test (SBS). The values were recorded, and fracture types were evaluated using a microscope. Data were analyzed using two-way ANOVA and Tukey's post-hoc test. Generally, all decontaminating agents improved the SBS of composites to Katana Zirconia UTML, IPS e.max, and Vita Enamic materials (p<0.05). However, for Shofu materials, group 6 samples exhibited significantly higher bond strength values as compared with group 2 samples (p=0.026). The highest SBS values were seen in the phosphoric acid-treated group in Katana zirconia materials (26.45 ± 9.38 MPa), whereas the lowest values were seen in group 2 samples in Shofu materials (13.17±3.40 MPa). Each decontaminant agent improved the bond strength of composites to the contaminated CAD/CAM materials. If saliva is not cleaned before adhesive procedure, SBS values may decrease. All decontamination agents can be used safely on zirconia, lithium-disilicate glass-ceramic, hybrid ceramic, and polymer-infiltrated ceramic surfaces.
Resumen El propósito de este estudio fue examinar el efecto de diferentes agentes descontaminantes sobre la fuerza de unión de bloques CAD/CAM contaminados con saliva y materiales compuestos de reparación. Se prepararon doscientas ochenta muestras de 3 mm de espesor a partir de cuatro materiales CAD/CAM diferentes: disco Katana Zirconia UTML, bloque IPS e.max CAD, bloque Shofu y bloque Vita Enamic. Cada material se dividió en siete subgrupos diferentes (N=70). El grupo 1 tenía una superficie limpia. Los otros grupos estaban compuestos por muestras que estaban contaminadas con saliva humana: grupo 2: control negativo (no limpio); grupo 3: limpiado con agua pulverizada; grupo 4: limpiado con etanol al 70%; grupo 5: limpiado con Ivoclean; grupo 6: limpiado con Katana Cleaner; y grupo 7: limpiado con ácido fosfórico. Después de los protocolos de descontaminación, los cilindros de composite de resina se adhirieron a las superficies CAD/CAM con una fina capa de cemento de resina de curado dual. Las muestras se almacenaron durante 24 horas a 37°C en agua destilada. Luego, fueron sometidos a una prueba de resistencia al corte (SBS). Se registraron los valores y se evaluaron los tipos de fracturas utilizando un microscopio. Los datos se analizaron mediante ANOVA de dos factores y la prueba post-hoc de Tukey. En general, todos los agentes descontaminantes mejoraron el SBS de los composites con los materiales Katana Zirconia UTML, IPS e.max y Vita Enamic (p<0,05). Sin embargo, para los materiales Shofu, las muestras del grupo 6 exhibieron valores de fuerza de unión significativamente más altos en comparación con las muestras del grupo 2 (p=0,026). Los valores más altos de SBS se observaron en el grupo tratado con ácido fosfórico en materiales de circonio Katana (26,45 ± 9,38 MPa), mientras que los valores más bajos se observaron en las muestras del grupo 2 en materiales Shofu (13,17 ± 3,40 MPa). Cada agente descontaminante mejoró la fuerza de unión de los composites a los materiales CAD/CAM contaminados. Si no se limpia la saliva antes del procedimiento adhesivo, los valores de SBS pueden disminuir. Todos los agentes descontaminantes se pueden utilizar de forma segura en superficies de circonio, cerámica de vidrio de disilicato de litio, cerámica híbrida y cerámica con infiltraciones de polímeros.
Subject(s)
Decontamination/methods , Computer-Aided Design , Shear Strength , Denture Cleansers摘要
ABSTRACT: The aim of the study was to investigate the fracture strength of different composite resins and the quantity of voids in conventional posterior composite, high- flow flowable composite, bulk-fill flowable composite, and fiber-reinforced composite. Forty-four caries-free, freshly extracted mandibular premolars were used for this study. Teeth were prepared for cavity and root canal treatment. Subsequently, root canal treatment was applied to the teeth and cavities in order to prepare them for restorations. The specimens were then divided into four groups: group-1: Estelite Posterior; group-2: Estelite Flow Quick High Flow; group-3: Estelite Bulk-fill Flow; group-4: everX Posterior. One specimen from each experimental group was examined using micro-CT to perform measurement of voids. The fracture strength values of high-flow flowable, bulk-fill flowable, fiber-reinforced, and conventional micro- hybrid composites were found to be similar (p=0.497). EverX Posterior showed the highest fracture strength values (841.1±149.4 N), followed by Estelite Bulk-fill Flow (822.8±170.8 N). Volume of voids (%) obtained from Micro-CT analysis revealed that restorations with high-flow liner or bulk-fill flowable exhibited more voids. The fiber-reinforced composite showed the lowest percentage volume of incorporating voids and the highest fracture strength results.
RESUMEN: El objetivo del estudio fue investigar la resistencia a la fractura de diferentes resinas compuestas y la cantidad de burbujas en resinas posteriores convencionales, resinas fluidas de alto flujo, resinas fluidas tipo bulk-fill y resinas reforzados con fibras. Cuarenta y cuatro premolares mandibulares libres de caries, recién extraídos, fueron usados para este estudio. Los dientes se prepararon para el tratamiento de conductos radiculares y las cavidades para prepararlos para las restauraciones. Los especímenes se dividieron en cuatro grupos: Grupo-1: Estelite Posterior; Grupo-2: Estelite Flow Quick High Flow; Grupo-3: Estelite Bulk-fill Flow; Grupo-4: everX Posterior. Un espécimen de cada grupo experimental fue examinado usando micro-CT para realizar la medición de las burbujas. Los valores de resistencia a la fractura de los compuestos de alto flujo, flujo de relleno, reforzados con fibra y microhíbridos convencionales fueron similares (p=0,497). EverX Posterior mostró los valores más altos de resistencia a la fractura (841,1±149,4 N), seguido de Estelite Bulk-fill Flow (822,8±170,8 N). El volumen de las burbujas (%) obtenido del análisis de Micro-TC reveló que las restauraciones con revestimiento de alto flujo o con flujo de relleno a granel presentaban más huecos. El compuesto reforzado con fibra mostró el menor porcentaje de volumen de incorporación de vacíos y los resultados más altos de resistencia a la fractura.
Subject(s)
Composite Resins/analysis , Flexural Strength摘要
Abstract: Purpose: The objective of this study is to evaluate and compare the microtensile bond strength (μTBS) of four different self-adhesive resin cements to a resin-based ceramic CAD/CAM block, at the baseline, and after subjecting them to 5,000 thermo-cycles.Materials and Methods: Four self-adhesive dual-cured resin cements; G-CEM LinkAce (GC EUROPE, Leuven, Belgium), RelyX U200 (3M ESPE, Seefeld, Germany), Maxcem Elite (Kerr, CA, USA), TheraCem (Bisco, Schaumburg, USA) were applied to Cerasmart CAD/CAM blocks (GC EUROPE, Leuven, Belgium). CAD/CAM blocks were sectioned into sticks and subjected to µTBS tests at 24 hours, and the other half were subjected to tests after 5000 thermo-cycles. The data were tested by one-way variance analysis (p<0.05). Results: The highest bond strength values were observed in TheraCem, followed by G-CEM LinkAce and RelyX U200, respectively (p<0.05). At the baseline, G-CEM LinkAce, RelyX U200, and Maxcem Elite showed statistically similar results. After 5,000 thermal-cycles, a significant decrease was observed in the bond strength values of G-CEM LinkAce (p<0.05). Conclusion: Between the adhesive cements used in the study, TheraCem showed the highest micro-tensile bond strength values both in the baseline (24h) results, and after the 5,000 thermal- cycle aging procedures.
Resumen: Propósito: Evaluar y comparar la resistencia adhesiva microtensil (μTBS) de cuatro cementos de resina autoadhesivos diferentes con un bloque CAD/CAM de cerámica a base de resina, antes y después de 5.000 ciclos de termociclado. Materiales y métodos: cuatro cementos de resina de doble curado autoadhesivos; G-CEM LinkAce (GC EUROPE, Lovaina, Bélgica), RelyX U200 (3M ESPE, Seefeld, Alemania), Maxcem Elite (Kerr, CA, EE. UU.), TheraCem (Bisco, Schaumburg, EE. UU.) fueron aplicados a bloques Cerasmart CAD/CAM (GC EUROPE, Lovaina, Bélgica). Los bloques CAD/CAM se seccionaron en barras y se sometieron a pruebas µTBS a las 24 horas, y la otra mitad se sometió a pruebas después de 5000 ciclos térmicos. Los datos fueron probados por análisis de varianza unidireccional (p<0.05). Resultados: Los valores más altos de fuerza de unión se observaron en TheraCem, seguido de G-CEM LinkAce y RelyX U200, respectivamente (p<0.05). En la línea de base, G-CEM LinkAce, RelyX U200, Maxcem Elite mostró resultados estadísticamente similares. Después de 5.000 procesos de ciclo térmico, se observó una disminución significativa en los valores de resistencia de la unión de G-CEM LinkAce (p<0.05). Conclusión: entre los cementos adhesivos utilizados en el estudio, TheraCem mostró los valores más altos de resistencia de la unión micro-extensible tanto en la línea de base (24 h) como después de 5,000 procedimientos de envejecimiento térmico.